Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_84700258_yJvjyJ.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 15.18 T-atoms per nm^3
Material density = 1.514 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6267 Angstrom
T1  -- O2  = 1.6210 Angstrom
T1  -- O3  = 1.6040 Angstrom
T1  -- O4  = 1.5918 Angstrom
      mean = 1.6109 Angstrom
        t1 = 0.011359  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007184  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5988 Angstrom
T2  -- O5  = 1.6310 Angstrom
T2  -- O6  = 1.6457 Angstrom
T2  -- O7  = 1.6431 Angstrom
      mean = 1.6297 Angstrom
        t1 = 0.027862  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029121  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6126 Angstrom
T3  -- O8  = 1.6446 Angstrom
T3  -- O9  = 1.5621 Angstrom
T3  -- O10 = 1.6028 Angstrom
      mean = 1.6055 Angstrom
        t1 = 0.027974  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032212  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.5683 Angstrom
T4  -- O11 = 1.6303 Angstrom
T4  -- O7  = 1.6445 Angstrom
T4  -- O12 = 1.6301 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.018199  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021457  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6152 Angstrom
T5  -- O13 = 1.6107 Angstrom
T5  -- O10 = 1.6152 Angstrom
T5  -- O13 = 1.6107 Angstrom
      mean = 1.6129 Angstrom
        t1 = 0.007187  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008416  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5621 A <--> 1.6457 A
          Mean   = 1.6157 A
          StdDev = 0.0241 A

       t1 Range  = 0.0072 <-- 0.0185 --> 0.0280
       t2 Range  = 0.0072 <-- 0.0197 --> 0.0322

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.542 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.109 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.845 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.024 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.012 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.277 deg; O3  -- O4  = 3 A
       107.277 deg <-- 109.468 deg --> 111.845 deg

O4  -- T2  -- O5  = 107.163 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.006 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 111.060 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 111.824 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.700 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 113.845 deg; O6  -- O7  = 3 A
       104.006 deg <-- 109.433 deg --> 113.845 deg

O6  -- T3  -- O8  = 115.244 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 104.425 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 108.902 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 108.548 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.794 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.731 deg; O9  -- O10 = 3 A
       104.425 deg <-- 109.441 deg --> 115.244 deg

O9  -- T4  -- O11 = 113.135 deg; O9  -- O11 = 3 A
O9  -- T4  -- O7  = 105.934 deg; O9  -- O7  = 3 A
O9  -- T4  -- O12 = 108.206 deg; O9  -- O12 = 3 A
O11 -- T4  -- O7  = 110.160 deg; O11 -- O7  = 3 A
O11 -- T4  -- O12 = 110.064 deg; O11 -- O12 = 3 A
O7  -- T4  -- O12 = 109.199 deg; O7  -- O12 = 3 A
       105.934 deg <-- 109.450 deg --> 113.135 deg

O10 -- T5  -- O13 = 108.303 deg; O10 -- O13 = 3 A
O10 -- T5  -- O10 = 111.094 deg; O10 -- O10 = 3 A
O10 -- T5  -- O13 = 110.118 deg; O10 -- O13 = 3 A
O13 -- T5  -- O10 = 110.118 deg; O13 -- O10 = 3 A
O13 -- T5  -- O13 = 108.880 deg; O13 -- O13 = 3 A
O10 -- T5  -- O13 = 108.304 deg; O10 -- O13 = 3 A
       108.303 deg <-- 109.470 deg --> 111.094 deg

        O-T-O SUMMARY
          Range  = 104.0057 deg <--> 115.2445 deg
          Mean   = 109.4457 deg
          StdDev = 2.4775 deg

        O--O SUMMARY
          Range  = 2.5092 A <--> 2.7558 A
          Mean   = 2.6368 A
          StdDev = 0.0550 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.937 deg; T1  -- T1  = 4.0769 A
T1  - O1  - T1  - O3  - T1  =  89.063 deg; T1  -- T1  = 4.0769 A
T1  - O1  - T1  - O4  - T2  = 146.383 deg; T1  -- T2  = 5.7318 A
T1  - O2  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.0778 A
T1  - O2  - T1  - O4  - T2  =  89.663 deg; T1  -- T2  = 4.2616 A
T1  - O3  - T1  - O4  - T2  = 119.284 deg; T1  -- T2  = 5.2913 A

T1  - O4  - T2  - O5  - T2  =  90.337 deg; T1  -- T2  = 4.2616 A
T1  - O4  - T2  - O6  - T3  = 124.834 deg; T1  -- T3  = 5.5249 A
T1  - O4  - T2  - O7  - T4  = 112.907 deg; T1  -- T4  = 5.3084 A
T2  - O5  - T2  - O6  - T3  = 135.110 deg; T2  -- T3  = 5.4798 A
T2  - O5  - T2  - O7  - T4  =  90.755 deg; T2  -- T4  = 4.3238 A
T3  - O6  - T2  - O7  - T4  =  98.225 deg; T3  -- T4  = 4.7605 A

T2  - O6  - T3  - O8  - T3  = 157.953 deg; T2  -- T3  = 5.8280 A
T2  - O6  - T3  - O9  - T4  =  84.980 deg; T2  -- T4  = 4.1818 A
T2  - O6  - T3  - O10 - T5  = 110.162 deg; T2  -- T5  = 5.0899 A
T3  - O8  - T3  - O9  - T4  =  91.244 deg; T3  -- T4  = 4.2695 A
T3  - O8  - T3  - O10 - T5  =  91.859 deg; T3  -- T5  = 4.3042 A
T4  - O9  - T3  - O10 - T5  = 103.034 deg; T4  -- T5  = 4.8834 A

T3  - O9  - T4  - O11 - T4  = 133.455 deg; T3  -- T4  = 5.5526 A
T3  - O9  - T4  - O7  - T4  =  88.756 deg; T3  -- T4  = 4.2695 A
T3  - O9  - T4  - O12 - T2  = 109.268 deg; T3  -- T2  = 5.1597 A
T4  - O11 - T4  - O7  - T4  = 120.000 deg; T4  -- T4  = 5.1317 A
T4  - O11 - T4  - O12 - T2  =  89.245 deg; T4  -- T2  = 4.3238 A
T4  - O7  - T4  - O12 - T2  = 118.512 deg; T4  -- T2  = 5.3371 A

T3  - O10 - T5  - O13 - T5  =  88.141 deg; T3  -- T5  = 4.3042 A
T3  - O10 - T5  - O10 - T5  = 134.035 deg; T3  -- T5  = 5.6968 A
T3  - O10 - T5  - O13 - T3  =  96.995 deg; T3  -- T3  = 4.6845 A
T5  - O13 - T5  - O10 - T5  = 120.000 deg; T5  -- T5  = 5.3007 A
T5  - O13 - T5  - O13 - T3  = 134.035 deg; T5  -- T3  = 5.6968 A
T5  - O10 - T5  - O13 - T3  =  88.141 deg; T5  -- T3  = 4.3042 A

        T-T-T SUMMARY
          Range  = 84.9799 deg <--> 157.9532 deg
          Mean   = 109.2972 deg
          StdDev = 20.1474 deg

        T--T SUMMARY
          Range  = 4.0769 A <--> 5.8280 A
          Mean   = 4.9043 A
          StdDev = 0.5703 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.158 deg ; T1  -- T1   2.8336 A

T1  -- O2  -- T1  = 125.741 deg ; T1  -- T1   2.8853 A

T1  -- O3  -- T1  = 136.344 deg ; T1  -- T1   2.9779 A

T1  -- O4  -- T2  = 162.453 deg ; T1  -- T2   3.1533 A

T2  -- O5  -- T2  = 121.649 deg ; T2  -- T2   2.8482 A

T2  -- O6  -- T3  = 141.905 deg ; T2  -- T3   3.0800 A

T2  -- O7  -- T4  = 156.036 deg ; T2  -- T4   3.2159 A

T3  -- O8  -- T3  = 120.628 deg ; T3  -- T3   2.8575 A

T3  -- O9  -- T4  = 167.214 deg ; T3  -- T4   3.1109 A

T3  -- O10 -- T5  = 152.760 deg ; T3  -- T5   3.1275 A

T4  -- O11 -- T4  = 128.190 deg ; T4  -- T4   2.9330 A

T4  -- O12 -- T4  = 133.265 deg ; T4  -- T4   2.9926 A

T5  -- O13 -- T5  = 143.628 deg ; T5  -- T5   3.0604 A


        T-O-T SUMMARY
          Range  = 120.6281° <--> 167.2138 deg
          Mean   = 139.1326 deg
          StdDev = 15.8520 deg

        T--T SUMMARY
          Range  = 2.8336 A <--> 3.2159 A
          Mean   = 3.0037 A
          StdDev = 0.1254 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 28 43 64 90 118 144 170 202 243 294 352 409 461
TD10 = 688
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.12
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 28 43 62 86 113 143 177 209 247 295 347 403 458
TD10 = 685
Circuit symbol = 4.5.4.8_{2}.6.6_{2}
Weight = 17
Vertex symbol  = 4.5.4.8.6.6
Weight = 17

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 30 44 60 82 111 143 177 213 252 294 343 396 450
TD10 = 681
Circuit symbol = 4.5.4.6_{2}.5.7
Weight = 13
Vertex symbol  = 4.5.4.6.5.12_{2}
Weight = 28

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 27 40 61 89 119 146 170 199 239 296 359 417 465
TD10 = 685
Circuit symbol = 4.4.5.6.6.6
Weight = 18
Vertex symbol  = 4.4.5.6.6.6
Weight = 18

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 19 30 43 58 78 104 138 178 219 258 293 328 374 438
TD10 = 663
Circuit symbol = 4.4.5_{2}.6.7_{3}.7_{3}
Weight = 16
Vertex symbol  = 4.4.5_{2}.6.8.8
Weight = 22

<TD10> = 682.333
Average ring size = 5.2615