Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_83750343__bJbG9.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 24.69 T-atoms per nm^3
Material density = 2.463 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6340 Angstrom
T1  -- O2  = 1.6577 Angstrom
T1  -- O3  = 1.5424 Angstrom
T1  -- O4  = 1.6134 Angstrom
      mean = 1.6119 Angstrom
        t1 = 0.044426  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039508  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6311 Angstrom
T2  -- O5  = 1.6398 Angstrom
T2  -- O6  = 1.6167 Angstrom
T2  -- O7  = 1.5923 Angstrom
      mean = 1.6200 Angstrom
        t1 = 0.027561  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016977  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.5648 Angstrom
T3  -- O8  = 1.6057 Angstrom
T3  -- O9  = 1.5988 Angstrom
T3  -- O10 = 1.5861 Angstrom
      mean = 1.5888 Angstrom
        t1 = 0.017216  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008946  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.5833 Angstrom
T4  -- O11 = 1.7229 Angstrom
T4  -- O12 = 1.7414 Angstrom
T4  -- O13 = 1.6751 Angstrom
      mean = 1.6807 Angstrom
        t1 = 0.079911  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.059389  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6288 Angstrom
T5  -- O14 = 1.6217 Angstrom
T5  -- O4  = 1.6288 Angstrom
T5  -- O14 = 1.6217 Angstrom
      mean = 1.6252 Angstrom
        t1 = 0.011483  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009130  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5424 A <--> 1.7414 A
          Mean   = 1.6253 A
          StdDev = 0.0490 A

       t1 Range  = 0.0115 <-- 0.0361 --> 0.0799
       t2 Range  = 0.0089 <-- 0.0268 --> 0.0594

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 116.170 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.519 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.463 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 106.414 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 114.879 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 104.066 deg; O3  -- O4  = 2 A
       104.066 deg <-- 109.252 deg --> 116.170 deg

O2  -- T2  -- O5  = 116.569 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 109.048 deg; O2  -- O6  = 3 A
O2  -- T2  -- O7  = 104.332 deg; O2  -- O7  = 3 A
O5  -- T2  -- O6  = 109.106 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.282 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.253 deg; O6  -- O7  = 3 A
       104.332 deg <-- 109.432 deg --> 116.569 deg

O3  -- T3  -- O8  = 111.370 deg; O3  -- O8  = 3 A
O3  -- T3  -- O9  = 108.789 deg; O3  -- O9  = 3 A
O3  -- T3  -- O10 = 107.417 deg; O3  -- O10 = 3 A
O8  -- T3  -- O9  = 109.062 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.565 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.631 deg; O9  -- O10 = 3 A
       107.417 deg <-- 109.472 deg --> 111.370 deg

O10 -- T4  -- O11 = 103.667 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 100.194 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 = 103.330 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 123.296 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.012 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 114.255 deg; O12 -- O13 = 3 A
       100.194 deg <-- 108.959 deg --> 123.296 deg

O4  -- T5  -- O14 = 110.563 deg; O4  -- O14 = 3 A
O4  -- T5  -- O4  = 107.064 deg; O4  -- O4  = 3 A
O4  -- T5  -- O14 = 109.335 deg; O4  -- O14 = 3 A
O14 -- T5  -- O4  = 109.335 deg; O14 -- O4  = 3 A
O14 -- T5  -- O14 = 109.942 deg; O14 -- O14 = 3 A
O4  -- T5  -- O14 = 110.563 deg; O4  -- O14 = 3 A
       107.064 deg <-- 109.467 deg --> 110.563 deg

        O-T-O SUMMARY
          Range  = 100.1938 deg <--> 123.2961 deg
          Mean   = 108.9764 deg
          StdDev = 4.3491 deg

        O--O SUMMARY
          Range  = 2.4883 A <--> 3.0488 A
          Mean   = 2.6382 A
          StdDev = 0.1013 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  98.760 deg; T2  -- T3  = 4.3583 A
T2  - O1  - T1  - O3  - T5  = 129.285 deg; T2  -- T5  = 5.3832 A
T2  - O1  - T1  - O4  - T1  = 139.912 deg; T2  -- T1  = 5.5908 A
T3  - O2  - T1  - O3  - T5  = 119.442 deg; T3  -- T5  = 4.6476 A
T3  - O2  - T1  - O4  - T1  = 107.750 deg; T3  -- T1  = 4.3436 A
T5  - O3  - T1  - O4  - T1  =  60.059 deg; T5  -- T1  = 2.8072 A

T1  - O2  - T2  - O5  - T2  = 137.920 deg; T1  -- T2  = 5.9110 A
T1  - O2  - T2  - O6  - T2  = 106.860 deg; T1  -- T2  = 4.8280 A
T1  - O2  - T2  - O7  - T2  = 112.232 deg; T1  -- T2  = 5.0045 A
T2  - O5  - T2  - O6  - T2  =  90.161 deg; T2  -- T2  = 4.2868 A
T2  - O5  - T2  - O7  - T2  =  89.839 deg; T2  -- T2  = 4.2868 A
T2  - O6  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 4.9689 A

T1  - O3  - T3  - O8  - T3  = 113.057 deg; T1  -- T3  = 4.3741 A
T1  - O3  - T3  - O9  - T3  = 123.034 deg; T1  -- T3  = 4.5855 A
T1  - O3  - T3  - O10 - T4  = 100.769 deg; T1  -- T4  = 4.4226 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 4.6026 A
T3  - O8  - T3  - O10 - T4  =  95.232 deg; T3  -- T4  = 4.3102 A
T3  - O9  - T3  - O10 - T4  =  93.863 deg; T3  -- T4  = 4.2457 A

T3  - O10 - T4  - O11 - T4  =  96.570 deg; T3  -- T4  = 4.8692 A
T3  - O10 - T4  - O12 - T4  =  86.137 deg; T3  -- T4  = 4.2457 A
T3  - O10 - T4  - O13 - T4  =  84.768 deg; T3  -- T4  = 4.3102 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.5587 A
T4  - O11 - T4  - O13 - T4  = 149.955 deg; T4  -- T4  = 6.3902 A
T4  - O12 - T4  - O13 - T4  = 120.000 deg; T4  -- T4  = 5.4680 A

T1  - O4  - T5  - O14 - T5  = 116.752 deg; T1  -- T5  = 4.8787 A
T1  - O4  - T5  - O4  - T5  = 114.608 deg; T1  -- T5  = 4.8217 A
T1  - O4  - T5  - O14 - T1  =  59.882 deg; T1  -- T1  = 2.8022 A
T5  - O14 - T5  - O4  - T5  = 120.000 deg; T5  -- T5  = 5.0609 A
T5  - O14 - T5  - O14 - T1  = 114.608 deg; T5  -- T1  = 4.8217 A
T5  - O4  - T5  - O14 - T1  = 116.752 deg; T5  -- T1  = 4.8787 A

        T-T-T SUMMARY
          Range  = 59.8820 deg <--> 149.9551 deg
          Mean   = 106.9588 deg
          StdDev = 20.5308 deg

        T--T SUMMARY
          Range  = 2.8022 A <--> 6.3902 A
          Mean   = 4.6297 A
          StdDev = 0.7140 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 118.060 deg ; T1  -- T1   2.8022 A

T1  -- O2  -- T2  = 146.314 deg ; T1  -- T2   3.1478 A

T1  -- O3  -- T3  = 111.795 deg ; T1  -- T3   2.5728 A

T1  -- O4  -- T5  = 119.955 deg ; T1  -- T5   2.8072 A

T2  -- O5  -- T2  = 152.490 deg ; T2  -- T2   3.1854 A

T2  -- O6  -- T2  = 124.370 deg ; T2  -- T2   2.8599 A

T2  -- O7  -- T2  = 129.276 deg ; T2  -- T2   2.8777 A

T3  -- O8  -- T3  = 112.523 deg ; T3  -- T3   2.6705 A

T3  -- O9  -- T3  = 111.561 deg ; T3  -- T3   2.6440 A

T3  -- O10 -- T4  = 166.819 deg ; T3  -- T4   3.1485 A

T4  -- O11 -- T4  = 156.155 deg ; T4  -- T4   3.3715 A

T4  -- O12 -- T4  = 137.367 deg ; T4  -- T4   3.2447 A

T4  -- O13 -- T4  = 132.668 deg ; T4  -- T4   3.0683 A

T5  -- O14 -- T5  = 128.558 deg ; T5  -- T5   2.9219 A


        T-O-T SUMMARY
          Range  = 111.5614° <--> 166.8194 deg
          Mean   = 132.1210 deg
          StdDev = 17.3725 deg

        T--T SUMMARY
          Range  = 2.5728 A <--> 3.3715 A
          Mean   = 2.9527 A
          StdDev = 0.2410 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T3  = 2.5728 Angstrom
T3  -- T1  = 2.5728 Angstrom
T3  -- T3  = 2.6705 Angstrom
T3  -- T3  = 2.6440 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 39 63 92 131 171 219 279 339 409 478 558 661 769
TD10 = 1032
Circuit symbol = 3.6.6.7.6.7
Weight = 14
Vertex symbol  = 3.6.6.8_{2}.6.8_{2}
Weight = 19

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 39 64 96 135 181 232 284 340 407 488 575 659 749
TD10 = 1067
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 36 58 86 120 160 208 261 323 396 477 560 648 751
TD10 = 964
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 20
Vertex symbol  = 4.6.4.6.6.8
Weight = 20

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 34 59 90 126 171 223 282 346 417 496 579 673 777
TD10 = 1017
Circuit symbol = 4.4.4.8_{2}.6.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.10_{3}.6.8
Weight = 24

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 21 40 67 96 128 168 218 276 339 408 489 574 658 756
TD10 = 1029
Circuit symbol = 3.6.6.6.6.6
Weight = 20
Vertex symbol  = 3.6.6.6.6.6
Weight = 20

<TD10> = 1021.000
Average ring size = 5.6278