Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_81092677_gbS2Cb.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 27.90 T-atoms per nm^3
Material density = 2.784 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6183 Angstrom
T1  -- O4  = 1.6847 Angstrom
T1  -- O2  = 1.7502 Angstrom
T1  -- O3  = 1.6078 Angstrom
      mean = 1.6653 Angstrom
        t1 = 0.104466  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.062904  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5985 Angstrom
T2  -- O5  = 1.6630 Angstrom
T2  -- O6  = 1.5229 Angstrom
T2  -- O7  = 1.6359 Angstrom
      mean = 1.6051 Angstrom
        t1 = 0.093794  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.125861  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6528 Angstrom
T3  -- O8  = 1.6126 Angstrom
T3  -- O9  = 1.7246 Angstrom
T3  -- O10 = 1.7482 Angstrom
      mean = 1.6845 Angstrom
        t1 = 0.205753  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.140775  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.5219 Angstrom
T4  -- O11 = 1.5646 Angstrom
T4  -- O12 = 1.5440 Angstrom
T4  -- O13 = 1.5711 Angstrom
      mean = 1.5504 Angstrom
        t1 = 0.056381  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058784  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6330 Angstrom
T5  -- O10 = 1.6772 Angstrom
T5  -- O7  = 1.6330 Angstrom
T5  -- O10 = 1.6772 Angstrom
      mean = 1.6551 Angstrom
        t1 = 0.078790  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056661  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5219 A <--> 1.7502 A
          Mean   = 1.6295 A
          StdDev = 0.0686 A

       t1 Range  = 0.0564 <-- 0.1078 --> 0.2058
       t2 Range  = 0.0567 <-- 0.0890 --> 0.1408

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 120.369 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 107.458 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  92.075 deg; O1  -- O3  = 2 A
O4  -- T1  -- O2  = 121.532 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  =  90.966 deg; O4  -- O3  = 2 A
O2  -- T1  -- O3  = 120.190 deg; O2  -- O3  = 3 A
       90.966 deg <-- 108.765 deg --> 121.532 deg

O3  -- T2  -- O5  = 123.593 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  86.405 deg; O3  -- O6  = 2 A
O3  -- T2  -- O7  = 111.988 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 102.501 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 117.196 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.084 deg; O6  -- O7  = 3 A
       86.405 deg <-- 108.295 deg --> 123.593 deg

O4  -- T3  -- O8  =  55.193 deg; O4  -- O8  = 2 A
O4  -- T3  -- O9  = 103.384 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  73.745 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 113.631 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 114.594 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 115.830 deg; O9  -- O10 = 3 A
       55.193 deg <-- 96.063 deg --> 115.830 deg

O6  -- T4  -- O11 = 114.046 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 =  98.279 deg; O6  -- O12 = 2 A
O6  -- T4  -- O13 = 105.984 deg; O6  -- O13 = 2 A
O11 -- T4  -- O12 = 110.100 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 111.306 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 116.548 deg; O12 -- O13 = 3 A
       98.279 deg <-- 109.377 deg --> 116.548 deg

O7  -- T5  -- O10 = 100.464 deg; O7  -- O10 = 3 A
O7  -- T5  -- O7  = 120.301 deg; O7  -- O7  = 3 A
O7  -- T5  -- O10 = 102.545 deg; O7  -- O10 = 3 A
O10 -- T5  -- O7  = 102.545 deg; O10 -- O7  = 3 A
O10 -- T5  -- O10 = 132.763 deg; O10 -- O10 = 3 A
O7  -- T5  -- O10 = 100.464 deg; O7  -- O10 = 3 A
       100.464 deg <-- 109.847 deg --> 132.763 deg

        O-T-O SUMMARY
          Range  = 55.1931 deg <--> 132.7628 deg
          Mean   = 105.9839 deg
          StdDev = 15.9373 deg

        O--O SUMMARY
          Range  = 1.5131 A <--> 3.0733 A
          Mean   = 2.5878 A
          StdDev = 0.3246 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.639 deg ; T1  -- T1   3.2364 A

T1  -- O2  -- T1  = 142.924 deg ; T1  -- T1   3.3188 A

T1  -- O3  -- T2  = 140.252 deg ; T1  -- T2   3.0154 A

T1  -- O4  -- T3  = 140.184 deg ; T1  -- T3   3.1381 A

T2  -- O5  -- T2  = 118.675 deg ; T2  -- T2   2.8610 A

T2  -- O6  -- T4  = 132.040 deg ; T2  -- T4   2.7820 A

T2  -- O7  -- T5  = 134.996 deg ; T2  -- T5   3.0201 A

T3  -- O8  -- T3  =  92.371 deg ; T3  -- T3   2.3272 A

T3  -- O9  -- T3  = 164.970 deg ; T3  -- T3   3.4196 A

T3  -- O10 -- T5  = 164.657 deg ; T3  -- T5   3.3947 A

T4  -- O11 -- T4  = 134.899 deg ; T4  -- T4   2.8900 A

T4  -- O12 -- T4  = 109.053 deg ; T4  -- T4   2.5148 A

T4  -- O13 -- T4  = 118.726 deg ; T4  -- T4   2.7037 A


        T-O-T SUMMARY
          Range  = 92.3708° <--> 178.6387 deg
          Mean   = 136.3375 deg
          StdDev = 22.9065 deg

        T--T SUMMARY
          Range  = 2.3272 A <--> 3.4196 A
          Mean   = 2.9709 A
          StdDev = 0.3230 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O6  = 2.1376 A
O4  -- O8  = 1.5131 A
O4  -- O10 = 2.0421 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.3188 Angstrom
  T1  -- T3  = 2.3360 Angstrom
  T1  -- T3  = 3.1381 Angstrom
  T1  -- T1  = 3.2364 Angstrom
  T1  -- T2  = 3.0154 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T2  = 3.1190 Angstrom
  T2  -- T2  = 2.8610 Angstrom
  T2  -- T4  = 2.7820 Angstrom
  T2  -- T5  = 3.0201 Angstrom
  T2  -- T1  = 3.0154 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.3360 Angstrom
  T3  -- T1  = 3.1381 Angstrom
  T3  -- T3  = 2.3272 Angstrom
  T3  -- T3  = 3.4196 Angstrom
  T3  -- T5  = 3.3947 Angstrom
T4  -- T2  = 2.7820 Angstrom
T4  -- T4  = 2.5148 Angstrom
T4  -- T4  = 2.7037 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 24 46 76 107 145 195 258 324 385 459 541 630 734 839
TD10 = 1191
Circuit symbol = 4.6.5.6.6.6
Weight = 19
Vertex symbol  = 4.6.5.6.6.6
Weight = 19

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 39 65 102 145 190 236 297 375 453 533 621 716 817
TD10 = 1113
Circuit symbol = 4.6.5.6.6.6
Weight = 20
Vertex symbol  = 4.6.5.6.6.6
Weight = 20

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 27 50 78 111 152 200 262 330 392 465 540 630 744 845
TD10 = 1227
Circuit symbol = 5.6.6.6.6.6_{2}
Weight = 23
Vertex symbol  = 5.6.6.6.6.6_{2}
Weight = 23

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 27 45 75 118 169 220 263 316 398 500 599 680 760
TD10 = 947
Circuit symbol = 4.4.4.6.5.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.6.5.6
Weight = 16

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 26 44 69 112 155 198 252 310 386 460 546 646 731 826
TD10 = 1183
Circuit symbol = 5.5.6.6.6.6
Weight = 21
Vertex symbol  = 5.5.6.6.6.6
Weight = 21

<TD10> = 1126.556
Average ring size = 5.3333