Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_80580100_cZW0G5.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 23.47 T-atoms per nm^3
Material density = 2.342 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5971 Angstrom
T1  -- O2  = 1.6297 Angstrom
T1  -- O3  = 1.5731 Angstrom
T1  -- O4  = 1.6158 Angstrom
      mean = 1.6039 Angstrom
        t1 = 0.024418  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029225  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5715 Angstrom
T2  -- O5  = 1.6535 Angstrom
T2  -- O6  = 1.5853 Angstrom
T2  -- O7  = 1.6305 Angstrom
      mean = 1.6102 Angstrom
        t1 = 0.041792  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038746  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6039 Angstrom
T3  -- O8  = 1.6468 Angstrom
T3  -- O9  = 1.6492 Angstrom
T3  -- O10 = 1.7151 Angstrom
      mean = 1.6538 Angstrom
        t1 = 0.045320  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031162  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6021 Angstrom
T4  -- O11 = 1.6761 Angstrom
T4  -- O12 = 1.6209 Angstrom
T4  -- O13 = 1.6579 Angstrom
      mean = 1.6392 Angstrom
        t1 = 0.046350  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030058  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6521 Angstrom
T5  -- O13 = 1.6064 Angstrom
T5  -- O10 = 1.6521 Angstrom
T5  -- O13 = 1.6064 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.060542  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056989  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5715 A <--> 1.7151 A
          Mean   = 1.6271 A
          StdDev = 0.0363 A

       t1 Range  = 0.0244 <-- 0.0437 --> 0.0605
       t2 Range  = 0.0292 <-- 0.0372 --> 0.0570

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.725 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.019 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.896 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.469 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.122 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.668 deg; O3  -- O4  = 3 A
       105.019 deg <-- 109.483 deg --> 113.896 deg

O3  -- T2  -- O5  = 113.822 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.239 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 102.074 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 106.579 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 117.458 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.095 deg; O6  -- O7  = 3 A
       102.074 deg <-- 109.378 deg --> 117.458 deg

O4  -- T3  -- O8  = 102.478 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 106.544 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 111.166 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 111.696 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 113.744 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.708 deg; O9  -- O10 = 3 A
       102.478 deg <-- 109.389 deg --> 113.744 deg

O7  -- T4  -- O11 = 112.147 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 108.535 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  99.247 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 109.403 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 118.334 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 108.503 deg; O12 -- O13 = 3 A
       99.247 deg <-- 109.362 deg --> 118.334 deg

O10 -- T5  -- O13 = 106.750 deg; O10 -- O13 = 3 A
O10 -- T5  -- O10 = 117.673 deg; O10 -- O10 = 3 A
O10 -- T5  -- O13 = 114.930 deg; O10 -- O13 = 3 A
O13 -- T5  -- O10 = 114.930 deg; O13 -- O10 = 3 A
O13 -- T5  -- O13 =  93.415 deg; O13 -- O13 = 2 A
O10 -- T5  -- O13 = 106.750 deg; O10 -- O13 = 3 A
       93.415 deg <-- 109.074 deg --> 117.673 deg

        O-T-O SUMMARY
          Range  = 93.4147 deg <--> 118.3336 deg
          Mean   = 109.3542 deg
          StdDev = 5.6709 deg

        O--O SUMMARY
          Range  = 2.3385 A <--> 2.8628 A
          Mean   = 2.6524 A
          StdDev = 0.1197 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 178.832 deg ; T1  -- T1   3.1941 A

T1  -- O2  -- T1  = 108.274 deg ; T1  -- T1   2.6414 A

T1  -- O3  -- T2  = 113.432 deg ; T1  -- T2   2.6288 A

T1  -- O4  -- T3  = 160.026 deg ; T1  -- T3   3.1709 A

T2  -- O5  -- T2  = 131.036 deg ; T2  -- T2   3.0095 A

T2  -- O6  -- T2  = 132.840 deg ; T2  -- T2   2.9059 A

T2  -- O7  -- T4  = 139.419 deg ; T2  -- T4   3.0320 A

T3  -- O8  -- T3  = 138.770 deg ; T3  -- T3   3.0828 A

T3  -- O9  -- T3  = 134.155 deg ; T3  -- T3   3.0380 A

T3  -- O10 -- T5  = 156.341 deg ; T3  -- T5   3.2957 A

T4  -- O11 -- T4  = 138.699 deg ; T4  -- T4   3.1366 A

T4  -- O12 -- T4  = 121.398 deg ; T4  -- T4   2.8270 A

T4  -- O13 -- T5  = 125.879 deg ; T4  -- T5   2.9071 A


        T-O-T SUMMARY
          Range  = 108.2738° <--> 178.8325 deg
          Mean   = 136.8541 deg
          StdDev = 18.5723 deg

        T--T SUMMARY
          Range  = 2.6288 A <--> 3.2957 A
          Mean   = 2.9900 A
          StdDev = 0.1953 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.
T1  -- T1  = 2.6414 Angstrom
T1  -- T2  = 2.6288 Angstrom
T2  -- T1  = 2.6288 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.0320 Angstrom
  T4  -- T4  = 2.8270 Angstrom
  T4  -- T5  = 2.9071 Angstrom
  T4  -- T4  = 3.1366 Angstrom
  T4  -- T4  = 3.4788 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 39 65 92 124 177 239 294 348 416 506 598 687 780
TD10 = 1066
Circuit symbol = 4.5.4.8_{2}.6.6
Weight = 16
Vertex symbol  = 4.5.4.10_{2}.6.7
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 37 58 88 127 172 222 279 349 422 493 579 677 772
TD10 = 1019
Circuit symbol = 4.5.4.6.6.7
Weight = 11
Vertex symbol  = 4.5.4.6.10.10_{2}
Weight = 25

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 25 45 72 106 147 195 246 304 369 443 518 597 693 793
TD10 = 1156
Circuit symbol = 4.7_{2}.5.8.6.6_{2}
Weight = 17
Vertex symbol  = 4.7.5.10_{2}.6.6_{2}
Weight = 23

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 90 134 186 238 287 347 430 523 607 678 768
TD10 = 1069
Circuit symbol = 4.6_{2}.5.6.6.6_{2}
Weight = 21
Vertex symbol  = 4.6_{2}.5.6.6.6_{2}
Weight = 21

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 24 40 66 102 140 182 238 302 366 422 490 590 690 792
TD10 = 1111
Circuit symbol = 5.5.6.6.6_{2}.7
Weight = 21
Vertex symbol  = 5.5.6.6.6_{2}.7
Weight = 21

<TD10> = 1081.222
Average ring size = 5.8527