Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_74145925_MFysLD.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 21.71 T-atoms per nm^3
Material density = 2.166 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6228 Angstrom
T1  -- O2  = 1.6784 Angstrom
T1  -- O3  = 1.6476 Angstrom
T1  -- O4  = 1.6836 Angstrom
      mean = 1.6581 Angstrom
        t1 = 0.042807  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026667  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6117 Angstrom
T2  -- O5  = 1.6176 Angstrom
T2  -- O6  = 1.5777 Angstrom
T2  -- O7  = 1.6182 Angstrom
      mean = 1.6063 Angstrom
        t1 = 0.028011  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027591  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6947 Angstrom
T3  -- O8  = 1.6026 Angstrom
T3  -- O9  = 1.6037 Angstrom
T3  -- O10 = 1.6497 Angstrom
      mean = 1.6377 Angstrom
        t1 = 0.038226  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023234  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6327 Angstrom
T4  -- O11 = 1.6515 Angstrom
T4  -- O12 = 1.6481 Angstrom
T4  -- O13 = 1.6528 Angstrom
      mean = 1.6463 Angstrom
        t1 = 0.027214  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009733  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.5837 Angstrom
T5  -- O10 = 1.6440 Angstrom
T5  -- O13 = 1.6241 Angstrom
T5  -- O14 = 1.6223 Angstrom
      mean = 1.6185 Angstrom
        t1 = 0.027568  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030177  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5777 A <--> 1.6947 A
          Mean   = 1.6334 A
          StdDev = 0.0304 A

       t1 Range  = 0.0272 <-- 0.0328 --> 0.0428
       t2 Range  = 0.0097 <-- 0.0235 --> 0.0302

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.726 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.878 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.478 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.726 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 117.145 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.341 deg; O3  -- O4  = 3 A
       106.341 deg <-- 109.382 deg --> 117.145 deg

O3  -- T2  -- O5  = 109.189 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.199 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 116.657 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.942 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.796 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 105.008 deg; O6  -- O7  = 3 A
       105.008 deg <-- 109.465 deg --> 116.657 deg

O4  -- T3  -- O8  = 108.686 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 110.488 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 116.570 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 106.207 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.022 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 106.362 deg; O9  -- O10 = 3 A
       106.207 deg <-- 109.389 deg --> 116.570 deg

O7  -- T4  -- O11 = 107.308 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 110.305 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 106.368 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 110.654 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 112.878 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.219 deg; O12 -- O13 = 3 A
       106.368 deg <-- 109.455 deg --> 112.878 deg

O9  -- T5  -- O10 = 106.158 deg; O9  -- O10 = 3 A
O9  -- T5  -- O13 = 104.567 deg; O9  -- O13 = 3 A
O9  -- T5  -- O14 = 109.955 deg; O9  -- O14 = 3 A
O10 -- T5  -- O13 = 115.138 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 110.440 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 110.269 deg; O13 -- O14 = 3 A
       104.567 deg <-- 109.421 deg --> 115.138 deg

        O-T-O SUMMARY
          Range  = 104.5671 deg <--> 117.1455 deg
          Mean   = 109.3867 deg
          StdDev = 3.5309 deg

        O--O SUMMARY
          Range  = 2.5338 A <--> 2.8689 A
          Mean   = 2.6651 A
          StdDev = 0.0817 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.543 deg ; T1  -- T1   2.8324 A

T1  -- O2  -- T1  = 140.031 deg ; T1  -- T1   3.1548 A

T1  -- O3  -- T2  = 127.198 deg ; T1  -- T2   2.9194 A

T1  -- O4  -- T3  = 165.974 deg ; T1  -- T3   3.3530 A

T2  -- O5  -- T2  = 115.966 deg ; T2  -- T2   2.7431 A

T2  -- O6  -- T2  = 131.930 deg ; T2  -- T2   2.8816 A

T2  -- O7  -- T4  = 126.437 deg ; T2  -- T4   2.9022 A

T3  -- O8  -- T3  = 122.058 deg ; T3  -- T3   2.8042 A

T3  -- O9  -- T5  = 119.215 deg ; T3  -- T5   2.7494 A

T3  -- O10 -- T5  = 123.337 deg ; T3  -- T5   2.8992 A

T4  -- O11 -- T4  = 134.874 deg ; T4  -- T4   3.0502 A

T4  -- O12 -- T4  = 160.686 deg ; T4  -- T4   3.2495 A

T4  -- O13 -- T5  = 138.239 deg ; T4  -- T5   3.0616 A

T5  -- O14 -- T5  = 128.566 deg ; T5  -- T5   2.9233 A


        T-O-T SUMMARY
          Range  = 115.9659° <--> 165.9744 deg
          Mean   = 132.5752 deg
          StdDev = 14.2915 deg

        T--T SUMMARY
          Range  = 2.7431 A <--> 3.3530 A
          Mean   = 2.9660 A
          StdDev = 0.1779 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.
T2  -- T2  = 2.7431 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.3530 Angstrom
  T3  -- T3  = 3.0805 Angstrom
  T3  -- T3  = 2.8042 Angstrom
  T3  -- T5  = 2.7494 Angstrom
  T3  -- T5  = 2.8992 Angstrom
T5  -- T3  = 2.7494 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 29 47 73 106 143 177 204 230 268 330 412 494 555
TD10 = 810
Circuit symbol = 4.4.4.8_{7}.6.6_{2}
Weight = 20
Vertex symbol  = 4.4.4.8_{5}.6.10
Weight = 26

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 13 23 41 68 102 137 170 202 237 278 330 396 466 530
TD10 = 769
Circuit symbol = 4.4.4.4.6_{2}.6_{3}
Weight = 12
Vertex symbol  = 4.4.4.4.6.10
Weight = 19

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 33 50 72 96 127 168 207 244 289 343 402 464 528
TD10 = 788
Circuit symbol = 4.4.6.8_{3}.8_{3}.8_{3}
Weight = 21
Vertex symbol  = 4.4.6.8_{3}.8_{2}.8_{2}
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 27 47 75 105 135 167 204 246 294 345 393 444 511
TD10 = 790
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.10
Weight = 20

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 37 55 73 94 125 162 202 257 313 352 391 447 517
TD10 = 784
Circuit symbol = 4.4.6.6_{2}.6_{2}.8_{4}
Weight = 16
Vertex symbol  = 4.4.6.6_{2}.6_{2}.8
Weight = 16

<TD10> = 788.200
Average ring size = 5.6404