Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_71361744_c4nsGM.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 20.29 T-atoms per nm^3
Material density = 2.024 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6179 Angstrom
T1  -- O2  = 1.6164 Angstrom
T1  -- O3  = 1.6173 Angstrom
T1  -- O4  = 1.6174 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.004808  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001240  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6174 Angstrom
T2  -- O5  = 1.6174 Angstrom
T2  -- O6  = 1.6168 Angstrom
T2  -- O7  = 1.6184 Angstrom
      mean = 1.6175 Angstrom
        t1 = 0.005110  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001357  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6188 Angstrom
T3  -- O8  = 1.6216 Angstrom
T3  -- O9  = 1.6296 Angstrom
T3  -- O10 = 1.6320 Angstrom
      mean = 1.6255 Angstrom
        t1 = 0.011439  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004596  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6200 Angstrom
T4  -- O10 = 1.6257 Angstrom
T4  -- O11 = 1.6188 Angstrom
T4  -- O12 = 1.6269 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.010179  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003993  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6207 Angstrom
T5  -- O13 = 1.6258 Angstrom
T5  -- O12 = 1.6290 Angstrom
T5  -- O14 = 1.6241 Angstrom
      mean = 1.6249 Angstrom
        t1 = 0.009620  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003700  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6164 A <--> 1.6320 A
          Mean   = 1.6216 A
          StdDev = 0.0048 A

       t1 Range  = 0.0048 <-- 0.0082 --> 0.0114
       t2 Range  = 0.0012 <-- 0.0030 --> 0.0046

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.091 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.278 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.550 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.515 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.022 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.370 deg; O3  -- O4  = 3 A
       109.091 deg <-- 109.471 deg --> 110.022 deg

O3  -- T2  -- O5  = 109.503 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.434 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.708 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.301 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.958 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.921 deg; O6  -- O7  = 3 A
       108.921 deg <-- 109.471 deg --> 109.958 deg

O4  -- T3  -- O8  = 108.867 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.964 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.758 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.356 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.922 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.942 deg; O9  -- O10 = 3 A
       108.867 deg <-- 109.468 deg --> 110.942 deg

O7  -- T4  -- O10 = 109.082 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.763 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.020 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 108.304 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 111.246 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.410 deg; O11 -- O12 = 3 A
       108.304 deg <-- 109.471 deg --> 111.246 deg

O11 -- T5  -- O13 = 110.178 deg; O11 -- O13 = 3 A
O11 -- T5  -- O12 = 108.636 deg; O11 -- O12 = 3 A
O11 -- T5  -- O14 = 109.635 deg; O11 -- O14 = 3 A
O13 -- T5  -- O12 = 109.160 deg; O13 -- O12 = 3 A
O13 -- T5  -- O14 = 109.608 deg; O13 -- O14 = 3 A
O12 -- T5  -- O14 = 109.606 deg; O12 -- O14 = 3 A
       108.636 deg <-- 109.470 deg --> 110.178 deg

        O-T-O SUMMARY
          Range  = 108.3045 deg <--> 111.2456 deg
          Mean   = 109.4796 deg
          StdDev = 0.6132 deg

        O--O SUMMARY
          Range  = 2.6299 A <--> 2.6871 A
          Mean   = 2.6482 A
          StdDev = 0.0130 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 147.435 deg; T1  -- T1  = 5.7634 A
T1  - O1  - T1  - O3  - T2  = 113.361 deg; T1  -- T2  = 4.9883 A
T1  - O1  - T1  - O4  - T3  =  89.396 deg; T1  -- T3  = 4.2370 A
T1  - O2  - T1  - O3  - T2  =  90.047 deg; T1  -- T2  = 4.3022 A
T1  - O2  - T1  - O4  - T3  =  89.122 deg; T1  -- T3  = 4.3045 A
T2  - O3  - T1  - O4  - T3  = 134.934 deg; T2  -- T3  = 5.6343 A

T1  - O3  - T2  - O5  - T2  = 109.165 deg; T1  -- T2  = 4.9054 A
T1  - O3  - T2  - O6  - T4  =  98.708 deg; T1  -- T4  = 4.5335 A
T1  - O3  - T2  - O7  - T2  =  89.953 deg; T1  -- T2  = 4.3022 A
T2  - O5  - T2  - O6  - T4  = 115.981 deg; T2  -- T4  = 5.0427 A
T2  - O5  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 5.2473 A
T4  - O6  - T2  - O7  - T2  = 116.242 deg; T4  -- T2  = 5.1075 A

T1  - O4  - T3  - O8  - T3  =  90.878 deg; T1  -- T3  = 4.3045 A
T1  - O4  - T3  - O9  - T3  = 109.152 deg; T1  -- T3  = 4.9213 A
T1  - O4  - T3  - O10 - T4  = 110.752 deg; T1  -- T4  = 5.0273 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 5.1322 A
T3  - O8  - T3  - O10 - T4  = 107.705 deg; T3  -- T4  = 4.8425 A
T3  - O9  - T3  - O10 - T4  = 115.581 deg; T3  -- T4  = 5.0726 A

T2  - O7  - T4  - O10 - T3  =  87.128 deg; T2  -- T3  = 4.1243 A
T2  - O7  - T4  - O11 - T5  = 126.734 deg; T2  -- T5  = 5.3024 A
T2  - O7  - T4  - O12 - T5  = 126.027 deg; T2  -- T5  = 5.3168 A
T3  - O10 - T4  - O11 - T5  =  86.553 deg; T3  -- T5  = 4.1225 A
T3  - O10 - T4  - O12 - T5  = 144.927 deg; T3  -- T5  = 5.7669 A
T5  - O11 - T4  - O12 - T5  =  81.810 deg; T5  -- T5  = 3.9262 A

T4  - O11 - T5  - O13 - T5  = 107.552 deg; T4  -- T5  = 4.8334 A
T4  - O11 - T5  - O12 - T5  = 114.325 deg; T4  -- T5  = 5.1313 A
T4  - O11 - T5  - O14 - T4  =  87.860 deg; T4  -- T4  = 4.1598 A
T5  - O13 - T5  - O12 - T5  = 120.000 deg; T5  -- T5  = 5.3148 A
T5  - O13 - T5  - O14 - T4  = 107.344 deg; T5  -- T4  = 4.8548 A
T5  - O12 - T5  - O14 - T4  = 114.984 deg; T5  -- T4  = 5.1792 A

        T-T-T SUMMARY
          Range  = 81.8097 deg <--> 147.4353 deg
          Mean   = 108.1527 deg
          StdDev = 16.8103 deg

        T--T SUMMARY
          Range  = 3.9262 A <--> 5.7669 A
          Mean   = 4.8323 A
          StdDev = 0.5052 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.114 deg ; T1  -- T1   2.9459 A

T1  -- O2  -- T1  = 142.171 deg ; T1  -- T1   3.0582 A

T1  -- O3  -- T2  = 138.360 deg ; T1  -- T2   3.0235 A

T1  -- O4  -- T3  = 143.845 deg ; T1  -- T3   3.0765 A

T2  -- O5  -- T2  = 142.499 deg ; T2  -- T2   3.0632 A

T2  -- O6  -- T2  = 135.765 deg ; T2  -- T2   2.9957 A

T2  -- O7  -- T4  = 131.371 deg ; T2  -- T4   2.9511 A

T3  -- O8  -- T3  = 132.089 deg ; T3  -- T3   2.9639 A

T3  -- O9  -- T3  = 130.714 deg ; T3  -- T3   2.9623 A

T3  -- O10 -- T4  = 137.169 deg ; T3  -- T4   3.0328 A

T4  -- O11 -- T5  = 133.875 deg ; T4  -- T5   2.9806 A

T4  -- O12 -- T5  = 135.664 deg ; T4  -- T5   3.0152 A

T5  -- O13 -- T5  = 135.616 deg ; T5  -- T5   3.0108 A

T5  -- O14 -- T5  = 148.453 deg ; T5  -- T5   3.1258 A


        T-O-T SUMMARY
          Range  = 130.7144° <--> 148.4530 deg
          Mean   = 137.0503 deg
          StdDev = 5.2275 deg

        T--T SUMMARY
          Range  = 2.9459 A <--> 3.1258 A
          Mean   = 3.0147 A
          StdDev = 0.0511 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 83 116 154 195 233 280 332 390 454 528 606
TD10 = 910
Circuit symbol = 4.5.4.5.6_{2}.7_{2}
Weight = 14
Vertex symbol  = 4.5.4.5.6.12
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 57 84 117 156 195 234 275 328 397 468 532 596
TD10 = 918
Circuit symbol = 4.6_{2}.5.6.6.6
Weight = 21
Vertex symbol  = 4.6_{2}.5.6.6.6
Weight = 21

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 34 54 83 116 150 187 233 281 332 389 455 526 600
TD10 = 894
Circuit symbol = 4.6_{2}.5.6.6.6_{2}
Weight = 22
Vertex symbol  = 4.6_{2}.5.6.6.6_{2}
Weight = 22

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 83 113 149 187 228 284 345 401 450 524 604
TD10 = 894
Circuit symbol = 4.5.6.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.5.6.6.6.6_{2}
Weight = 19

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 41 62 86 112 143 185 236 291 346 402 463 524 596
TD10 = 904
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

<TD10> = 904.000
Average ring size = 5.5059