Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_69179168_iQY7xo.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 19.88 T-atoms per nm^3
Material density = 1.983 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6069 Angstrom
T1  -- O2  = 1.6037 Angstrom
T1  -- O3  = 1.6049 Angstrom
T1  -- O4  = 1.6162 Angstrom
      mean = 1.6079 Angstrom
        t1 = 0.006815  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004635  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6125 Angstrom
T2  -- O5  = 1.6208 Angstrom
T2  -- O6  = 1.6311 Angstrom
T2  -- O7  = 1.6267 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.012138  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006963  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6157 Angstrom
T3  -- O8  = 1.6217 Angstrom
T3  -- O9  = 1.6184 Angstrom
T3  -- O10 = 1.6254 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.007937  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003629  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6126 Angstrom
T4  -- O10 = 1.6248 Angstrom
T4  -- O11 = 1.6190 Angstrom
T4  -- O12 = 1.6298 Angstrom
      mean = 1.6215 Angstrom
        t1 = 0.012460  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013814  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6303 Angstrom
T5  -- O13 = 1.6342 Angstrom
T5  -- O12 = 1.6299 Angstrom
T5  -- O14 = 1.6282 Angstrom
      mean = 1.6307 Angstrom
        t1 = 0.014375  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008082  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6037 A <--> 1.6342 A
          Mean   = 1.6207 A
          StdDev = 0.0090 A

       t1 Range  = 0.0068 <-- 0.0107 --> 0.0144
       t2 Range  = 0.0036 <-- 0.0074 --> 0.0138

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.736 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.157 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.032 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.253 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.586 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.045 deg; O3  -- O4  = 3 A
       107.736 deg <-- 109.468 deg --> 110.586 deg

O3  -- T2  -- O5  = 109.343 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.569 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.385 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.367 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.156 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.982 deg; O6  -- O7  = 3 A
       108.385 deg <-- 109.467 deg --> 111.982 deg

O4  -- T3  -- O8  = 109.125 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.255 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 111.060 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.399 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.255 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.725 deg; O9  -- O10 = 3 A
       108.725 deg <-- 109.470 deg --> 111.060 deg

O7  -- T4  -- O10 = 108.823 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 106.936 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 110.954 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 111.175 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.584 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.348 deg; O11 -- O12 = 3 A
       106.936 deg <-- 109.470 deg --> 111.175 deg

O11 -- T5  -- O13 = 111.095 deg; O11 -- O13 = 3 A
O11 -- T5  -- O12 = 107.755 deg; O11 -- O12 = 3 A
O11 -- T5  -- O14 = 109.430 deg; O11 -- O14 = 3 A
O13 -- T5  -- O12 = 109.010 deg; O13 -- O12 = 3 A
O13 -- T5  -- O14 = 109.868 deg; O13 -- O14 = 3 A
O12 -- T5  -- O14 = 109.647 deg; O12 -- O14 = 3 A
       107.755 deg <-- 109.467 deg --> 111.095 deg

        O-T-O SUMMARY
          Range  = 106.9359 deg <--> 111.9824 deg
          Mean   = 109.4953 deg
          StdDev = 1.0923 deg

        O--O SUMMARY
          Range  = 2.5931 A <--> 2.7006 A
          Mean   = 2.6468 A
          StdDev = 0.0231 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 150.000 deg; T1  -- T1  = 5.7221 A
T1  - O1  - T1  - O3  - T2  = 102.356 deg; T1  -- T2  = 4.5644 A
T1  - O1  - T1  - O4  - T3  = 100.610 deg; T1  -- T3  = 4.7220 A
T1  - O2  - T1  - O3  - T2  =  90.011 deg; T1  -- T2  = 4.2049 A
T1  - O2  - T1  - O4  - T3  =  89.611 deg; T1  -- T3  = 4.3851 A
T2  - O3  - T1  - O4  - T3  = 133.755 deg; T2  -- T3  = 5.6604 A

T1  - O3  - T2  - O5  - T2  =  89.989 deg; T1  -- T2  = 4.2049 A
T1  - O3  - T2  - O6  - T2  = 111.787 deg; T1  -- T2  = 4.8016 A
T1  - O3  - T2  - O7  - T4  = 106.668 deg; T1  -- T4  = 4.7586 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.0801 A
T2  - O5  - T2  - O7  - T4  = 106.953 deg; T2  -- T4  = 4.8207 A
T2  - O6  - T2  - O7  - T4  = 117.508 deg; T2  -- T4  = 5.0026 A

T1  - O4  - T3  - O8  - T3  =  90.389 deg; T1  -- T3  = 4.3851 A
T1  - O4  - T3  - O9  - T4  = 102.598 deg; T1  -- T4  = 4.9290 A
T1  - O4  - T3  - O10 - T3  = 107.768 deg; T1  -- T3  = 5.0846 A
T3  - O8  - T3  - O9  - T4  = 116.531 deg; T3  -- T4  = 5.1575 A
T3  - O8  - T3  - O10 - T3  = 120.000 deg; T3  -- T3  = 5.2327 A
T4  - O9  - T3  - O10 - T3  = 114.200 deg; T4  -- T3  = 5.1901 A

T2  - O7  - T4  - O10 - T3  =  85.958 deg; T2  -- T3  = 4.1551 A
T2  - O7  - T4  - O11 - T5  =  85.830 deg; T2  -- T5  = 4.0654 A
T2  - O7  - T4  - O12 - T5  = 146.551 deg; T2  -- T5  = 5.7576 A
T3  - O10 - T4  - O11 - T5  = 128.539 deg; T3  -- T5  = 5.4775 A
T3  - O10 - T4  - O12 - T5  = 125.952 deg; T3  -- T5  = 5.4532 A
T5  - O11 - T4  - O12 - T5  =  81.099 deg; T5  -- T5  = 3.8996 A

T4  - O11 - T5  - O13 - T5  = 106.487 deg; T4  -- T5  = 4.8390 A
T4  - O11 - T5  - O12 - T5  = 114.569 deg; T4  -- T5  = 5.1536 A
T4  - O11 - T5  - O14 - T4  =  89.762 deg; T4  -- T4  = 4.2327 A
T5  - O13 - T5  - O12 - T5  = 120.000 deg; T5  -- T5  = 5.3755 A
T5  - O13 - T5  - O14 - T4  = 106.255 deg; T5  -- T4  = 4.8645 A
T5  - O12 - T5  - O14 - T4  = 115.362 deg; T5  -- T4  = 5.2110 A

        T-T-T SUMMARY
          Range  = 81.0991 deg <--> 150.0000 deg
          Mean   = 108.2395 deg
          StdDev = 16.7664 deg

        T--T SUMMARY
          Range  = 3.8996 A <--> 5.7576 A
          Mean   = 4.8564 A
          StdDev = 0.5106 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.488 deg ; T1  -- T1   2.9183 A

T1  -- O2  -- T1  = 139.126 deg ; T1  -- T1   3.0056 A

T1  -- O3  -- T2  = 132.078 deg ; T1  -- T2   2.9402 A

T1  -- O4  -- T3  = 167.795 deg ; T1  -- T3   3.2136 A

T2  -- O5  -- T2  = 136.101 deg ; T2  -- T2   3.0067 A

T2  -- O6  -- T2  = 122.407 deg ; T2  -- T2   2.8587 A

T2  -- O7  -- T4  = 134.944 deg ; T2  -- T4   2.9921 A

T3  -- O8  -- T3  = 131.908 deg ; T3  -- T3   2.9619 A

T3  -- O9  -- T3  = 144.175 deg ; T3  -- T3   3.0798 A

T3  -- O10 -- T4  = 145.211 deg ; T3  -- T4   3.1016 A

T4  -- O11 -- T5  = 132.886 deg ; T4  -- T5   2.9785 A

T4  -- O12 -- T5  = 135.760 deg ; T4  -- T5   3.0198 A

T5  -- O13 -- T5  = 138.948 deg ; T5  -- T5   3.0610 A

T5  -- O14 -- T5  = 150.049 deg ; T5  -- T5   3.1459 A


        T-O-T SUMMARY
          Range  = 122.4072° <--> 167.7951 deg
          Mean   = 138.7055 deg
          StdDev = 10.4784 deg

        T--T SUMMARY
          Range  = 2.8587 A <--> 3.2136 A
          Mean   = 3.0203 A
          StdDev = 0.0904 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 83 116 154 195 233 280 332 390 454 528 606
TD10 = 910
Circuit symbol = 4.5.4.5.6_{2}.7_{2}
Weight = 14
Vertex symbol  = 4.5.4.5.6.12
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 34 54 83 116 150 187 233 281 332 389 455 526 600
TD10 = 894
Circuit symbol = 4.6_{2}.5.6.6.6_{2}
Weight = 22
Vertex symbol  = 4.6_{2}.5.6.6.6_{2}
Weight = 22

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 57 84 117 156 195 234 275 328 397 468 532 596
TD10 = 918
Circuit symbol = 4.6_{2}.5.6.6.6
Weight = 21
Vertex symbol  = 4.6_{2}.5.6.6.6
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 83 113 149 187 228 284 345 401 450 524 604
TD10 = 894
Circuit symbol = 4.5.6.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.5.6.6.6.6_{2}
Weight = 19

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 41 62 86 112 143 185 236 291 346 402 463 524 596
TD10 = 904
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

<TD10> = 904.000
Average ring size = 5.5059