Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_69179167_TbDiEP.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 19.02 T-atoms per nm^3
Material density = 1.898 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6105 Angstrom
T1  -- O2  = 1.6110 Angstrom
T1  -- O3  = 1.6167 Angstrom
T1  -- O4  = 1.6128 Angstrom
      mean = 1.6127 Angstrom
        t1 = 0.007745  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006992  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6204 Angstrom
T2  -- O5  = 1.6211 Angstrom
T2  -- O6  = 1.6213 Angstrom
T2  -- O7  = 1.6159 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.006383  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001408  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6122 Angstrom
T3  -- O8  = 1.6226 Angstrom
T3  -- O9  = 1.6141 Angstrom
T3  -- O10 = 1.6261 Angstrom
      mean = 1.6188 Angstrom
        t1 = 0.006729  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004874  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6142 Angstrom
T4  -- O10 = 1.6231 Angstrom
T4  -- O11 = 1.6270 Angstrom
T4  -- O12 = 1.6222 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.008737  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003856  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6236 Angstrom
T5  -- O14 = 1.6290 Angstrom
T5  -- O12 = 1.6225 Angstrom
T5  -- O13 = 1.6291 Angstrom
      mean = 1.6260 Angstrom
        t1 = 0.010983  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006812  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6105 A <--> 1.6291 A
          Mean   = 1.6198 A
          StdDev = 0.0058 A

       t1 Range  = 0.0064 <-- 0.0081 --> 0.0110
       t2 Range  = 0.0014 <-- 0.0048 --> 0.0070

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.549 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.692 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.595 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.237 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.195 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.539 deg; O3  -- O4  = 3 A
       107.595 deg <-- 109.468 deg --> 110.692 deg

O3  -- T2  -- O5  = 109.622 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.296 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.925 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.444 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.537 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.003 deg; O6  -- O7  = 3 A
       108.925 deg <-- 109.471 deg --> 110.003 deg

O4  -- T3  -- O8  = 109.209 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.962 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 110.402 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.537 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.377 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.338 deg; O9  -- O10 = 3 A
       108.962 deg <-- 109.471 deg --> 110.402 deg

O7  -- T4  -- O10 = 109.464 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 108.986 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 108.607 deg; O7  -- O12 = 3 A
O10 -- T4  -- O11 = 109.507 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.821 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 110.433 deg; O11 -- O12 = 3 A
       108.607 deg <-- 109.470 deg --> 110.433 deg

O11 -- T5  -- O14 = 109.775 deg; O11 -- O14 = 3 A
O11 -- T5  -- O12 = 108.200 deg; O11 -- O12 = 3 A
O11 -- T5  -- O13 = 109.541 deg; O11 -- O13 = 3 A
O14 -- T5  -- O12 = 109.411 deg; O14 -- O12 = 3 A
O14 -- T5  -- O13 = 109.837 deg; O14 -- O13 = 3 A
O12 -- T5  -- O13 = 110.053 deg; O12 -- O13 = 3 A
       108.200 deg <-- 109.469 deg --> 110.053 deg

        O-T-O SUMMARY
          Range  = 107.5955 deg <--> 110.6922 deg
          Mean   = 109.4790 deg
          StdDev = 0.6862 deg

        O--O SUMMARY
          Range  = 2.6010 A <--> 2.6686 A
          Mean   = 2.6451 A
          StdDev = 0.0146 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 150.000 deg; T1  -- T1  = 5.6826 A
T1  - O1  - T1  - O3  - T2  = 104.125 deg; T1  -- T2  = 4.5792 A
T1  - O1  - T1  - O4  - T3  = 101.327 deg; T1  -- T3  = 4.7495 A
T1  - O2  - T1  - O3  - T2  =  90.666 deg; T1  -- T2  = 4.1641 A
T1  - O2  - T1  - O4  - T3  =  90.374 deg; T1  -- T3  = 4.3907 A
T2  - O3  - T1  - O4  - T3  = 125.608 deg; T2  -- T3  = 5.4341 A

T1  - O3  - T2  - O5  - T2  =  89.334 deg; T1  -- T2  = 4.1641 A
T1  - O3  - T2  - O6  - T2  = 116.492 deg; T1  -- T2  = 4.9268 A
T1  - O3  - T2  - O7  - T4  = 106.330 deg; T1  -- T4  = 4.7118 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.1430 A
T2  - O5  - T2  - O7  - T4  = 107.775 deg; T2  -- T4  = 4.8719 A
T2  - O6  - T2  - O7  - T4  = 113.854 deg; T2  -- T4  = 4.9468 A

T1  - O4  - T3  - O8  - T3  =  89.626 deg; T1  -- T3  = 4.3907 A
T1  - O4  - T3  - O9  - T4  = 101.682 deg; T1  -- T4  = 4.9573 A
T1  - O4  - T3  - O10 - T3  = 110.676 deg; T1  -- T3  = 5.2873 A
T3  - O8  - T3  - O9  - T4  = 120.959 deg; T3  -- T4  = 5.3803 A
T3  - O8  - T3  - O10 - T3  = 120.000 deg; T3  -- T3  = 5.3854 A
T4  - O9  - T3  - O10 - T3  = 109.507 deg; T4  -- T3  = 5.2140 A

T2  - O7  - T4  - O10 - T3  =  87.795 deg; T2  -- T3  = 4.2816 A
T2  - O7  - T4  - O11 - T5  = 145.017 deg; T2  -- T5  = 5.7857 A
T2  - O7  - T4  - O12 - T5  =  95.553 deg; T2  -- T5  = 4.5088 A
T3  - O10 - T4  - O11 - T5  = 118.097 deg; T3  -- T5  = 5.3544 A
T3  - O10 - T4  - O12 - T5  = 134.147 deg; T3  -- T5  = 5.7702 A
T5  - O11 - T4  - O12 - T5  =  83.023 deg; T5  -- T5  = 4.0819 A

T4  - O11 - T5  - O14 - T5  = 106.156 deg; T4  -- T5  = 4.9761 A
T4  - O11 - T5  - O12 - T5  = 120.567 deg; T4  -- T5  = 5.4034 A
T4  - O11 - T5  - O13 - T4  =  88.151 deg; T4  -- T4  = 4.2842 A
T5  - O14 - T5  - O12 - T5  = 120.000 deg; T5  -- T5  = 5.4633 A
T5  - O14 - T5  - O13 - T4  = 106.038 deg; T5  -- T4  = 4.9896 A
T5  - O12 - T5  - O13 - T4  = 110.623 deg; T5  -- T4  = 5.1337 A

        T-T-T SUMMARY
          Range  = 83.0225 deg <--> 150.0000 deg
          Mean   = 108.3930 deg
          StdDev = 15.8802 deg

        T--T SUMMARY
          Range  = 4.0819 A <--> 5.7857 A
          Mean   = 4.9220 A
          StdDev = 0.4983 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.853 deg ; T1  -- T1   2.9174 A

T1  -- O2  -- T1  = 133.982 deg ; T1  -- T1   2.9657 A

T1  -- O3  -- T2  = 126.354 deg ; T1  -- T2   2.8888 A

T1  -- O4  -- T3  = 172.717 deg ; T1  -- T3   3.2185 A

T2  -- O5  -- T2  = 138.600 deg ; T2  -- T2   3.0329 A

T2  -- O6  -- T2  = 127.255 deg ; T2  -- T2   2.9053 A

T2  -- O7  -- T4  = 136.267 deg ; T2  -- T4   2.9977 A

T3  -- O8  -- T3  = 135.891 deg ; T3  -- T3   3.0077 A

T3  -- O9  -- T3  = 167.762 deg ; T3  -- T3   3.2097 A

T3  -- O10 -- T4  = 155.402 deg ; T3  -- T4   3.1746 A

T4  -- O11 -- T5  = 141.469 deg ; T4  -- T5   3.0685 A

T4  -- O12 -- T5  = 144.519 deg ; T4  -- T5   3.0904 A

T5  -- O13 -- T5  = 151.164 deg ; T5  -- T5   3.1556 A

T5  -- O14 -- T5  = 150.811 deg ; T5  -- T5   3.1529 A


        T-O-T SUMMARY
          Range  = 126.3538° <--> 172.7173 deg
          Mean   = 143.7177 deg
          StdDev = 13.8226 deg

        T--T SUMMARY
          Range  = 2.8888 A <--> 3.2185 A
          Mean   = 3.0561 A
          StdDev = 0.1100 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 83 116 154 195 233 280 332 390 454 528 606
TD10 = 910
Circuit symbol = 4.5.4.5.6_{2}.7_{2}
Weight = 14
Vertex symbol  = 4.5.4.5.6.12
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 34 54 83 116 150 187 233 281 332 389 455 526 600
TD10 = 894
Circuit symbol = 4.6_{2}.5.6.6.6_{2}
Weight = 22
Vertex symbol  = 4.6_{2}.5.6.6.6_{2}
Weight = 22

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 57 84 117 156 195 234 275 328 397 468 532 596
TD10 = 918
Circuit symbol = 4.6_{2}.5.6.6.6
Weight = 21
Vertex symbol  = 4.6_{2}.5.6.6.6
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 83 113 149 187 228 284 345 401 450 524 604
TD10 = 894
Circuit symbol = 4.5.6.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.5.6.6.6.6_{2}
Weight = 19

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 41 62 86 112 143 185 236 291 346 402 463 524 596
TD10 = 904
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

<TD10> = 904.000
Average ring size = 5.5059