Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_68334625_IRATPP.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 20.32 T-atoms per nm^3
Material density = 2.028 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7293 Angstrom
T1  -- O2  = 1.7143 Angstrom
T1  -- O3  = 1.6434 Angstrom
T1  -- O4  = 1.5808 Angstrom
      mean = 1.6670 Angstrom
        t1 = 0.076051  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045563  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6656 Angstrom
T2  -- O5  = 1.6157 Angstrom
T2  -- O6  = 1.6287 Angstrom
T2  -- O7  = 1.6546 Angstrom
      mean = 1.6411 Angstrom
        t1 = 0.033988  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020712  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5421 Angstrom
T3  -- O8  = 1.6470 Angstrom
T3  -- O9  = 1.6252 Angstrom
T3  -- O10 = 1.5874 Angstrom
      mean = 1.6004 Angstrom
        t1 = 0.037833  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030776  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.5784 Angstrom
T4  -- O11 = 1.6391 Angstrom
T4  -- O12 = 1.6126 Angstrom
T4  -- O7  = 1.6573 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.028148  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034743  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5689 Angstrom
T5  -- O12 = 1.6146 Angstrom
T5  -- O13 = 1.5991 Angstrom
T5  -- O14 = 1.5991 Angstrom
      mean = 1.5954 Angstrom
        t1 = 0.014426  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008800  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5421 A <--> 1.7293 A
          Mean   = 1.6252 A
          StdDev = 0.0451 A

       t1 Range  = 0.0144 <-- 0.0381 --> 0.0761
       t2 Range  = 0.0088 <-- 0.0281 --> 0.0456

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 122.250 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.891 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.181 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.580 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 102.997 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.591 deg; O3  -- O4  = 2 A
       97.591 deg <-- 108.915 deg --> 122.250 deg

O3  -- T2  -- O5  = 102.997 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 111.568 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 114.453 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 107.160 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 112.283 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.138 deg; O6  -- O7  = 3 A
       102.997 deg <-- 109.433 deg --> 114.453 deg

O4  -- T3  -- O8  = 110.386 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 105.999 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 107.270 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 118.641 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.396 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 106.604 deg; O9  -- O10 = 3 A
       105.999 deg <-- 109.383 deg --> 118.641 deg

O9  -- T4  -- O11 = 116.411 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 104.313 deg; O9  -- O12 = 3 A
O9  -- T4  -- O7  = 106.445 deg; O9  -- O7  = 3 A
O11 -- T4  -- O12 = 109.938 deg; O11 -- O12 = 3 A
O11 -- T4  -- O7  = 110.532 deg; O11 -- O7  = 3 A
O12 -- T4  -- O7  = 108.817 deg; O12 -- O7  = 3 A
       104.313 deg <-- 109.410 deg --> 116.411 deg

O10 -- T5  -- O12 = 108.618 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 109.313 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 108.026 deg; O10 -- O14 = 3 A
O12 -- T5  -- O13 = 110.185 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 110.775 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 109.873 deg; O13 -- O14 = 3 A
       108.026 deg <-- 109.465 deg --> 110.775 deg

        O-T-O SUMMARY
          Range  = 97.5914 deg <--> 122.2496 deg
          Mean   = 109.1225 deg
          StdDev = 4.4270 deg

        O--O SUMMARY
          Range  = 2.4261 A <--> 3.0155 A
          Mean   = 2.6450 A
          StdDev = 0.1038 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 148.587 deg; T1  -- T1  = 6.3280 A
T1  - O1  - T1  - O3  - T2  =  86.458 deg; T1  -- T2  = 4.3601 A
T1  - O1  - T1  - O4  - T3  =  89.281 deg; T1  -- T3  = 4.3054 A
T1  - O2  - T1  - O3  - T2  = 124.704 deg; T1  -- T2  = 5.3515 A
T1  - O2  - T1  - O4  - T3  =  85.419 deg; T1  -- T3  = 3.9330 A
T2  - O3  - T1  - O4  - T3  = 106.677 deg; T2  -- T3  = 4.4476 A

T1  - O3  - T2  - O5  - T2  =  90.490 deg; T1  -- T2  = 4.3601 A
T1  - O3  - T2  - O6  - T2  = 169.726 deg; T1  -- T2  = 5.6543 A
T1  - O3  - T2  - O7  - T4  =  99.092 deg; T1  -- T4  = 4.7036 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2553 A
T2  - O5  - T2  - O7  - T4  = 119.922 deg; T2  -- T4  = 5.6246 A
T2  - O6  - T2  - O7  - T4  =  89.541 deg; T2  -- T4  = 4.2703 A

T1  - O4  - T3  - O8  - T3  =  94.581 deg; T1  -- T3  = 3.9330 A
T1  - O4  - T3  - O9  - T4  = 131.642 deg; T1  -- T4  = 4.8644 A
T1  - O4  - T3  - O10 - T5  = 108.901 deg; T1  -- T5  = 4.2572 A
T3  - O8  - T3  - O9  - T4  = 130.424 deg; T3  -- T4  = 4.9117 A
T3  - O8  - T3  - O10 - T5  =  90.961 deg; T3  -- T5  = 3.7873 A
T4  - O9  - T3  - O10 - T5  =  61.122 deg; T4  -- T5  = 2.6914 A

T3  - O9  - T4  - O11 - T4  = 143.932 deg; T3  -- T4  = 5.1499 A
T3  - O9  - T4  - O12 - T5  =  57.610 deg; T3  -- T5  = 2.5954 A
T3  - O9  - T4  - O7  - T2  = 121.508 deg; T3  -- T2  = 5.2120 A
T4  - O11 - T4  - O12 - T5  =  88.650 deg; T4  -- T5  = 3.7817 A
T4  - O11 - T4  - O7  - T2  =  90.459 deg; T4  -- T2  = 4.2703 A
T5  - O12 - T4  - O7  - T2  = 134.460 deg; T5  -- T2  = 5.5010 A

T3  - O10 - T5  - O12 - T4  =  61.268 deg; T3  -- T4  = 2.6952 A
T3  - O10 - T5  - O13 - T5  =  89.039 deg; T3  -- T5  = 3.7873 A
T3  - O10 - T5  - O14 - T5  = 149.749 deg; T3  -- T5  = 5.0096 A
T4  - O12 - T5  - O13 - T5  = 129.286 deg; T4  -- T5  = 4.9644 A
T4  - O12 - T5  - O14 - T5  =  91.350 deg; T4  -- T5  = 3.7817 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 4.6742 A

        T-T-T SUMMARY
          Range  = 57.6101 deg <--> 169.7259 deg
          Mean   = 105.8086 deg
          StdDev = 27.3816 deg

        T--T SUMMARY
          Range  = 2.5954 A <--> 6.3280 A
          Mean   = 4.4152 A
          StdDev = 0.8521 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.097 deg ; T1  -- T1   3.4366 A

T1  -- O2  -- T1  = 132.328 deg ; T1  -- T1   3.1362 A

T1  -- O3  -- T2  = 122.704 deg ; T1  -- T2   2.9039 A

T1  -- O4  -- T3  = 115.204 deg ; T1  -- T3   2.6369 A

T2  -- O5  -- T2  = 174.526 deg ; T2  -- T2   3.2276 A

T2  -- O6  -- T2  = 116.712 deg ; T2  -- T2   2.7732 A

T2  -- O7  -- T4  = 161.672 deg ; T2  -- T4   3.2696 A

T3  -- O8  -- T3  = 111.021 deg ; T3  -- T3   2.7150 A

T3  -- O9  -- T4  = 114.549 deg ; T3  -- T4   2.6952 A

T3  -- O10 -- T5  = 110.626 deg ; T3  -- T5   2.5954 A

T4  -- O11 -- T4  = 112.186 deg ; T4  -- T4   2.7208 A

T4  -- O12 -- T5  = 113.011 deg ; T4  -- T5   2.6914 A

T5  -- O13 -- T5  = 122.365 deg ; T5  -- T5   2.8021 A

T5  -- O14 -- T5  = 108.392 deg ; T5  -- T5   2.5940 A


        T-O-T SUMMARY
          Range  = 108.3925° <--> 174.5265 deg
          Mean   = 127.3139 deg
          StdDev = 22.0940 deg

        T--T SUMMARY
          Range  = 2.5940 A <--> 3.4366 A
          Mean   = 2.8713 A
          StdDev = 0.2688 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T3  = 2.6369 Angstrom
T2  -- T2  = 2.7732 Angstrom
T3  -- T1  = 2.6369 Angstrom
T3  -- T3  = 2.7150 Angstrom
T3  -- T4  = 2.6952 Angstrom
T3  -- T5  = 2.5954 Angstrom
T4  -- T3  = 2.6952 Angstrom
T4  -- T4  = 2.7208 Angstrom
T4  -- T5  = 2.6914 Angstrom
T5  -- T3  = 2.5954 Angstrom
T5  -- T4  = 2.6914 Angstrom
T5  -- T5  = 2.5940 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 34 51 74 102 140 183 225 265 312 377 448 517 593
TD10 = 845
Circuit symbol = 4.4.8.8_{2}.8_{2}.8_{2}
Weight = 30
Vertex symbol  = 4.4.8.8_{2}.8_{2}.8_{2}
Weight = 30

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 33 50 68 92 123 161 209 269 330 376 416 474 553
TD10 = 768
Circuit symbol = 4.4.4.8_{4}.6.6
Weight = 19
Vertex symbol  = 4.4.4.8_{3}.12.22_{9}
Weight = 67

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 15 27 41 64 94 125 164 206 246 290 352 432 512 578
TD10 = 749
Circuit symbol = 3.4.4.7.5.6
Weight = 7
Vertex symbol  = 3.4.4.8_{2}.8.8
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 14 25 42 63 89 119 154 204 261 309 356 415 482 558
TD10 = 723
Circuit symbol = 3.4.4.7.5.6
Weight = 7
Vertex symbol  = 3.4.4.8_{2}.8.8
Weight = 21

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 13 21 35 57 86 121 157 196 241 285 333 396 483 575
TD10 = 699
Circuit symbol = 3.6.4.4.5.5
Weight = 10
Vertex symbol  = 3.6.4.4.8.8
Weight = 20

<TD10> = 756.800
Average ring size = 6.5132