Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_60067696_R3bbKi.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 28.72 T-atoms per nm^3
Material density = 2.865 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6715 Angstrom
T1  -- O2  = 1.6839 Angstrom
T1  -- O3  = 1.7086 Angstrom
T1  -- O4  = 1.6820 Angstrom
      mean = 1.6865 Angstrom
        t1 = 0.055820  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026989  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.7817 Angstrom
T2  -- O6  = 1.3999 Angstrom
T2  -- O7  = 1.6878 Angstrom
T2  -- O3  = 1.6897 Angstrom
      mean = 1.6398 Angstrom
        t1 = 0.204439  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.219854  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6316 Angstrom
T3  -- O8  = 1.6761 Angstrom
T3  -- O9  = 1.6633 Angstrom
T3  -- O10 = 1.6425 Angstrom
      mean = 1.6534 Angstrom
        t1 = 0.115884  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.104966  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.3688 Angstrom
T4  -- O11 = 1.5713 Angstrom
T4  -- O12 = 1.5480 Angstrom
T4  -- O9  = 1.6683 Angstrom
      mean = 1.5391 Angstrom
        t1 = 0.079681  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.087144  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.5775 Angstrom
T5  -- O10 = 1.6838 Angstrom
T5  -- O13 = 1.6205 Angstrom
T5  -- O14 = 1.6747 Angstrom
      mean = 1.6391 Angstrom
        t1 = 0.099373  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.145734  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.3688 A <--> 1.7817 A
          Mean   = 1.6316 A
          StdDev = 0.0969 A

       t1 Range  = 0.0558 <-- 0.1110 --> 0.2044
       t2 Range  = 0.0270 <-- 0.1169 --> 0.2199

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.456 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 104.120 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.663 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.309 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 103.146 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 113.356 deg; O3  -- O4  = 3 A
       103.146 deg <-- 109.508 deg --> 114.309 deg

O5  -- T2  -- O6  =  69.085 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 135.196 deg; O5  -- O7  = 3 A
O5  -- T2  -- O3  = 129.352 deg; O5  -- O3  = 3 A
O6  -- T2  -- O7  =  78.715 deg; O6  -- O7  = 2 A
O6  -- T2  -- O3  = 109.385 deg; O6  -- O3  = 3 A
O7  -- T2  -- O3  =  89.921 deg; O7  -- O3  = 2 A
       69.085 deg <-- 101.942 deg --> 135.196 deg

O4  -- T3  -- O8  = 101.521 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 130.880 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  79.020 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 106.836 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 124.851 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 113.562 deg; O9  -- O10 = 3 A
       79.020 deg <-- 109.445 deg --> 130.880 deg

O6  -- T4  -- O11 = 106.310 deg; O6  -- O11 = 2 A
O6  -- T4  -- O12 =  98.584 deg; O6  -- O12 = 2 A
O6  -- T4  -- O9  = 112.757 deg; O6  -- O9  = 3 A
O11 -- T4  -- O12 = 112.987 deg; O11 -- O12 = 3 A
O11 -- T4  -- O9  = 111.741 deg; O11 -- O9  = 3 A
O12 -- T4  -- O9  = 113.569 deg; O12 -- O9  = 3 A
       98.584 deg <-- 109.325 deg --> 113.569 deg

O7  -- T5  -- O10 = 120.291 deg; O7  -- O10 = 3 A
O7  -- T5  -- O13 =  82.258 deg; O7  -- O13 = 2 A
O7  -- T5  -- O14 = 109.135 deg; O7  -- O14 = 3 A
O10 -- T5  -- O13 = 113.508 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 107.949 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 122.477 deg; O13 -- O14 = 3 A
       82.258 deg <-- 109.270 deg --> 122.477 deg

        O-T-O SUMMARY
          Range  = 69.0849 deg <--> 135.1959 deg
          Mean   = 107.4906 deg
          StdDev = 15.5134 deg

        O--O SUMMARY
          Range  = 1.8313 A <--> 3.2079 A
          Mean   = 2.6144 A
          StdDev = 0.3269 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.877 deg ; T1  -- T1   3.1091 A

T1  -- O2  -- T1  = 136.333 deg ; T1  -- T1   3.1264 A

T1  -- O3  -- T2  = 125.977 deg ; T1  -- T2   3.0276 A

T1  -- O4  -- T3  = 136.405 deg ; T1  -- T3   3.0767 A

T2  -- O5  -- T2  = 169.996 deg ; T2  -- T2   3.5499 A

T2  -- O6  -- T4  = 131.512 deg ; T2  -- T4   2.5245 A

T2  -- O7  -- T5  = 153.439 deg ; T2  -- T5   3.1781 A

T3  -- O8  -- T3  = 105.598 deg ; T3  -- T3   2.6701 A

T3  -- O9  -- T4  = 175.344 deg ; T3  -- T4   3.3288 A

T3  -- O10 -- T5  = 137.706 deg ; T3  -- T5   3.1024 A

T4  -- O11 -- T4  = 121.204 deg ; T4  -- T4   2.7380 A

T4  -- O12 -- T4  = 101.660 deg ; T4  -- T4   2.4004 A

T5  -- O13 -- T5  = 158.514 deg ; T5  -- T5   3.1842 A

T5  -- O14 -- T5  = 120.265 deg ; T5  -- T5   2.9046 A


        T-O-T SUMMARY
          Range  = 101.6601° <--> 175.3444 deg
          Mean   = 136.4879 deg
          StdDev = 21.0752 deg

        T--T SUMMARY
          Range  = 2.4004 A <--> 3.5499 A
          Mean   = 2.9943 A
          StdDev = 0.3042 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O10 = 2.0831 A
O5  -- O6  = 1.8313 A
O5  -- O6  = 1.8313 A
O6  -- O7  = 1.9707 A
O6  -- O12 = 2.2141 A
O7  -- O13 = 2.1038 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1264 Angstrom
  T1  -- T2  = 3.4656 Angstrom
  T1  -- T3  = 3.0767 Angstrom
  T1  -- T5  = 3.2894 Angstrom
  T1  -- T1  = 3.1091 Angstrom
  T1  -- T2  = 3.0276 Angstrom
T2  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.4656 Angstrom
  T2  -- T4  = 2.5245 Angstrom
  T2  -- T5  = 3.1781 Angstrom
  T2  -- T5  = 3.4758 Angstrom
  T2  -- T1  = 3.0276 Angstrom
  T2  -- T2  = 2.1271 Angstrom
T3  -- T3  = 2.6701 Angstrom
T4  -- T2  = 2.5245 Angstrom
T4  -- T4  = 2.7380 Angstrom
T4  -- T4  = 2.4004 Angstrom
T5  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 3.2894 Angstrom
  T5  -- T2  = 3.1781 Angstrom
  T5  -- T2  = 3.4758 Angstrom
  T5  -- T3  = 3.1024 Angstrom
  T5  -- T5  = 3.1842 Angstrom
  T5  -- T5  = 2.9046 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 42 70 105 144 189 241 299 361 434 516 601 690 788
TD10 = 1129
Circuit symbol = 4.5.5.6_{2}.7.7_{2}
Weight = 16
Vertex symbol  = 4.5.5.6_{2}.7.8
Weight = 20

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 25 45 70 102 141 185 240 306 372 439 514 600 692 792
TD10 = 1130
Circuit symbol = 4.5.6.6.6.8_{2}
Weight = 19
Vertex symbol  = 4.5.6.6.6.8
Weight = 19

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 24 43 67 102 142 186 235 296 369 436 505 592 690 780
TD10 = 1110
Circuit symbol = 4.5.4.6.6.7
Weight = 12
Vertex symbol  = 4.5.4.6.8.8
Weight = 19

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 39 66 100 139 183 233 293 363 440 514 592 682 784
TD10 = 1089
Circuit symbol = 4.4.6.6_{2}.6.7
Weight = 20
Vertex symbol  = 4.4.6.6_{2}.6.7
Weight = 20

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 26 47 73 106 146 194 251 310 370 443 528 613 698 792
TD10 = 1170
Circuit symbol = 5.6.6.6.6_{2}.7_{2}
Weight = 25
Vertex symbol  = 5.6.6.6.6_{2}.7_{2}
Weight = 25

<TD10> = 1125.600
Average ring size = 5.6000