Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_58715018_GGMBam.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.80 T-atoms per nm^3
Material density = 2.474 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5761 Angstrom
T1  -- O2  = 1.6169 Angstrom
T1  -- O3  = 1.5813 Angstrom
T1  -- O4  = 1.5964 Angstrom
      mean = 1.5927 Angstrom
        t1 = 0.022912  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024558  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6099 Angstrom
T2  -- O5  = 1.5521 Angstrom
T2  -- O6  = 1.6414 Angstrom
T2  -- O7  = 1.6722 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.047982  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032675  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5981 Angstrom
T3  -- O5  = 1.5384 Angstrom
T3  -- O8  = 1.5898 Angstrom
T3  -- O9  = 1.6098 Angstrom
      mean = 1.5840 Angstrom
        t1 = 0.021088  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008739  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6350 Angstrom
T4  -- O11 = 1.7093 Angstrom
T4  -- O12 = 1.6589 Angstrom
T4  -- O6  = 1.6556 Angstrom
      mean = 1.6647 Angstrom
        t1 = 0.047809  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031084  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6648 Angstrom
T5  -- O12 = 1.6796 Angstrom
T5  -- O13 = 1.5904 Angstrom
T5  -- O14 = 1.6898 Angstrom
      mean = 1.6561 Angstrom
        t1 = 0.107834  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.120278  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5384 A <--> 1.7093 A
          Mean   = 1.6233 A
          StdDev = 0.0459 A

       t1 Range  = 0.0211 <-- 0.0495 --> 0.1078
       t2 Range  = 0.0087 <-- 0.0435 --> 0.1203

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.469 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.522 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.413 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.670 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.052 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.485 deg; O3  -- O4  = 3 A
       105.522 deg <-- 109.435 deg --> 112.485 deg

O3  -- T2  -- O5  = 102.897 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 111.755 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 111.086 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 101.915 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 110.878 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 117.007 deg; O6  -- O7  = 3 A
       101.915 deg <-- 109.256 deg --> 117.007 deg

O4  -- T3  -- O5  = 109.291 deg; O4  -- O5  = 3 A
O4  -- T3  -- O8  = 108.460 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.524 deg; O4  -- O9  = 3 A
O5  -- T3  -- O8  = 108.617 deg; O5  -- O8  = 3 A
O5  -- T3  -- O9  = 109.422 deg; O5  -- O9  = 3 A
O8  -- T3  -- O9  = 111.491 deg; O8  -- O9  = 3 A
       108.460 deg <-- 109.468 deg --> 111.491 deg

O10 -- T4  -- O11 = 108.192 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 105.279 deg; O10 -- O12 = 3 A
O10 -- T4  -- O6  = 107.671 deg; O10 -- O6  = 3 A
O11 -- T4  -- O12 = 115.670 deg; O11 -- O12 = 3 A
O11 -- T4  -- O6  = 114.121 deg; O11 -- O6  = 3 A
O12 -- T4  -- O6  = 105.313 deg; O12 -- O6  = 3 A
       105.279 deg <-- 109.374 deg --> 115.670 deg

O7  -- T5  -- O12 = 101.494 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 =  86.603 deg; O7  -- O13 = 2 A
O7  -- T5  -- O14 = 108.118 deg; O7  -- O14 = 3 A
O12 -- T5  -- O13 =  94.726 deg; O12 -- O13 = 2 A
O12 -- T5  -- O14 = 117.055 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 140.145 deg; O13 -- O14 = 3 A
       86.603 deg <-- 108.023 deg --> 140.145 deg

        O-T-O SUMMARY
          Range  = 86.6028 deg <--> 140.1446 deg
          Mean   = 108.5068 deg
          StdDev = 7.6006 deg

        O--O SUMMARY
          Range  = 2.2332 A <--> 3.0840 A
          Mean   = 2.6293 A
          StdDev = 0.1472 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 168.520 deg ; T1  -- T1   3.1364 A

T1  -- O2  -- T1  = 130.873 deg ; T1  -- T1   2.9410 A

T1  -- O3  -- T2  = 142.797 deg ; T1  -- T2   3.0245 A

T1  -- O4  -- T3  = 159.003 deg ; T1  -- T3   3.1410 A

T2  -- O5  -- T3  = 128.943 deg ; T2  -- T3   2.7888 A

T2  -- O6  -- T4  = 143.349 deg ; T2  -- T4   3.1298 A

T2  -- O7  -- T5  = 141.772 deg ; T2  -- T5   3.1530 A

T3  -- O8  -- T3  = 130.688 deg ; T3  -- T3   2.8898 A

T3  -- O9  -- T3  = 114.025 deg ; T3  -- T3   2.7005 A

T4  -- O10 -- T4  = 132.507 deg ; T4  -- T4   2.9932 A

T4  -- O11 -- T4  = 168.910 deg ; T4  -- T4   3.4029 A

T4  -- O12 -- T5  = 156.495 deg ; T4  -- T5   3.2685 A

T5  -- O13 -- T5  = 111.119 deg ; T5  -- T5   2.6233 A

T5  -- O14 -- T5  = 102.056 deg ; T5  -- T5   2.6275 A


        T-O-T SUMMARY
          Range  = 102.0558° <--> 168.9103 deg
          Mean   = 137.9327 deg
          StdDev = 19.9155 deg

        T--T SUMMARY
          Range  = 2.6233 A <--> 3.4029 A
          Mean   = 2.9872 A
          StdDev = 0.2305 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O13 = 2.2332 A

T-T-T analysis was not conducted.
T2  -- T3  = 2.7888 Angstrom
T3  -- T2  = 2.7888 Angstrom
T3  -- T3  = 2.7005 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T4  = 2.9932 Angstrom
  T4  -- T4  = 3.4029 Angstrom
  T4  -- T5  = 3.3619 Angstrom
  T4  -- T5  = 3.2685 Angstrom
  T4  -- T2  = 3.1298 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.1530 Angstrom
  T5  -- T4  = 3.3619 Angstrom
  T5  -- T4  = 3.2685 Angstrom
  T5  -- T5  = 2.6233 Angstrom
  T5  -- T5  = 2.6275 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 24 38 60 88 120 158 196 238 292 348 408 474 540 614
TD10 = 939
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 940.600
Average ring size = 5.7600