Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_58398864_Km9Eyo.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 26.95 T-atoms per nm^3
Material density = 2.689 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6604 Angstrom
T1  -- O2  = 1.6843 Angstrom
T1  -- O3  = 1.5917 Angstrom
T1  -- O4  = 1.6732 Angstrom
      mean = 1.6524 Angstrom
        t1 = 0.065417  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066878  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5335 Angstrom
T2  -- O5  = 1.6318 Angstrom
T2  -- O6  = 1.6151 Angstrom
T2  -- O7  = 1.4642 Angstrom
      mean = 1.5612 Angstrom
        t1 = 0.075273  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.047318  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.7134 Angstrom
T3  -- O7  = 1.5443 Angstrom
T3  -- O8  = 1.6098 Angstrom
T3  -- O9  = 1.6395 Angstrom
      mean = 1.6268 Angstrom
        t1 = 0.176327  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.130373  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.6220 Angstrom
T4  -- O10 = 1.6168 Angstrom
T4  -- O11 = 1.5607 Angstrom
T4  -- O12 = 1.6401 Angstrom
      mean = 1.6099 Angstrom
        t1 = 0.042196  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035919  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6478 Angstrom
T5  -- O13 = 1.6676 Angstrom
T5  -- O14 = 1.6685 Angstrom
T5  -- O12 = 1.6613 Angstrom
      mean = 1.6613 Angstrom
        t1 = 0.033948  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009388  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4642 A <--> 1.7134 A
          Mean   = 1.6223 A
          StdDev = 0.0580 A

       t1 Range  = 0.0339 <-- 0.0786 --> 0.1763
       t2 Range  = 0.0094 <-- 0.0580 --> 0.1304

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 122.703 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  98.127 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 107.623 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 101.612 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.298 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 118.988 deg; O3  -- O4  = 3 A
       98.127 deg <-- 109.558 deg --> 122.703 deg

O3  -- T2  -- O5  = 115.297 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 111.936 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  92.379 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 112.474 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.796 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.405 deg; O6  -- O7  = 3 A
       92.379 deg <-- 109.215 deg --> 115.297 deg

O4  -- T3  -- O7  = 130.362 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 107.138 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  =  68.426 deg; O4  -- O9  = 2 A
O7  -- T3  -- O8  = 104.680 deg; O7  -- O8  = 2 A
O7  -- T3  -- O9  =  73.415 deg; O7  -- O9  = 2 A
O8  -- T3  -- O9  =  91.980 deg; O8  -- O9  = 2 A
       68.426 deg <-- 96.000 deg --> 130.362 deg

O8  -- T4  -- O10 = 108.776 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 104.949 deg; O8  -- O11 = 3 A
O8  -- T4  -- O12 = 120.174 deg; O8  -- O12 = 3 A
O10 -- T4  -- O11 = 107.765 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 111.346 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 102.846 deg; O11 -- O12 = 3 A
       102.846 deg <-- 109.309 deg --> 120.174 deg

O9  -- T5  -- O13 = 107.052 deg; O9  -- O13 = 3 A
O9  -- T5  -- O14 = 111.242 deg; O9  -- O14 = 3 A
O9  -- T5  -- O12 = 107.609 deg; O9  -- O12 = 3 A
O13 -- T5  -- O14 = 110.739 deg; O13 -- O14 = 3 A
O13 -- T5  -- O12 = 110.351 deg; O13 -- O12 = 3 A
O14 -- T5  -- O12 = 109.772 deg; O14 -- O12 = 3 A
       107.052 deg <-- 109.461 deg --> 111.242 deg

        O-T-O SUMMARY
          Range  = 68.4257 deg <--> 130.3616 deg
          Mean   = 106.2292 deg
          StdDev = 12.5118 deg

        O--O SUMMARY
          Range  = 1.8863 A <--> 2.9577 A
          Mean   = 2.5792 A
          StdDev = 0.2462 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 137.850 deg ; T1  -- T1   3.0986 A

T1  -- O2  -- T1  = 119.958 deg ; T1  -- T1   2.9167 A

T1  -- O3  -- T2  = 151.867 deg ; T1  -- T2   3.0314 A

T1  -- O4  -- T3  = 157.546 deg ; T1  -- T3   3.3218 A

T2  -- O5  -- T2  = 118.468 deg ; T2  -- T2   2.8042 A

T2  -- O6  -- T2  = 106.901 deg ; T2  -- T2   2.5951 A

T2  -- O7  -- T3  = 124.823 deg ; T2  -- T3   2.6667 A

T3  -- O8  -- T4  = 163.427 deg ; T3  -- T4   3.1981 A

T3  -- O9  -- T5  = 166.115 deg ; T3  -- T5   3.2632 A

T4  -- O10 -- T4  = 111.310 deg ; T4  -- T4   2.6697 A

T4  -- O11 -- T4  = 153.051 deg ; T4  -- T4   3.0354 A

T4  -- O12 -- T5  = 130.127 deg ; T4  -- T5   2.9936 A

T5  -- O13 -- T5  = 160.586 deg ; T5  -- T5   3.2874 A

T5  -- O14 -- T5  = 175.386 deg ; T5  -- T5   3.3342 A


        T-O-T SUMMARY
          Range  = 106.9010° <--> 175.3858 deg
          Mean   = 141.2440 deg
          StdDev = 21.7678 deg

        T--T SUMMARY
          Range  = 2.5951 A <--> 3.3342 A
          Mean   = 3.0154 A
          StdDev = 0.2458 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O7  = 2.1638 A
O4  -- O9  = 1.8863 A
O7  -- O9  = 1.9046 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.9167 Angstrom
  T1  -- T2  = 3.0314 Angstrom
  T1  -- T3  = 2.7832 Angstrom
  T1  -- T3  = 3.3218 Angstrom
  T1  -- T5  = 3.4960 Angstrom
  T1  -- T1  = 3.0986 Angstrom
T2  -- T2  = 2.5951 Angstrom
T2  -- T3  = 2.6667 Angstrom
T3  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.7832 Angstrom
  T3  -- T1  = 3.3218 Angstrom
  T3  -- T2  = 2.6667 Angstrom
  T3  -- T3  = 2.7176 Angstrom
  T3  -- T4  = 3.1981 Angstrom
  T3  -- T5  = 3.2632 Angstrom
T4  -- T4  = 2.6697 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 3.4960 Angstrom
  T5  -- T3  = 3.2632 Angstrom
  T5  -- T5  = 3.2874 Angstrom
  T5  -- T5  = 3.3342 Angstrom
  T5  -- T4  = 2.9936 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 24 38 60 88 120 158 196 238 292 348 408 474 540 614
TD10 = 939
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 940.600
Average ring size = 5.7600