Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_56100440_w5UFNc.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 21.81 T-atoms per nm^3
Material density = 2.176 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6195 Angstrom
T1  -- O2  = 1.6167 Angstrom
T1  -- O3  = 1.6255 Angstrom
T1  -- O4  = 1.6262 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.008494  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003717  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6242 Angstrom
T2  -- O5  = 1.6233 Angstrom
T2  -- O6  = 1.6239 Angstrom
T2  -- O7  = 1.6194 Angstrom
      mean = 1.6227 Angstrom
        t1 = 0.008317  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001785  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6218 Angstrom
T3  -- O7  = 1.6197 Angstrom
T3  -- O8  = 1.6173 Angstrom
T3  -- O9  = 1.6210 Angstrom
      mean = 1.6200 Angstrom
        t1 = 0.007291  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005128  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.6148 Angstrom
T4  -- O10 = 1.6163 Angstrom
T4  -- O11 = 1.6194 Angstrom
T4  -- O12 = 1.6188 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.004916  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001460  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6189 Angstrom
T5  -- O13 = 1.6216 Angstrom
T5  -- O14 = 1.6211 Angstrom
T5  -- O12 = 1.6191 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.006338  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000587  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6148 A <--> 1.6262 A
          Mean   = 1.6204 A
          StdDev = 0.0030 A

       t1 Range  = 0.0049 <-- 0.0071 --> 0.0085
       t2 Range  = 0.0006 <-- 0.0025 --> 0.0051

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.848 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.101 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.634 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.133 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.128 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.973 deg; O3  -- O4  = 3 A
       108.848 deg <-- 109.469 deg --> 110.101 deg

O3  -- T2  -- O5  = 109.780 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.511 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.655 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.513 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.642 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.725 deg; O6  -- O7  = 3 A
       108.655 deg <-- 109.471 deg --> 109.780 deg

O4  -- T3  -- O7  = 110.199 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 108.358 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.667 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 109.403 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.811 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.378 deg; O8  -- O9  = 3 A
       108.358 deg <-- 109.469 deg --> 110.199 deg

O8  -- T4  -- O10 = 109.842 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 109.276 deg; O8  -- O11 = 3 A
O8  -- T4  -- O12 = 109.563 deg; O8  -- O12 = 3 A
O10 -- T4  -- O11 = 109.568 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 108.902 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.676 deg; O11 -- O12 = 3 A
       108.902 deg <-- 109.471 deg --> 109.842 deg

O9  -- T5  -- O13 = 109.335 deg; O9  -- O13 = 3 A
O9  -- T5  -- O14 = 109.615 deg; O9  -- O14 = 3 A
O9  -- T5  -- O12 = 109.619 deg; O9  -- O12 = 3 A
O13 -- T5  -- O14 = 109.413 deg; O13 -- O14 = 3 A
O13 -- T5  -- O12 = 109.405 deg; O13 -- O12 = 3 A
O14 -- T5  -- O12 = 109.440 deg; O14 -- O12 = 3 A
       109.335 deg <-- 109.471 deg --> 109.619 deg

        O-T-O SUMMARY
          Range  = 108.3576 deg <--> 110.1991 deg
          Mean   = 109.4800 deg
          StdDev = 0.4019 deg

        O--O SUMMARY
          Range  = 2.6265 A <--> 2.6632 A
          Mean   = 2.6463 A
          StdDev = 0.0083 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  91.652 deg; T1  -- T2  = 4.2578 A
T1  - O1  - T1  - O3  - T3  = 114.309 deg; T1  -- T3  = 4.9354 A
T1  - O1  - T1  - O4  - T1  = 123.286 deg; T1  -- T1  = 5.1967 A
T2  - O2  - T1  - O3  - T3  = 100.381 deg; T2  -- T3  = 4.5946 A
T2  - O2  - T1  - O4  - T1  = 116.155 deg; T2  -- T1  = 5.1025 A
T3  - O3  - T1  - O4  - T1  = 108.058 deg; T3  -- T1  = 4.8159 A

T1  - O3  - T2  - O5  - T2  =  88.348 deg; T1  -- T2  = 4.2578 A
T1  - O3  - T2  - O6  - T3  = 105.096 deg; T1  -- T3  = 4.8640 A
T1  - O3  - T2  - O7  - T2  = 120.397 deg; T1  -- T2  = 5.3465 A
T2  - O5  - T2  - O6  - T3  = 111.364 deg; T2  -- T3  = 5.1161 A
T2  - O5  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 5.3943 A
T3  - O6  - T2  - O7  - T2  = 109.535 deg; T3  -- T2  = 5.1016 A

T1  - O4  - T3  - O7  - T2  = 126.954 deg; T1  -- T2  = 5.4276 A
T1  - O4  - T3  - O8  - T4  = 108.138 deg; T1  -- T4  = 4.8876 A
T1  - O4  - T3  - O9  - T5  =  98.137 deg; T1  -- T5  = 4.5513 A
T2  - O7  - T3  - O8  - T4  = 111.085 deg; T2  -- T4  = 5.0968 A
T2  - O7  - T3  - O9  - T5  =  88.084 deg; T2  -- T5  = 4.2889 A
T4  - O8  - T3  - O9  - T5  = 124.263 deg; T4  -- T5  = 5.4272 A

T3  - O8  - T4  - O10 - T4  = 100.795 deg; T3  -- T4  = 4.8199 A
T3  - O8  - T4  - O11 - T4  = 110.396 deg; T3  -- T4  = 5.0490 A
T3  - O8  - T4  - O12 - T5  = 108.286 deg; T3  -- T5  = 4.9634 A
T4  - O10 - T4  - O11 - T4  = 111.703 deg; T4  -- T4  = 5.1750 A
T4  - O10 - T4  - O12 - T5  = 135.028 deg; T4  -- T5  = 5.7545 A
T4  - O11 - T4  - O12 - T5  =  89.565 deg; T4  -- T5  = 4.3122 A

T3  - O9  - T5  - O13 - T5  = 110.942 deg; T3  -- T5  = 5.0177 A
T3  - O9  - T5  - O14 - T5  = 112.375 deg; T3  -- T5  = 5.0539 A
T3  - O9  - T5  - O12 - T4  = 107.403 deg; T3  -- T4  = 4.9260 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 5.2360 A
T5  - O13 - T5  - O12 - T4  =  90.435 deg; T5  -- T4  = 4.3122 A
T5  - O14 - T5  - O12 - T4  = 113.241 deg; T5  -- T4  = 5.0666 A

        T-T-T SUMMARY
          Range  = 88.0837 deg <--> 135.0275 deg
          Mean   = 109.2161 deg
          StdDev = 11.7909 deg

        T--T SUMMARY
          Range  = 4.2578 A <--> 5.7545 A
          Mean   = 4.9449 A
          StdDev = 0.3785 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.842 deg ; T1  -- T1   2.9906 A

T1  -- O2  -- T1  = 128.665 deg ; T1  -- T1   2.9145 A

T1  -- O3  -- T2  = 136.757 deg ; T1  -- T2   3.0210 A

T1  -- O4  -- T3  = 131.369 deg ; T1  -- T3   2.9599 A

T2  -- O5  -- T2  = 150.524 deg ; T2  -- T2   3.1400 A

T2  -- O6  -- T2  = 143.959 deg ; T2  -- T2   3.0888 A

T2  -- O7  -- T3  = 146.988 deg ; T2  -- T3   3.1057 A

T3  -- O8  -- T4  = 144.196 deg ; T3  -- T4   3.0756 A

T3  -- O9  -- T5  = 142.021 deg ; T3  -- T5   3.0636 A

T4  -- O10 -- T4  = 159.223 deg ; T4  -- T4   3.1794 A

T4  -- O11 -- T4  = 143.202 deg ; T4  -- T4   3.0733 A

T4  -- O12 -- T5  = 140.604 deg ; T4  -- T5   3.0484 A

T5  -- O13 -- T5  = 137.918 deg ; T5  -- T5   3.0270 A

T5  -- O14 -- T5  = 137.242 deg ; T5  -- T5   3.0190 A


        T-O-T SUMMARY
          Range  = 128.6654° <--> 159.2233 deg
          Mean   = 141.2507 deg
          StdDev = 7.6009 deg

        T--T SUMMARY
          Range  = 2.9145 A <--> 3.1794 A
          Mean   = 3.0505 A
          StdDev = 0.0672 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 24 38 60 88 120 158 196 238 292 348 408 474 540 614
TD10 = 939
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 940.600
Average ring size = 5.7600