Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_56080964_LKcIig.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 26.12 T-atoms per nm^3
Material density = 2.606 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6612 Angstrom
T1  -- O3  = 1.6256 Angstrom
T1  -- O4  = 1.5138 Angstrom
T1  -- O2  = 1.6823 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.081795  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.051867  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5191 Angstrom
T2  -- O5  = 1.6305 Angstrom
T2  -- O7  = 1.7385 Angstrom
T2  -- O6  = 1.6905 Angstrom
      mean = 1.6447 Angstrom
        t1 = 0.095148  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060293  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.4423 Angstrom
T3  -- O8  = 1.7667 Angstrom
T3  -- O9  = 1.8624 Angstrom
T3  -- O10 = 1.3858 Angstrom
      mean = 1.6143 Angstrom
        t1 = 0.143312  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090963  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.7324 Angstrom
T4  -- O9  = 1.7660 Angstrom
T4  -- O11 = 1.6248 Angstrom
T4  -- O12 = 1.5948 Angstrom
      mean = 1.6795 Angstrom
        t1 = 0.080389  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045540  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.7539 Angstrom
T5  -- O10 = 1.4931 Angstrom
T5  -- O13 = 1.5936 Angstrom
T5  -- O14 = 1.5926 Angstrom
      mean = 1.6083 Angstrom
        t1 = 0.052248  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048065  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.3858 A <--> 1.8624 A
          Mean   = 1.6335 A
          StdDev = 0.1183 A

       t1 Range  = 0.0522 <-- 0.0906 --> 0.1433
       t2 Range  = 0.0455 <-- 0.0593 --> 0.0910

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 108.634 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.708 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 116.634 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  =  92.768 deg; O3  -- O4  = 2 A
O3  -- T1  -- O2  = 123.136 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 101.223 deg; O4  -- O2  = 2 A
       92.768 deg <-- 108.850 deg --> 123.136 deg

O3  -- T2  -- O5  = 110.732 deg; O3  -- O5  = 3 A
O3  -- T2  -- O7  = 106.161 deg; O3  -- O7  = 3 A
O3  -- T2  -- O6  =  89.842 deg; O3  -- O6  = 2 A
O5  -- T2  -- O7  = 108.772 deg; O5  -- O7  = 3 A
O5  -- T2  -- O6  = 109.076 deg; O5  -- O6  = 3 A
O7  -- T2  -- O6  = 129.779 deg; O7  -- O6  = 3 A
       89.842 deg <-- 109.060 deg --> 129.779 deg

O4  -- T3  -- O8  = 104.167 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 104.683 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 105.135 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 140.951 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 101.529 deg; O8  -- O10 = 2 A
O9  -- T3  -- O10 =  95.721 deg; O9  -- O10 = 2 A
       95.721 deg <-- 108.698 deg --> 140.951 deg

O6  -- T4  -- O9  = 123.808 deg; O6  -- O9  = 3 A
O6  -- T4  -- O11 = 113.037 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 104.938 deg; O6  -- O12 = 3 A
O9  -- T4  -- O11 = 106.957 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 104.050 deg; O9  -- O12 = 3 A
O11 -- T4  -- O12 = 101.277 deg; O11 -- O12 = 2 A
       101.277 deg <-- 109.011 deg --> 123.808 deg

O7  -- T5  -- O10 =  91.739 deg; O7  -- O10 = 2 A
O7  -- T5  -- O13 = 110.922 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 108.967 deg; O7  -- O14 = 3 A
O10 -- T5  -- O13 = 118.538 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 114.181 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 110.694 deg; O13 -- O14 = 3 A
       91.739 deg <-- 109.173 deg --> 118.538 deg

        O-T-O SUMMARY
          Range  = 89.8421 deg <--> 140.9512 deg
          Mean   = 108.9283 deg
          StdDev = 10.9391 deg

        O--O SUMMARY
          Range  = 2.2460 A <--> 3.4206 A
          Mean   = 2.6535 A
          StdDev = 0.2539 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.805 deg ; T1  -- T1   2.9709 A

T1  -- O2  -- T1  = 137.636 deg ; T1  -- T1   3.1374 A

T1  -- O3  -- T2  = 119.912 deg ; T1  -- T2   2.7227 A

T1  -- O4  -- T3  =  95.367 deg ; T1  -- T3   2.1864 A

T2  -- O5  -- T2  = 129.151 deg ; T2  -- T2   2.9452 A

T2  -- O6  -- T4  = 146.777 deg ; T2  -- T4   3.2801 A

T2  -- O7  -- T5  = 151.439 deg ; T2  -- T5   3.3845 A

T3  -- O8  -- T3  = 113.608 deg ; T3  -- T3   2.9570 A

T3  -- O9  -- T4  = 146.541 deg ; T3  -- T4   3.4749 A

T3  -- O10 -- T5  = 106.060 deg ; T3  -- T5   2.3010 A

T4  -- O11 -- T4  = 170.016 deg ; T4  -- T4   3.2373 A

T4  -- O12 -- T4  = 126.484 deg ; T4  -- T4   2.8479 A

T5  -- O13 -- T5  = 109.578 deg ; T5  -- T5   2.6040 A

T5  -- O14 -- T5  = 114.596 deg ; T5  -- T5   2.6802 A


        T-O-T SUMMARY
          Range  = 95.3670° <--> 170.0161 deg
          Mean   = 128.1408 deg
          StdDev = 19.7437 deg

        T--T SUMMARY
          Range  = 2.1864 A <--> 3.4749 A
          Mean   = 2.9092 A
          StdDev = 0.3714 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.2742 A
O3  -- O6  = 2.2697 A
O4  -- O10 = 2.2460 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1374 Angstrom
  T1  -- T2  = 2.7227 Angstrom
  T1  -- T3  = 2.1864 Angstrom
  T1  -- T1  = 2.9709 Angstrom
  T1  -- T4  = 3.0369 Angstrom
T2  -- T1  = 2.7227 Angstrom
T3  -- T1  = 2.1864 Angstrom
T3  -- T5  = 2.3010 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 3.4749 Angstrom
  T4  -- T4  = 3.2373 Angstrom
  T4  -- T4  = 2.8479 Angstrom
  T4  -- T1  = 3.0369 Angstrom
  T4  -- T2  = 3.2801 Angstrom
T5  -- T3  = 2.3010 Angstrom
T5  -- T5  = 2.6040 Angstrom
T5  -- T5  = 2.6802 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 42 70 105 144 189 241 299 361 434 516 601 690 788
TD10 = 1129
Circuit symbol = 4.5.5.6_{2}.7.7_{2}
Weight = 16
Vertex symbol  = 4.5.5.6_{2}.7.8
Weight = 20

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 25 45 70 102 141 185 240 306 372 439 514 600 692 792
TD10 = 1130
Circuit symbol = 4.5.6.6.6.8_{2}
Weight = 19
Vertex symbol  = 4.5.6.6.6.8
Weight = 19

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 24 43 67 102 142 186 235 296 369 436 505 592 690 780
TD10 = 1110
Circuit symbol = 4.5.4.6.6.7
Weight = 12
Vertex symbol  = 4.5.4.6.8.8
Weight = 19

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 26 47 73 106 146 194 251 310 370 443 528 613 698 792
TD10 = 1170
Circuit symbol = 5.6.6.6.6_{2}.7_{2}
Weight = 25
Vertex symbol  = 5.6.6.6.6_{2}.7_{2}
Weight = 25

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 39 66 100 139 183 233 293 363 440 514 592 682 784
TD10 = 1089
Circuit symbol = 4.4.6.6_{2}.6.7
Weight = 20
Vertex symbol  = 4.4.6.6_{2}.6.7
Weight = 20

<TD10> = 1125.600
Average ring size = 5.6000