Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_56023252_8EwT7p.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 17.49 T-atoms per nm^3
Material density = 1.745 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6128 Angstrom
T1  -- O2  = 1.5927 Angstrom
T1  -- O3  = 1.6260 Angstrom
T1  -- O4  = 1.6377 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.020165  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013253  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6316 Angstrom
T2  -- O5  = 1.6248 Angstrom
T2  -- O6  = 1.6296 Angstrom
T2  -- O7  = 1.6095 Angstrom
      mean = 1.6239 Angstrom
        t1 = 0.012916  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009897  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6256 Angstrom
T3  -- O8  = 1.6114 Angstrom
T3  -- O9  = 1.6164 Angstrom
T3  -- O10 = 1.6408 Angstrom
      mean = 1.6236 Angstrom
        t1 = 0.017539  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6232 Angstrom
T4  -- O9  = 1.6047 Angstrom
T4  -- O11 = 1.6236 Angstrom
T4  -- O12 = 1.5819 Angstrom
      mean = 1.6083 Angstrom
        t1 = 0.015747  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012423  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6416 Angstrom
T5  -- O12 = 1.5879 Angstrom
T5  -- O13 = 1.6262 Angstrom
T5  -- O14 = 1.6319 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.014455  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009441  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5819 A <--> 1.6416 A
          Mean   = 1.6190 A
          StdDev = 0.0165 A

       t1 Range  = 0.0129 <-- 0.0162 --> 0.0202
       t2 Range  = 0.0094 <-- 0.0120 --> 0.0149

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.971 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.379 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.398 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 106.996 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.978 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.817 deg; O3  -- O4  = 3 A
       106.971 deg <-- 109.423 deg --> 112.817 deg

O3  -- T2  -- O5  = 109.937 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.795 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.838 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.741 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.480 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.002 deg; O6  -- O7  = 3 A
       106.838 deg <-- 109.466 deg --> 110.795 deg

O4  -- T3  -- O8  = 108.928 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 106.849 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 111.691 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 107.827 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.126 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 112.289 deg; O9  -- O10 = 3 A
       106.849 deg <-- 109.452 deg --> 112.289 deg

O7  -- T4  -- O9  = 111.600 deg; O7  -- O9  = 3 A
O7  -- T4  -- O11 = 109.840 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 107.792 deg; O7  -- O12 = 3 A
O9  -- T4  -- O11 = 110.855 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 106.620 deg; O9  -- O12 = 3 A
O11 -- T4  -- O12 = 110.035 deg; O11 -- O12 = 3 A
       106.620 deg <-- 109.457 deg --> 111.600 deg

O10 -- T5  -- O12 = 106.357 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 109.586 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 109.502 deg; O10 -- O14 = 3 A
O12 -- T5  -- O13 = 109.408 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 111.742 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 110.162 deg; O13 -- O14 = 3 A
       106.357 deg <-- 109.459 deg --> 111.742 deg

        O-T-O SUMMARY
          Range  = 106.3569 deg <--> 112.8167 deg
          Mean   = 109.4773 deg
          StdDev = 1.8000 deg

        O--O SUMMARY
          Range  = 2.5553 A <--> 2.7187 A
          Mean   = 2.6436 A
          StdDev = 0.0405 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.569 deg; T1  -- T2  = 4.3190 A
T1  - O1  - T1  - O3  - T3  = 110.446 deg; T1  -- T3  = 5.1398 A
T1  - O1  - T1  - O4  - T1  = 115.279 deg; T1  -- T1  = 5.3028 A
T2  - O2  - T1  - O3  - T3  =  91.812 deg; T2  -- T3  = 4.3241 A
T2  - O2  - T1  - O4  - T1  = 118.667 deg; T2  -- T1  = 5.1950 A
T3  - O3  - T1  - O4  - T1  = 123.301 deg; T3  -- T1  = 5.4763 A

T1  - O3  - T2  - O5  - T2  = 146.629 deg; T1  -- T2  = 5.7189 A
T1  - O3  - T2  - O6  - T2  =  89.431 deg; T1  -- T2  = 4.3190 A
T1  - O3  - T2  - O7  - T4  =  89.273 deg; T1  -- T4  = 4.1574 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.4283 A
T2  - O5  - T2  - O7  - T4  =  88.849 deg; T2  -- T4  = 4.2368 A
T2  - O6  - T2  - O7  - T4  = 119.813 deg; T2  -- T4  = 5.3772 A

T1  - O4  - T3  - O8  - T3  = 115.761 deg; T1  -- T3  = 5.2745 A
T1  - O4  - T3  - O9  - T4  =  85.552 deg; T1  -- T4  = 4.1574 A
T1  - O4  - T3  - O10 - T5  = 137.660 deg; T1  -- T5  = 5.8061 A
T3  - O8  - T3  - O9  - T4  = 140.313 deg; T3  -- T4  = 5.7815 A
T3  - O8  - T3  - O10 - T5  =  89.619 deg; T3  -- T5  = 4.4059 A
T4  - O9  - T3  - O10 - T5  =  95.793 deg; T4  -- T5  = 4.5598 A

T2  - O7  - T4  - O9  - T3  =  91.839 deg; T2  -- T3  = 4.3241 A
T2  - O7  - T4  - O11 - T4  =  91.151 deg; T2  -- T4  = 4.2368 A
T2  - O7  - T4  - O12 - T5  = 107.417 deg; T2  -- T5  = 4.7463 A
T3  - O9  - T4  - O11 - T4  = 156.098 deg; T3  -- T4  = 5.8235 A
T3  - O9  - T4  - O12 - T5  = 110.129 deg; T3  -- T5  = 4.8443 A
T4  - O11 - T4  - O12 - T5  =  91.511 deg; T4  -- T5  = 4.1702 A

T3  - O10 - T5  - O12 - T4  = 116.277 deg; T3  -- T4  = 5.1092 A
T3  - O10 - T5  - O13 - T5  =  90.381 deg; T3  -- T5  = 4.4059 A
T3  - O10 - T5  - O14 - T5  = 111.615 deg; T3  -- T5  = 5.0837 A
T4  - O12 - T5  - O13 - T5  =  88.489 deg; T4  -- T5  = 4.1702 A
T4  - O12 - T5  - O14 - T5  = 123.354 deg; T4  -- T5  = 5.2019 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 5.2874 A

        T-T-T SUMMARY
          Range  = 85.5522 deg <--> 156.0979 deg
          Mean   = 108.8330 deg
          StdDev = 19.4378 deg

        T--T SUMMARY
          Range  = 4.1574 A <--> 5.8235 A
          Mean   = 4.8725 A
          StdDev = 0.5727 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 150.806 deg ; T1  -- T1   3.1214 A

T1  -- O2  -- T1  = 164.452 deg ; T1  -- T1   3.1563 A

T1  -- O3  -- T2  = 127.130 deg ; T1  -- T2   2.9170 A

T1  -- O4  -- T3  = 143.721 deg ; T1  -- T3   3.1011 A

T2  -- O5  -- T2  = 139.959 deg ; T2  -- T2   3.0531 A

T2  -- O6  -- T2  = 160.957 deg ; T2  -- T2   3.2142 A

T2  -- O7  -- T4  = 136.203 deg ; T2  -- T4   2.9995 A

T3  -- O8  -- T3  = 151.939 deg ; T3  -- T3   3.1265 A

T3  -- O9  -- T4  = 139.277 deg ; T3  -- T4   3.0199 A

T3  -- O10 -- T5  = 144.391 deg ; T3  -- T5   3.1252 A

T4  -- O11 -- T4  = 129.150 deg ; T4  -- T4   2.9326 A

T4  -- O12 -- T5  = 131.369 deg ; T4  -- T5   2.8886 A

T5  -- O13 -- T5  = 143.077 deg ; T5  -- T5   3.0849 A

T5  -- O14 -- T5  = 135.469 deg ; T5  -- T5   3.0204 A


        T-O-T SUMMARY
          Range  = 127.1304° <--> 164.4522 deg
          Mean   = 142.7072 deg
          StdDev = 10.8001 deg

        T--T SUMMARY
          Range  = 2.8886 A <--> 3.2142 A
          Mean   = 3.0543 A
          StdDev = 0.0928 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 34 51 69 90 120 159 199 236 274 316 364 423 493
TD10 = 757
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 21
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 29 47 72 100 127 153 183 223 273 328 382 431 480
TD10 = 742
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 33 50 70 92 122 157 194 236 276 318 370 428 491
TD10 = 753
Circuit symbol = 4.4.6.6.6.8_{3}
Weight = 17
Vertex symbol  = 4.4.6.6.6.12
Weight = 25

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 31 47 70 98 126 155 186 223 273 332 385 430 478
TD10 = 745
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.12
Weight = 23

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 30 46 70 100 130 157 186 223 270 325 383 437 486
TD10 = 753
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 750.000
Average ring size = 5.2174