Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_55473051_gNSNnX.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 17.05 T-atoms per nm^3
Material density = 1.701 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6159 Angstrom
T1  -- O2  = 1.6189 Angstrom
T1  -- O3  = 1.6229 Angstrom
T1  -- O4  = 1.6188 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.006676  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002812  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6231 Angstrom
T2  -- O5  = 1.6184 Angstrom
T2  -- O6  = 1.6227 Angstrom
T2  -- O7  = 1.6223 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.007400  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001919  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6184 Angstrom
T3  -- O8  = 1.6236 Angstrom
T3  -- O9  = 1.6168 Angstrom
T3  -- O10 = 1.6202 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.006723  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002354  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6218 Angstrom
T4  -- O11 = 1.6179 Angstrom
T4  -- O12 = 1.6210 Angstrom
T4  -- O9  = 1.6169 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006538  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003053  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6196 Angstrom
T5  -- O11 = 1.6179 Angstrom
T5  -- O12 = 1.6217 Angstrom
T5  -- O13 = 1.6186 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001024  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6159 A <--> 1.6236 A
          Mean   = 1.6199 A
          StdDev = 0.0023 A

       t1 Range  = 0.0060 <-- 0.0067 --> 0.0074
       t2 Range  = 0.0010 <-- 0.0022 --> 0.0031

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.333 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.882 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.590 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.466 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.548 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.004 deg; O3  -- O4  = 3 A
       108.590 deg <-- 109.470 deg --> 110.004 deg

O3  -- T2  -- O5  = 109.487 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.760 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.382 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.456 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.168 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.573 deg; O6  -- O7  = 3 A
       109.168 deg <-- 109.471 deg --> 109.760 deg

O4  -- T3  -- O8  = 109.558 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.315 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.235 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 110.007 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.800 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.907 deg; O9  -- O10 = 3 A
       108.907 deg <-- 109.470 deg --> 110.007 deg

O7  -- T4  -- O11 = 109.448 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.889 deg; O7  -- O12 = 3 A
O7  -- T4  -- O9  = 109.788 deg; O7  -- O9  = 3 A
O11 -- T4  -- O12 = 109.216 deg; O11 -- O12 = 3 A
O11 -- T4  -- O9  = 108.780 deg; O11 -- O9  = 3 A
O12 -- T4  -- O9  = 109.698 deg; O12 -- O9  = 3 A
       108.780 deg <-- 109.470 deg --> 109.889 deg

O10 -- T5  -- O11 = 109.571 deg; O10 -- O11 = 3 A
O10 -- T5  -- O12 = 109.501 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 109.396 deg; O10 -- O13 = 3 A
O11 -- T5  -- O12 = 109.591 deg; O11 -- O12 = 3 A
O11 -- T5  -- O13 = 109.165 deg; O11 -- O13 = 3 A
O12 -- T5  -- O13 = 109.603 deg; O12 -- O13 = 3 A
       109.165 deg <-- 109.471 deg --> 109.603 deg

        O-T-O SUMMARY
          Range  = 108.5898 deg <--> 110.0068 deg
          Mean   = 109.4732 deg
          StdDev = 0.3350 deg

        O--O SUMMARY
          Range  = 2.6267 A <--> 2.6556 A
          Mean   = 2.6453 A
          StdDev = 0.0071 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  91.980 deg; T1  -- T2  = 4.3438 A
T1  - O1  - T1  - O3  - T3  =  89.947 deg; T1  -- T3  = 4.2905 A
T1  - O1  - T1  - O4  - T1  = 118.047 deg; T1  -- T1  = 5.2751 A
T2  - O2  - T1  - O3  - T3  =  84.081 deg; T2  -- T3  = 4.0773 A
T2  - O2  - T1  - O4  - T1  = 124.053 deg; T2  -- T1  = 5.4496 A
T3  - O3  - T1  - O4  - T1  = 136.433 deg; T3  -- T1  = 5.7583 A

T1  - O3  - T2  - O5  - T2  =  88.020 deg; T1  -- T2  = 4.3438 A
T1  - O3  - T2  - O6  - T2  = 117.832 deg; T1  -- T2  = 5.2805 A
T1  - O3  - T2  - O7  - T4  =  93.873 deg; T1  -- T4  = 4.4392 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.5052 A
T2  - O5  - T2  - O7  - T4  = 108.946 deg; T2  -- T4  = 5.1016 A
T2  - O6  - T2  - O7  - T4  = 120.729 deg; T2  -- T4  = 5.3751 A

T1  - O4  - T3  - O8  - T3  =  90.053 deg; T1  -- T3  = 4.2905 A
T1  - O4  - T3  - O9  - T5  = 125.715 deg; T1  -- T5  = 5.4359 A
T1  - O4  - T3  - O10 - T4  =  92.434 deg; T1  -- T4  = 4.4392 A
T3  - O8  - T3  - O9  - T5  =  90.194 deg; T3  -- T5  = 4.2882 A
T3  - O8  - T3  - O10 - T4  = 110.798 deg; T3  -- T4  = 5.0165 A
T5  - O9  - T3  - O10 - T4  = 137.057 deg; T5  -- T4  = 5.7121 A

T5  - O7  - T4  - O11 - T5  =  84.573 deg; T5  -- T5  = 4.0822 A
T5  - O7  - T4  - O12 - T2  = 117.210 deg; T5  -- T2  = 5.2092 A
T5  - O7  - T4  - O9  - T3  = 144.809 deg; T5  -- T3  = 5.8570 A
T5  - O11 - T4  - O12 - T2  = 134.677 deg; T5  -- T2  = 5.5912 A
T5  - O11 - T4  - O9  - T3  = 101.206 deg; T5  -- T3  = 4.7147 A
T2  - O12 - T4  - O9  - T3  =  83.276 deg; T2  -- T3  = 4.0773 A

T3  - O10 - T5  - O11 - T4  = 139.290 deg; T3  -- T4  = 5.7231 A
T3  - O10 - T5  - O12 - T4  = 105.558 deg; T3  -- T4  = 4.8262 A
T3  - O10 - T5  - O13 - T5  =  89.806 deg; T3  -- T5  = 4.2882 A
T4  - O11 - T5  - O12 - T4  =  87.321 deg; T4  -- T4  = 4.1887 A
T4  - O11 - T5  - O13 - T5  = 121.856 deg; T4  -- T5  = 5.3149 A
T4  - O12 - T5  - O13 - T5  = 111.148 deg; T4  -- T5  = 4.9800 A

        T-T-T SUMMARY
          Range  = 83.2763 deg <--> 144.8095 deg
          Mean   = 108.7908 deg
          StdDev = 18.9976 deg

        T--T SUMMARY
          Range  = 4.0773 A <--> 5.8570 A
          Mean   = 4.9086 A
          StdDev = 0.5882 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 152.835 deg ; T1  -- T1   3.1414 A

T1  -- O2  -- T1  = 136.828 deg ; T1  -- T1   3.0107 A

T1  -- O3  -- T2  = 137.849 deg ; T1  -- T2   3.0289 A

T1  -- O4  -- T3  = 141.869 deg ; T1  -- T3   3.0596 A

T2  -- O5  -- T2  = 168.324 deg ; T2  -- T2   3.2200 A

T2  -- O6  -- T2  = 150.232 deg ; T2  -- T2   3.1366 A

T2  -- O7  -- T4  = 139.882 deg ; T2  -- T4   3.0473 A

T3  -- O8  -- T3  = 135.472 deg ; T3  -- T3   3.0050 A

T3  -- O9  -- T4  = 145.603 deg ; T3  -- T4   3.0891 A

T3  -- O10 -- T5  = 140.478 deg ; T3  -- T5   3.0490 A

T4  -- O11 -- T5  = 141.548 deg ; T4  -- T5   3.0553 A

T4  -- O12 -- T5  = 136.482 deg ; T4  -- T5   3.0116 A

T5  -- O13 -- T5  = 138.354 deg ; T5  -- T5   3.0257 A


        T-O-T SUMMARY
          Range  = 135.4719° <--> 168.3236 deg
          Mean   = 143.5196 deg
          StdDev = 8.7730 deg

        T--T SUMMARY
          Range  = 3.0050 A <--> 3.2200 A
          Mean   = 3.0677 A
          StdDev = 0.0611 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 30 49 72 97 128 164 197 234 283 338 393 452 518
TD10 = 768
Circuit symbol = 4.6.4.6.4.8_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.10_{4}
Weight = 25

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 31 48 72 103 135 166 199 235 278 332 399 466 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{4}
Weight = 20
Vertex symbol  = 4.6.4.6.6.6_{3}
Weight = 20

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 33 51 70 93 123 157 194 240 290 334 381 442 508
TD10 = 753
Circuit symbol = 4.4.4.6.6.6_{4}
Weight = 14
Vertex symbol  = 4.4.4.6.6_{3}.10_{4}
Weight = 24

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 31 50 74 96 124 161 200 242 287 334 388 451 512
TD10 = 770
Circuit symbol = 4.4.6.6_{2}.6.8_{3}
Weight = 17
Vertex symbol  = 4.4.6.6_{2}.6.10_{2}
Weight = 23

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 32 51 71 93 122 159 200 238 285 342 390 435 502
TD10 = 762
Circuit symbol = 4.4.6.6.6_{2}.8_{2}
Weight = 17
Vertex symbol  = 4.4.6.6.6_{2}.10_{4}
Weight = 30

<TD10> = 768.200
Average ring size = 5.9483