Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_53434619_IEfavO.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 25.41 T-atoms per nm^3
Material density = 2.535 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6205 Angstrom
T1  -- O2  = 1.7006 Angstrom
T1  -- O3  = 1.6643 Angstrom
T1  -- O4  = 1.6410 Angstrom
      mean = 1.6566 Angstrom
        t1 = 0.106906  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.083544  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6407 Angstrom
T2  -- O5  = 1.6785 Angstrom
T2  -- O6  = 1.6179 Angstrom
T2  -- O7  = 1.6264 Angstrom
      mean = 1.6409 Angstrom
        t1 = 0.038113  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024713  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6419 Angstrom
T3  -- O7  = 1.6181 Angstrom
T3  -- O8  = 1.6003 Angstrom
T3  -- O9  = 1.6124 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.021265  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014452  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.6136 Angstrom
T4  -- O10 = 1.6295 Angstrom
T4  -- O11 = 1.6376 Angstrom
T4  -- O12 = 1.5688 Angstrom
      mean = 1.6124 Angstrom
        t1 = 0.023588  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016970  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5668 Angstrom
T5  -- O13 = 1.6125 Angstrom
T5  -- O14 = 1.6063 Angstrom
T5  -- O9  = 1.6135 Angstrom
      mean = 1.5998 Angstrom
        t1 = 0.011973  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010866  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5668 A <--> 1.7006 A
          Mean   = 1.6256 A
          StdDev = 0.0311 A

       t1 Range  = 0.0120 <-- 0.0404 --> 0.1069
       t2 Range  = 0.0109 <-- 0.0301 --> 0.0835

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 140.795 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  96.036 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  =  87.965 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 115.997 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 105.865 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 101.456 deg; O3  -- O4  = 3 A
       87.965 deg <-- 108.019 deg --> 140.795 deg

O3  -- T2  -- O5  = 116.419 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.058 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 104.613 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 107.253 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 113.964 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 107.000 deg; O6  -- O7  = 3 A
       104.613 deg <-- 109.385 deg --> 116.419 deg

O4  -- T3  -- O7  = 114.864 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 110.710 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.126 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 106.577 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 107.346 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.059 deg; O8  -- O9  = 3 A
       106.577 deg <-- 109.447 deg --> 114.864 deg

O8  -- T4  -- O10 = 110.393 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 110.171 deg; O8  -- O11 = 3 A
O8  -- T4  -- O12 = 105.827 deg; O8  -- O12 = 3 A
O10 -- T4  -- O11 = 113.401 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 108.313 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 108.415 deg; O11 -- O12 = 3 A
       105.827 deg <-- 109.420 deg --> 113.401 deg

O12 -- T5  -- O13 = 109.057 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 108.567 deg; O12 -- O14 = 3 A
O12 -- T5  -- O9  = 109.230 deg; O12 -- O9  = 3 A
O13 -- T5  -- O14 = 110.125 deg; O13 -- O14 = 3 A
O13 -- T5  -- O9  = 109.809 deg; O13 -- O9  = 3 A
O14 -- T5  -- O9  = 110.025 deg; O14 -- O9  = 3 A
       108.567 deg <-- 109.469 deg --> 110.125 deg

        O-T-O SUMMARY
          Range  = 87.9646 deg <--> 140.7953 deg
          Mean   = 108.5232 deg
          StdDev = 7.0916 deg

        O--O SUMMARY
          Range  = 2.2649 A <--> 3.1287 A
          Mean   = 2.6327 A
          StdDev = 0.1270 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 110.800 deg ; T1  -- T1   2.6678 A

T1  -- O2  -- T1  = 103.900 deg ; T1  -- T1   2.6783 A

T1  -- O3  -- T2  = 161.207 deg ; T1  -- T2   3.2607 A

T1  -- O4  -- T3  = 147.674 deg ; T1  -- T3   3.1531 A

T2  -- O5  -- T2  = 158.530 deg ; T2  -- T2   3.2981 A

T2  -- O6  -- T2  = 127.901 deg ; T2  -- T2   2.9071 A

T2  -- O7  -- T3  = 146.286 deg ; T2  -- T3   3.1051 A

T3  -- O8  -- T4  = 138.807 deg ; T3  -- T4   3.0084 A

T3  -- O9  -- T5  = 128.106 deg ; T3  -- T5   2.9008 A

T4  -- O10 -- T4  = 154.012 deg ; T4  -- T4   3.1754 A

T4  -- O11 -- T4  = 125.328 deg ; T4  -- T4   2.9095 A

T4  -- O12 -- T5  = 168.434 deg ; T4  -- T5   3.1197 A

T5  -- O13 -- T5  = 117.774 deg ; T5  -- T5   2.7610 A

T5  -- O14 -- T5  = 119.461 deg ; T5  -- T5   2.7746 A


        T-O-T SUMMARY
          Range  = 103.8998° <--> 168.4339 deg
          Mean   = 136.3015 deg
          StdDev = 19.4413 deg

        T--T SUMMARY
          Range  = 2.6678 A <--> 3.2981 A
          Mean   = 2.9800 A
          StdDev = 0.2036 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2649 A
O1  -- O4  = 2.2649 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.6678 Angstrom
  T1  -- T1  = 2.6783 Angstrom
  T1  -- T2  = 3.3517 Angstrom
  T1  -- T2  = 3.2607 Angstrom
  T1  -- T3  = 3.1531 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.3517 Angstrom
  T2  -- T1  = 3.2607 Angstrom
  T2  -- T2  = 2.9071 Angstrom
  T2  -- T3  = 3.1051 Angstrom
  T2  -- T2  = 3.2981 Angstrom
T5  -- T5  = 2.7610 Angstrom
T5  -- T5  = 2.7746 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 12 24 38 60 88 120 158 196 238 292 348 408 474 540 614
TD10 = 939
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

<TD10> = 940.600
Average ring size = 5.7600