Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_49274912_1yVlhe.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.81 T-atoms per nm^3
Material density = 2.476 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6304 Angstrom
T1  -- O2  = 1.6429 Angstrom
T1  -- O3  = 1.5981 Angstrom
T1  -- O4  = 1.5809 Angstrom
      mean = 1.6131 Angstrom
        t1 = 0.033392  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023744  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5832 Angstrom
T2  -- O5  = 1.6401 Angstrom
T2  -- O6  = 1.6125 Angstrom
T2  -- O7  = 1.6332 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.034232  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022124  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6194 Angstrom
T3  -- O8  = 1.6279 Angstrom
T3  -- O9  = 1.7756 Angstrom
T3  -- O10 = 1.6552 Angstrom
      mean = 1.6695 Angstrom
        t1 = 0.063199  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035839  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6679 Angstrom
T4  -- O12 = 1.6061 Angstrom
T4  -- O11 = 1.6152 Angstrom
T4  -- O13 = 1.6130 Angstrom
      mean = 1.6255 Angstrom
        t1 = 0.023978  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013837  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6798 Angstrom
T5  -- O10 = 1.6109 Angstrom
T5  -- O13 = 1.6153 Angstrom
T5  -- O14 = 1.7123 Angstrom
      mean = 1.6546 Angstrom
        t1 = 0.078247  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049075  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5809 A <--> 1.7756 A
          Mean   = 1.6360 A
          StdDev = 0.0446 A

       t1 Range  = 0.0240 <-- 0.0466 --> 0.0782
       t2 Range  = 0.0138 <-- 0.0289 --> 0.0491

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 115.777 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.037 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 102.161 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 108.186 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.246 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.042 deg; O3  -- O4  = 3 A
       102.161 deg <-- 109.408 deg --> 115.777 deg

O3  -- T2  -- O5  = 111.409 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.894 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 101.960 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 106.722 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 117.735 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.984 deg; O6  -- O7  = 3 A
       101.960 deg <-- 109.451 deg --> 117.735 deg

O4  -- T3  -- O8  = 108.142 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 110.756 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 100.204 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.799 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.263 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 117.998 deg; O9  -- O10 = 3 A
       100.204 deg <-- 109.360 deg --> 117.998 deg

O7  -- T4  -- O12 = 109.155 deg; O7  -- O12 = 3 A
O7  -- T4  -- O11 = 108.085 deg; O7  -- O11 = 3 A
O7  -- T4  -- O13 = 114.911 deg; O7  -- O13 = 3 A
O12 -- T4  -- O11 = 109.980 deg; O12 -- O11 = 3 A
O12 -- T4  -- O13 = 106.481 deg; O12 -- O13 = 3 A
O11 -- T4  -- O13 = 108.177 deg; O11 -- O13 = 3 A
       106.481 deg <-- 109.465 deg --> 114.911 deg

O9  -- T5  -- O10 =  91.560 deg; O9  -- O10 = 2 A
O9  -- T5  -- O13 = 105.287 deg; O9  -- O13 = 3 A
O9  -- T5  -- O14 = 126.163 deg; O9  -- O14 = 3 A
O10 -- T5  -- O13 = 115.806 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 110.692 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 107.220 deg; O13 -- O14 = 3 A
       91.560 deg <-- 109.454 deg --> 126.163 deg

        O-T-O SUMMARY
          Range  = 91.5598 deg <--> 126.1631 deg
          Mean   = 109.3542 deg
          StdDev = 6.1902 deg

        O--O SUMMARY
          Range  = 2.3588 A <--> 3.0246 A
          Mean   = 2.6676 A
          StdDev = 0.1306 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.468 deg ; T1  -- T1   2.7420 A

T1  -- O2  -- T1  = 121.271 deg ; T1  -- T1   2.8636 A

T1  -- O3  -- T2  = 154.194 deg ; T1  -- T2   3.1010 A

T1  -- O4  -- T3  = 113.200 deg ; T1  -- T3   2.6718 A

T2  -- O5  -- T2  = 155.324 deg ; T2  -- T2   3.2043 A

T2  -- O6  -- T2  = 124.827 deg ; T2  -- T2   2.8583 A

T2  -- O7  -- T4  = 117.236 deg ; T2  -- T4   2.8182 A

T3  -- O8  -- T3  = 140.388 deg ; T3  -- T3   3.0632 A

T3  -- O9  -- T5  = 142.363 deg ; T3  -- T5   3.2709 A

T3  -- O10 -- T5  = 126.274 deg ; T3  -- T5   2.9137 A

T4  -- O11 -- T4  = 114.551 deg ; T4  -- T4   2.7176 A

T4  -- O12 -- T4  = 134.728 deg ; T4  -- T4   2.9646 A

T4  -- O13 -- T5  = 172.603 deg ; T4  -- T5   3.2216 A

T5  -- O14 -- T5  = 127.366 deg ; T5  -- T5   3.0696 A


        T-O-T SUMMARY
          Range  = 113.1996° <--> 172.6030 deg
          Mean   = 132.7709 deg
          StdDev = 17.4738 deg

        T--T SUMMARY
          Range  = 2.6718 A <--> 3.2709 A
          Mean   = 2.9629 A
          StdDev = 0.1889 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.
T1  -- T3  = 2.6718 Angstrom
T1  -- T1  = 2.7420 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.6718 Angstrom
  T3  -- T3  = 3.1744 Angstrom
  T3  -- T3  = 3.0632 Angstrom
  T3  -- T5  = 3.2709 Angstrom
  T3  -- T5  = 2.9137 Angstrom
T4  -- T4  = 2.7176 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 24 43 69 97 130 174 230 295 359 424 499 582 669 769
TD10 = 1078
Circuit symbol = 4.6_{2}.6.6.6.7_{2}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6.6.7_{2}
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 40 61 90 129 173 222 281 348 418 501 591 680 767
TD10 = 1033
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 21
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 21

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 40 67 97 134 185 238 288 355 436 509 581 675 782
TD10 = 1087
Circuit symbol = 4.6.6.6_{3}.6.6_{3}
Weight = 20
Vertex symbol  = 4.6.6.6_{3}.6.6_{3}
Weight = 20

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 34 57 87 125 169 218 272 337 413 493 576 665 761
TD10 = 996
Circuit symbol = 4.4.6.6.6.6_{2}
Weight = 20
Vertex symbol  = 4.4.6.6.6.6_{2}
Weight = 20

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 37 61 97 136 174 224 284 343 410 494 585 672 757
TD10 = 1049
Circuit symbol = 4.4.6.6_{2}.6.8_{3}
Weight = 17
Vertex symbol  = 4.4.6.6_{2}.6.10
Weight = 23

<TD10> = 1048.600
Average ring size = 5.5676