Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_46487181_PJNk95.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 22.40 T-atoms per nm^3
Material density = 2.235 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5602 Angstrom
T1  -- O2  = 1.6449 Angstrom
T1  -- O3  = 1.6155 Angstrom
T1  -- O4  = 1.6419 Angstrom
      mean = 1.6156 Angstrom
        t1 = 0.041011  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028816  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5514 Angstrom
T2  -- O5  = 1.6085 Angstrom
T2  -- O6  = 1.6180 Angstrom
T2  -- O7  = 1.4876 Angstrom
      mean = 1.5664 Angstrom
        t1 = 0.060938  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037325  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.5172 Angstrom
T3  -- O8  = 1.5499 Angstrom
T3  -- O9  = 1.5848 Angstrom
T3  -- O10 = 1.7102 Angstrom
      mean = 1.5905 Angstrom
        t1 = 0.081400  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050566  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6710 Angstrom
T4  -- O11 = 1.7136 Angstrom
T4  -- O12 = 1.6780 Angstrom
T4  -- O13 = 1.6515 Angstrom
      mean = 1.6785 Angstrom
        t1 = 0.104063  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.077209  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6772 Angstrom
T5  -- O14 = 1.6229 Angstrom
T5  -- O15 = 1.7352 Angstrom
T5  -- O13 = 1.6357 Angstrom
      mean = 1.6677 Angstrom
        t1 = 0.077386  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.075829  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4876 A <--> 1.7352 A
          Mean   = 1.6238 A
          StdDev = 0.0649 A

       t1 Range  = 0.0410 <-- 0.0730 --> 0.1041
       t2 Range  = 0.0288 <-- 0.0539 --> 0.0772

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.451 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.760 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 101.830 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 109.398 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 119.331 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.442 deg; O3  -- O4  = 3 A
       101.830 deg <-- 109.368 deg --> 119.331 deg

O4  -- T2  -- O5  = 115.283 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.596 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  =  95.610 deg; O4  -- O7  = 2 A
O5  -- T2  -- O6  = 110.589 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.959 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 114.156 deg; O6  -- O7  = 3 A
       95.610 deg <-- 109.365 deg --> 115.283 deg

O7  -- T3  -- O8  = 133.473 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 113.549 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 100.248 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 108.517 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 =  83.580 deg; O8  -- O10 = 2 A
O9  -- T3  -- O10 = 109.104 deg; O9  -- O10 = 3 A
       83.580 deg <-- 108.078 deg --> 133.473 deg

O10 -- T4  -- O11 = 136.248 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 =  97.302 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 =  96.752 deg; O10 -- O13 = 2 A
O11 -- T4  -- O12 = 101.006 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 101.004 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 130.082 deg; O12 -- O13 = 3 A
       96.752 deg <-- 110.399 deg --> 136.248 deg

O12 -- T5  -- O14 = 107.448 deg; O12 -- O14 = 3 A
O12 -- T5  -- O15 = 121.678 deg; O12 -- O15 = 3 A
O12 -- T5  -- O13 =  93.253 deg; O12 -- O13 = 2 A
O14 -- T5  -- O15 = 107.723 deg; O14 -- O15 = 3 A
O14 -- T5  -- O13 = 107.287 deg; O14 -- O13 = 3 A
O15 -- T5  -- O13 = 118.061 deg; O15 -- O13 = 3 A
       93.253 deg <-- 109.241 deg --> 121.678 deg

        O-T-O SUMMARY
          Range  = 83.5795 deg <--> 136.2476 deg
          Mean   = 109.3518 deg
          StdDev = 11.9434 deg

        O--O SUMMARY
          Range  = 2.1758 A <--> 3.1409 A
          Mean   = 2.6375 A
          StdDev = 0.2095 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  86.459 deg; T1  -- T2  = 3.7672 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.0389 A
T1  - O1  - T1  - O4  - T1  =  91.204 deg; T1  -- T1  = 4.1708 A
T2  - O2  - T1  - O3  - T1  = 119.152 deg; T2  -- T1  = 4.8504 A
T2  - O2  - T1  - O4  - T1  = 148.778 deg; T2  -- T1  = 5.4324 A
T1  - O3  - T1  - O4  - T1  =  88.796 deg; T1  -- T1  = 4.1708 A

T1  - O4  - T2  - O5  - T2  = 150.147 deg; T1  -- T2  = 5.6709 A
T1  - O4  - T2  - O6  - T2  =  93.541 deg; T1  -- T2  = 3.7672 A
T1  - O4  - T2  - O7  - T3  = 100.320 deg; T1  -- T3  = 4.0783 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.0857 A
T2  - O5  - T2  - O7  - T3  =  82.686 deg; T2  -- T3  = 3.9053 A
T2  - O6  - T2  - O7  - T3  = 163.235 deg; T2  -- T3  = 5.1249 A

T2  - O7  - T3  - O8  - T3  =  89.339 deg; T2  -- T3  = 3.9053 A
T2  - O7  - T3  - O9  - T3  = 119.256 deg; T2  -- T3  = 4.8455 A
T2  - O7  - T3  - O10 - T4  = 100.435 deg; T2  -- T4  = 4.5363 A
T3  - O8  - T3  - O9  - T3  = 150.000 deg; T3  -- T3  = 5.6422 A
T3  - O8  - T3  - O10 - T4  =  82.373 deg; T3  -- T4  = 4.0327 A
T3  - O9  - T3  - O10 - T4  =  99.668 deg; T3  -- T4  = 4.7223 A

T3  - O10 - T4  - O11 - T5  = 105.801 deg; T3  -- T5  = 5.0007 A
T3  - O10 - T4  - O12 - T4  = 166.705 deg; T3  -- T4  = 5.8709 A
T3  - O10 - T4  - O13 - T5  = 121.704 deg; T3  -- T5  = 5.4443 A
T5  - O11 - T4  - O12 - T4  =  62.972 deg; T5  -- T4  = 3.0095 A
T5  - O11 - T4  - O13 - T5  = 121.681 deg; T5  -- T5  = 5.2874 A
T4  - O12 - T4  - O13 - T5  =  64.335 deg; T4  -- T5  = 3.0452 A

T4  - O12 - T5  - O14 - T5  = 101.532 deg; T4  -- T5  = 4.5432 A
T4  - O12 - T5  - O15 - T5  = 134.246 deg; T4  -- T5  = 5.8531 A
T4  - O12 - T5  - O13 - T4  =  52.694 deg; T4  -- T4  = 2.6873 A
T5  - O14 - T5  - O15 - T5  = 120.000 deg; T5  -- T5  = 5.3091 A
T5  - O14 - T5  - O13 - T4  = 101.671 deg; T5  -- T4  = 4.5193 A
T5  - O15 - T5  - O13 - T4  = 127.044 deg; T5  -- T4  = 5.6552 A

        T-T-T SUMMARY
          Range  = 52.6937 deg <--> 166.7052 deg
          Mean   = 107.8876 deg
          StdDev = 29.0376 deg

        T--T SUMMARY
          Range  = 2.6873 A <--> 5.8709 A
          Mean   = 4.5787 A
          StdDev = 0.8711 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 146.691 deg ; T1  -- T1   2.9896 A

T1  -- O2  -- T1  = 129.190 deg ; T1  -- T1   2.9718 A

T1  -- O3  -- T1  = 123.484 deg ; T1  -- T1   2.8462 A

T1  -- O4  -- T2  = 112.141 deg ; T1  -- T2   2.6501 A

T2  -- O5  -- T2  = 179.109 deg ; T2  -- T2   3.2169 A

T2  -- O6  -- T2  = 102.222 deg ; T2  -- T2   2.5189 A

T2  -- O7  -- T3  = 124.671 deg ; T2  -- T3   2.6613 A

T3  -- O8  -- T3  = 137.480 deg ; T3  -- T3   2.8889 A

T3  -- O9  -- T3  = 137.322 deg ; T3  -- T3   2.9523 A

T3  -- O10 -- T4  = 144.809 deg ; T3  -- T4   3.2231 A

T4  -- O11 -- T4  = 103.279 deg ; T4  -- T4   2.6873 A

T4  -- O12 -- T5  = 130.353 deg ; T4  -- T5   3.0452 A

T4  -- O13 -- T5  = 132.567 deg ; T4  -- T5   3.0095 A

T5  -- O14 -- T5  = 120.445 deg ; T5  -- T5   2.8173 A

T5  -- O15 -- T5  = 144.664 deg ; T5  -- T5   3.3067 A


        T-O-T SUMMARY
          Range  = 102.2221° <--> 179.1092 deg
          Mean   = 131.2286 deg
          StdDev = 18.6105 deg

        T--T SUMMARY
          Range  = 2.5189 A <--> 3.3067 A
          Mean   = 2.9190 A
          StdDev = 0.2213 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O7  = 2.2519 A
O8  -- O10 = 2.1760 A
O8  -- O10 = 2.1758 A
T1  -- T2  = 2.6501 Angstrom
T2  -- T1  = 2.6501 Angstrom
T2  -- T2  = 2.5189 Angstrom
T2  -- T3  = 2.6613 Angstrom
T3  -- T2  = 2.6613 Angstrom
T4  -- T4  = 2.6873 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 28 50 79 110 143 180 226 281 341 402 466 541 625
TD10 = 846
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.10_{4}
Weight = 22

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 19 35 53 76 108 148 190 230 281 339 400 475 544 605
TD10 = 873
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.10_{2}
Weight = 23

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 38 59 82 114 154 196 238 286 349 409 469 542 624
TD10 = 919
Circuit symbol = 4.6_{2}.6.8.8.8_{2}
Weight = 27
Vertex symbol  = 4.6_{2}.6.8.8.8
Weight = 27

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 20 37 56 79 114 153 186 230 295 347 391 470 557 609
TD10 = 888
Circuit symbol = 3.6.3.6.4.7_{2}
Weight = 9
Vertex symbol  = 3.6.3.6.6_{2}.10_{4}
Weight = 19

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 29 54 84 113 143 183 230 282 340 401 462 531 614
TD10 = 866
Circuit symbol = 3.6.6_{3}.8.6_{3}.8
Weight = 24
Vertex symbol  = 3.6.6_{3}.8.6_{3}.8
Weight = 24

<TD10> = 878.400
Average ring size = 5.8636