Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_44624825_GaI38T.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 23.03 T-atoms per nm^3
Material density = 2.297 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7315 Angstrom
T1  -- O2  = 1.6201 Angstrom
T1  -- O3  = 1.6018 Angstrom
T1  -- O4  = 1.6887 Angstrom
      mean = 1.6605 Angstrom
        t1 = 0.085863  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.055193  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6456 Angstrom
T2  -- O6  = 1.6248 Angstrom
T2  -- O7  = 1.5923 Angstrom
T2  -- O3  = 1.5657 Angstrom
      mean = 1.6071 Angstrom
        t1 = 0.046475  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043400  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6953 Angstrom
T3  -- O8  = 1.5496 Angstrom
T3  -- O9  = 1.6468 Angstrom
T3  -- O10 = 1.5646 Angstrom
      mean = 1.6141 Angstrom
        t1 = 0.117348  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.089096  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6282 Angstrom
T4  -- O11 = 1.7106 Angstrom
T4  -- O12 = 1.6534 Angstrom
T4  -- O13 = 1.5889 Angstrom
      mean = 1.6453 Angstrom
        t1 = 0.069547  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.041800  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6152 Angstrom
T5  -- O13 = 1.6095 Angstrom
T5  -- O14 = 1.6277 Angstrom
T5  -- O15 = 1.6298 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.124445  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.108676  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5496 A <--> 1.7315 A
          Mean   = 1.6295 A
          StdDev = 0.0475 A

       t1 Range  = 0.0465 <-- 0.0887 --> 0.1244
       t2 Range  = 0.0418 <-- 0.0676 --> 0.1087

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.237 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.453 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 125.040 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 102.133 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 115.301 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  91.758 deg; O3  -- O4  = 2 A
       91.758 deg <-- 108.987 deg --> 125.040 deg

O5  -- T2  -- O6  = 111.677 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 116.361 deg; O5  -- O7  = 3 A
O5  -- T2  -- O3  = 107.925 deg; O5  -- O3  = 3 A
O6  -- T2  -- O7  = 111.716 deg; O6  -- O7  = 3 A
O6  -- T2  -- O3  = 110.834 deg; O6  -- O3  = 3 A
O7  -- T2  -- O3  =  97.322 deg; O7  -- O3  = 2 A
       97.322 deg <-- 109.306 deg --> 116.361 deg

O4  -- T3  -- O8  =  83.633 deg; O4  -- O8  = 2 A
O4  -- T3  -- O9  = 110.137 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  79.307 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 114.385 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 126.394 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 119.214 deg; O9  -- O10 = 3 A
       79.307 deg <-- 105.512 deg --> 126.394 deg

O7  -- T4  -- O11 = 119.322 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.703 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  93.038 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 113.029 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 112.938 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 106.579 deg; O12 -- O13 = 3 A
       93.038 deg <-- 109.102 deg --> 119.322 deg

O10 -- T5  -- O13 =  74.296 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 = 123.145 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 119.003 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 =  94.165 deg; O13 -- O14 = 2 A
O13 -- T5  -- O15 = 103.457 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 117.835 deg; O14 -- O15 = 3 A
       74.296 deg <-- 105.317 deg --> 123.145 deg

        O-T-O SUMMARY
          Range  = 74.2960 deg <--> 126.3941 deg
          Mean   = 107.1911 deg
          StdDev = 13.3751 deg

        O--O SUMMARY
          Range  = 1.9473 A <--> 3.0343 A
          Mean   = 2.6047 A
          StdDev = 0.2530 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 161.319 deg ; T1  -- T1   3.4170 A

T1  -- O2  -- T1  = 130.812 deg ; T1  -- T1   2.9463 A

T1  -- O3  -- T2  = 122.877 deg ; T1  -- T2   2.7821 A

T1  -- O4  -- T3  = 142.949 deg ; T1  -- T3   3.2086 A

T2  -- O5  -- T2  = 118.305 deg ; T2  -- T2   2.8257 A

T2  -- O6  -- T2  = 141.524 deg ; T2  -- T2   3.0681 A

T2  -- O7  -- T4  = 154.849 deg ; T2  -- T4   3.1433 A

T3  -- O8  -- T3  = 179.243 deg ; T3  -- T3   3.0992 A

T3  -- O9  -- T3  = 129.839 deg ; T3  -- T3   2.9829 A

T3  -- O10 -- T5  = 111.935 deg ; T3  -- T5   2.6353 A

T4  -- O11 -- T4  = 172.514 deg ; T4  -- T4   3.4138 A

T4  -- O12 -- T4  = 132.211 deg ; T4  -- T4   3.0235 A

T4  -- O13 -- T5  = 155.391 deg ; T4  -- T5   3.1250 A

T5  -- O14 -- T5  = 176.597 deg ; T5  -- T5   3.2539 A

T5  -- O15 -- T5  = 118.452 deg ; T5  -- T5   2.8007 A


        T-O-T SUMMARY
          Range  = 111.9346° <--> 179.2434 deg
          Mean   = 143.2544 deg
          StdDev = 21.5679 deg

        T--T SUMMARY
          Range  = 2.6353 A <--> 3.4170 A
          Mean   = 3.0484 A
          StdDev = 0.2198 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O8  = 2.1662 A
O4  -- O10 = 2.0827 A
O10 -- O13 = 1.9473 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.9463 Angstrom
  T1  -- T3  = 3.2086 Angstrom
  T1  -- T5  = 2.9061 Angstrom
  T1  -- T1  = 3.4170 Angstrom
  T1  -- T2  = 2.7821 Angstrom
  T1  -- T4  = 3.4200 Angstrom
T2  -- T1  = 2.7821 Angstrom
T3  -- T5  = 2.6353 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.1433 Angstrom
  T4  -- T4  = 3.0235 Angstrom
  T4  -- T5  = 3.1250 Angstrom
  T4  -- T1  = 3.4200 Angstrom
  T4  -- T4  = 3.4138 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 2.9061 Angstrom
  T5  -- T3  = 2.6353 Angstrom
  T5  -- T4  = 3.1250 Angstrom
  T5  -- T5  = 3.2539 Angstrom
  T5  -- T5  = 2.8007 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

<TD10> = 975.600
Average ring size = 5.7307