Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_43932212_5lZfKg.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.34 T-atoms per nm^3
Material density = 2.429 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5863 Angstrom
T1  -- O2  = 1.6595 Angstrom
T1  -- O4  = 1.6463 Angstrom
T1  -- O3  = 1.6620 Angstrom
      mean = 1.6385 Angstrom
        t1 = 0.042702  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031367  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6585 Angstrom
T2  -- O5  = 1.6938 Angstrom
T2  -- O6  = 1.7136 Angstrom
T2  -- O7  = 1.6406 Angstrom
      mean = 1.6766 Angstrom
        t1 = 0.090552  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.065357  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6461 Angstrom
T3  -- O7  = 1.6427 Angstrom
T3  -- O8  = 1.5603 Angstrom
T3  -- O9  = 1.6325 Angstrom
      mean = 1.6204 Angstrom
        t1 = 0.054602  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043851  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.5722 Angstrom
T4  -- O10 = 1.5733 Angstrom
T4  -- O11 = 1.6483 Angstrom
T4  -- O12 = 1.5393 Angstrom
      mean = 1.5833 Angstrom
        t1 = 0.044172  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052995  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5724 Angstrom
T5  -- O13 = 1.5810 Angstrom
T5  -- O14 = 1.6219 Angstrom
T5  -- O15 = 1.6160 Angstrom
      mean = 1.5978 Angstrom
        t1 = 0.024274  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021755  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5393 A <--> 1.7136 A
          Mean   = 1.6233 A
          StdDev = 0.0456 A

       t1 Range  = 0.0243 <-- 0.0513 --> 0.0906
       t2 Range  = 0.0218 <-- 0.0431 --> 0.0654

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.123 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 106.435 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 102.762 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 110.387 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 116.545 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 113.504 deg; O4  -- O3  = 3 A
       102.762 deg <-- 109.292 deg --> 116.545 deg

O3  -- T2  -- O5  = 114.673 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 115.403 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  96.724 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 126.080 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  91.325 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 101.449 deg; O6  -- O7  = 3 A
       91.325 deg <-- 107.609 deg --> 126.080 deg

O4  -- T3  -- O7  = 116.544 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 103.693 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.727 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 106.984 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 118.530 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  =  98.559 deg; O8  -- O9  = 2 A
       98.559 deg <-- 109.006 deg --> 118.530 deg

O9  -- T4  -- O10 = 102.594 deg; O9  -- O10 = 2 A
O9  -- T4  -- O11 = 118.758 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 104.571 deg; O9  -- O12 = 2 A
O10 -- T4  -- O11 = 108.328 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 112.828 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.708 deg; O11 -- O12 = 3 A
       102.594 deg <-- 109.465 deg --> 118.758 deg

O12 -- T5  -- O13 = 104.118 deg; O12 -- O13 = 2 A
O12 -- T5  -- O14 = 113.703 deg; O12 -- O14 = 3 A
O12 -- T5  -- O15 = 109.529 deg; O12 -- O15 = 3 A
O13 -- T5  -- O14 = 109.643 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.205 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 110.406 deg; O14 -- O15 = 3 A
       104.118 deg <-- 109.434 deg --> 113.703 deg

        O-T-O SUMMARY
          Range  = 91.3255 deg <--> 126.0804 deg
          Mean   = 108.6647 deg
          StdDev = 7.1349 deg

        O--O SUMMARY
          Range  = 2.3852 A <--> 3.0371 A
          Mean   = 2.6327 A
          StdDev = 0.1440 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 164.819 deg; T1  -- T2  = 5.8677 A
T1  - O1  - T1  - O4  - T3  =  89.944 deg; T1  -- T3  = 4.1936 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2961 A
T2  - O2  - T1  - O4  - T3  = 104.827 deg; T2  -- T3  = 4.7715 A
T2  - O2  - T1  - O3  - T1  =  87.995 deg; T2  -- T1  = 4.2800 A
T3  - O4  - T1  - O3  - T1  =  84.485 deg; T3  -- T1  = 4.1510 A

T2  - O3  - T2  - O5  - T2  = 150.000 deg; T2  -- T2  = 6.3191 A
T2  - O3  - T2  - O6  - T1  =  84.807 deg; T2  -- T1  = 4.2800 A
T2  - O3  - T2  - O7  - T3  =  89.260 deg; T2  -- T3  = 4.6443 A
T2  - O5  - T2  - O6  - T1  = 124.121 deg; T2  -- T1  = 5.4901 A
T2  - O5  - T2  - O7  - T3  =  87.379 deg; T2  -- T3  = 4.4815 A
T1  - O6  - T2  - O7  - T3  =  82.217 deg; T1  -- T3  = 4.1356 A

T1  - O4  - T3  - O7  - T2  = 140.474 deg; T1  -- T2  = 5.9251 A
T1  - O4  - T3  - O8  - T3  =  90.056 deg; T1  -- T3  = 4.1936 A
T1  - O4  - T3  - O9  - T4  = 116.347 deg; T1  -- T4  = 5.0761 A
T2  - O7  - T3  - O8  - T3  =  92.621 deg; T2  -- T3  = 4.4815 A
T2  - O7  - T3  - O9  - T4  =  93.316 deg; T2  -- T4  = 4.5399 A
T3  - O8  - T3  - O9  - T4  = 126.190 deg; T3  -- T4  = 5.2316 A

T3  - O9  - T4  - O10 - T4  =  96.190 deg; T3  -- T4  = 4.5427 A
T3  - O9  - T4  - O11 - T4  = 173.810 deg; T3  -- T4  = 5.6044 A
T3  - O9  - T4  - O12 - T5  =  84.819 deg; T3  -- T5  = 3.8367 A
T4  - O10 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.1158 A
T4  - O10 - T4  - O12 - T5  = 141.896 deg; T4  -- T5  = 5.5508 A
T4  - O11 - T4  - O12 - T5  =  90.312 deg; T4  -- T5  = 3.8162 A

T4  - O12 - T5  - O13 - T5  = 133.174 deg; T4  -- T5  = 4.9527 A
T4  - O12 - T5  - O14 - T5  =  89.688 deg; T4  -- T5  = 3.8162 A
T4  - O12 - T5  - O15 - T5  = 128.023 deg; T4  -- T5  = 5.2844 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 4.6385 A
T5  - O13 - T5  - O15 - T5  =  90.131 deg; T5  -- T5  = 4.1338 A
T5  - O14 - T5  - O15 - T5  =  89.869 deg; T5  -- T5  = 4.1338 A

        T-T-T SUMMARY
          Range  = 82.2170 deg <--> 173.8105 deg
          Mean   = 106.9370 deg
          StdDev = 25.6147 deg

        T--T SUMMARY
          Range  = 3.8162 A <--> 6.3191 A
          Mean   = 4.6887 A
          StdDev = 0.6694 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 168.064 deg ; T1  -- T1   3.1555 A

T1  -- O2  -- T1  = 122.897 deg ; T1  -- T1   2.9154 A

T1  -- O3  -- T2  = 129.573 deg ; T1  -- T2   3.0041 A

T1  -- O4  -- T3  = 132.811 deg ; T1  -- T3   3.0172 A

T2  -- O5  -- T2  = 159.324 deg ; T2  -- T2   3.3326 A

T2  -- O6  -- T2  = 138.897 deg ; T2  -- T2   3.2093 A

T2  -- O7  -- T3  = 173.538 deg ; T2  -- T3   3.2781 A

T3  -- O8  -- T3  = 137.614 deg ; T3  -- T3   2.9095 A

T3  -- O9  -- T4  = 134.642 deg ; T3  -- T4   2.9570 A

T4  -- O10 -- T4  = 175.644 deg ; T4  -- T4   3.1445 A

T4  -- O11 -- T4  = 107.333 deg ; T4  -- T4   2.6555 A

T4  -- O12 -- T5  = 122.354 deg ; T4  -- T5   2.7262 A

T5  -- O13 -- T5  = 169.644 deg ; T5  -- T5   3.1490 A

T5  -- O14 -- T5  = 110.847 deg ; T5  -- T5   2.6708 A

T5  -- O15 -- T5  = 112.362 deg ; T5  -- T5   2.6852 A


        T-O-T SUMMARY
          Range  = 107.3330° <--> 175.6445 deg
          Mean   = 139.7030 deg
          StdDev = 22.9917 deg

        T--T SUMMARY
          Range  = 2.6555 A <--> 3.3326 A
          Mean   = 2.9873 A
          StdDev = 0.2186 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T4  -- T4  = 2.6555 Angstrom
T4  -- T5  = 2.7262 Angstrom
T5  -- T4  = 2.7262 Angstrom
T5  -- T5  = 2.6708 Angstrom
T5  -- T5  = 2.6852 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 35 60 86 112 147 196 256 315 367 421 487 571 667
TD10 = 924
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 13
Vertex symbol  = 4.4.4.6_{2}.10_{4}.12
Weight = 35

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 88 126 166 207 253 305 368 444 519 589 662
TD10 = 969
Circuit symbol = 4.4.6_{2}.8.8_{3}.8_{4}
Weight = 24
Vertex symbol  = 4.4.6_{2}.8.8_{2}.10_{3}
Weight = 29

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 36 57 79 107 147 197 251 305 359 420 495 578 664
TD10 = 909
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.6.6
Weight = 14

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 32 46 68 102 140 176 218 271 333 400 471 546 620
TD10 = 817
Circuit symbol = 4.6.4.6_{2}.6.8_{4}
Weight = 19
Vertex symbol  = 4.6.4.6_{2}.8.10
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 30 49 72 98 132 175 219 262 313 381 462 545 627
TD10 = 806
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 18

<TD10> = 885.000
Average ring size = 5.8427