Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_42774298_xz3L3o.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 23.50 T-atoms per nm^3
Material density = 2.344 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5714 Angstrom
T1  -- O2  = 1.6323 Angstrom
T1  -- O3  = 1.5593 Angstrom
T1  -- O4  = 1.6920 Angstrom
      mean = 1.6137 Angstrom
        t1 = 0.109841  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090019  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6383 Angstrom
T2  -- O6  = 1.6274 Angstrom
T2  -- O3  = 1.5959 Angstrom
T2  -- O7  = 1.6127 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.121991  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.102687  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6926 Angstrom
T3  -- O8  = 1.7421 Angstrom
T3  -- O9  = 1.6169 Angstrom
T3  -- O10 = 1.6156 Angstrom
      mean = 1.6668 Angstrom
        t1 = 0.082050  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048070  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.5791 Angstrom
T4  -- O11 = 1.7169 Angstrom
T4  -- O12 = 1.6661 Angstrom
T4  -- O13 = 1.6338 Angstrom
      mean = 1.6490 Angstrom
        t1 = 0.082012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053408  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5737 Angstrom
T5  -- O13 = 1.5791 Angstrom
T5  -- O14 = 1.6186 Angstrom
T5  -- O15 = 1.6353 Angstrom
      mean = 1.6017 Angstrom
        t1 = 0.047987  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031131  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5593 A <--> 1.7421 A
          Mean   = 1.6300 A
          StdDev = 0.0491 A

       t1 Range  = 0.0480 <-- 0.0888 --> 0.1220
       t2 Range  = 0.0311 <-- 0.0651 --> 0.1027

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 115.877 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 125.303 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  86.058 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 118.652 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.681 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  80.001 deg; O3  -- O4  = 2 A
       80.001 deg <-- 105.929 deg --> 125.303 deg

O5  -- T2  -- O6  = 118.696 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 122.303 deg; O5  -- O3  = 3 A
O5  -- T2  -- O7  =  97.593 deg; O5  -- O7  = 2 A
O6  -- T2  -- O3  = 118.610 deg; O6  -- O3  = 3 A
O6  -- T2  -- O7  = 104.680 deg; O6  -- O7  = 3 A
O3  -- T2  -- O7  =  74.067 deg; O3  -- O7  = 2 A
       74.067 deg <-- 105.991 deg --> 122.303 deg

O4  -- T3  -- O8  = 124.932 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 112.736 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  94.902 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 105.155 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 114.623 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 102.341 deg; O9  -- O10 = 3 A
       94.902 deg <-- 109.115 deg --> 124.932 deg

O7  -- T4  -- O11 = 112.338 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 106.089 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  89.261 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 115.570 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 118.664 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 111.261 deg; O12 -- O13 = 3 A
       89.261 deg <-- 108.864 deg --> 118.664 deg

O10 -- T5  -- O13 =  96.130 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 = 111.619 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 107.997 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 112.732 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 115.941 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 111.367 deg; O14 -- O15 = 3 A
       96.130 deg <-- 109.298 deg --> 115.941 deg

        O-T-O SUMMARY
          Range  = 74.0674 deg <--> 125.3033 deg
          Mean   = 107.3399 deg
          StdDev = 13.0486 deg

        O--O SUMMARY
          Range  = 1.9326 A <--> 3.0458 A
          Mean   = 2.6086 A
          StdDev = 0.2495 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.106 deg ; T1  -- T1   3.1428 A

T1  -- O2  -- T1  = 127.329 deg ; T1  -- T1   2.9258 A

T1  -- O3  -- T2  = 113.636 deg ; T1  -- T2   2.6407 A

T1  -- O4  -- T3  = 143.885 deg ; T1  -- T3   3.2179 A

T2  -- O5  -- T2  = 177.611 deg ; T2  -- T2   3.2759 A

T2  -- O6  -- T2  = 117.882 deg ; T2  -- T2   2.7883 A

T2  -- O7  -- T4  = 149.757 deg ; T2  -- T4   3.0813 A

T3  -- O8  -- T3  = 164.214 deg ; T3  -- T3   3.4510 A

T3  -- O9  -- T3  = 131.060 deg ; T3  -- T3   2.9433 A

T3  -- O10 -- T5  = 122.996 deg ; T3  -- T5   2.8028 A

T4  -- O11 -- T4  = 170.249 deg ; T4  -- T4   3.4214 A

T4  -- O12 -- T4  = 131.748 deg ; T4  -- T4   3.0412 A

T4  -- O13 -- T5  = 143.960 deg ; T4  -- T5   3.0554 A

T5  -- O14 -- T5  = 143.604 deg ; T5  -- T5   3.0752 A

T5  -- O15 -- T5  = 123.355 deg ; T5  -- T5   2.8791 A


        T-O-T SUMMARY
          Range  = 113.6357° <--> 179.1061 deg
          Mean   = 142.6929 deg
          StdDev = 20.8911 deg

        T--T SUMMARY
          Range  = 2.6407 A <--> 3.4510 A
          Mean   = 3.0495 A
          StdDev = 0.2225 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2286 A
O1  -- O4  = 2.2286 A
O3  -- O7  = 1.9326 A
O3  -- O4  = 2.0923 A
O7  -- O13 = 2.2575 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.6407 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.6407 Angstrom
  T2  -- T2  = 3.2759 Angstrom
  T2  -- T2  = 2.7883 Angstrom
  T2  -- T3  = 3.0181 Angstrom
  T2  -- T4  = 3.0813 Angstrom
T3  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.2179 Angstrom
  T3  -- T2  = 3.0181 Angstrom
  T3  -- T3  = 3.4510 Angstrom
  T3  -- T3  = 2.9433 Angstrom
  T3  -- T4  = 3.2692 Angstrom
  T3  -- T5  = 2.8028 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.0813 Angstrom
  T4  -- T3  = 3.2692 Angstrom
  T4  -- T4  = 3.4214 Angstrom
  T4  -- T4  = 3.0412 Angstrom
  T4  -- T5  = 3.0554 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

<TD10> = 975.600
Average ring size = 5.7307