Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_42698732_gkl577.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 22.31 T-atoms per nm^3
Material density = 2.226 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5360 Angstrom
T1  -- O7  = 2.0361 Angstrom
T1  -- O2  = 1.6255 Angstrom
T1  -- O3  = 1.6277 Angstrom
T1  -- O4  = 1.7018 Angstrom
      mean = 1.7054 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5623 Angstrom
T2  -- O5  = 1.6357 Angstrom
T2  -- O6  = 1.6495 Angstrom
T2  -- O7  = 1.6510 Angstrom
      mean = 1.6246 Angstrom
        t1 = 0.081351  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053075  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.7069 Angstrom
T3  -- O7  = 1.6897 Angstrom
T3  -- O8  = 1.6564 Angstrom
T3  -- O9  = 1.6372 Angstrom
      mean = 1.6726 Angstrom
        t1 = 0.073734  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040135  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6598 Angstrom
T4  -- O10 = 1.5659 Angstrom
T4  -- O11 = 1.6746 Angstrom
T4  -- O12 = 1.6239 Angstrom
      mean = 1.6311 Angstrom
        t1 = 0.054778  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.069771  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5897 Angstrom
T5  -- O13 = 1.6163 Angstrom
T5  -- O14 = 1.5947 Angstrom
T5  -- O15 = 1.6126 Angstrom
      mean = 1.6033 Angstrom
        t1 = 0.015683  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019658  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5360 A <--> 2.0361 A
          Mean   = 1.6502 A
          StdDev = 0.0968 A

       t1 Range  = 0.0157 <-- 0.0451 --> 0.0814
       t2 Range  = 0.0197 <-- 0.0365 --> 0.0698

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O7  =  96.868 deg; O1  -- O7  = 3 A
O1  -- T1  -- O2  = 118.373 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.652 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  63.327 deg; O1  -- O4  = 2 A
O7  -- T1  -- O2  = 135.170 deg; O7  -- O2  = 3 A
O7  -- T1  -- O3  =  73.558 deg; O7  -- O3  = 2 A
O7  -- T1  -- O4  = 126.309 deg; O7  -- O4  = 3 A
O2  -- T1  -- O3  = 107.087 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  95.463 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  75.425 deg; O3  -- O4  = 2 A
       63.327 deg <-- 101.123 deg --> 135.170 deg

O3  -- T2  -- O5  = 121.933 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 112.477 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  87.250 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 118.671 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  97.368 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 111.912 deg; O6  -- O7  = 3 A
       87.250 deg <-- 108.268 deg --> 121.933 deg

O4  -- T3  -- O7  = 113.099 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 106.205 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 119.793 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 120.796 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  =  98.875 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  =  97.895 deg; O8  -- O9  = 2 A
       97.895 deg <-- 109.444 deg --> 120.796 deg

O9  -- T4  -- O10 = 101.415 deg; O9  -- O10 = 2 A
O9  -- T4  -- O11 = 121.675 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 111.723 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 105.192 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 104.702 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 110.130 deg; O11 -- O12 = 3 A
       101.415 deg <-- 109.139 deg --> 121.675 deg

O12 -- T5  -- O13 = 113.557 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 106.207 deg; O12 -- O14 = 3 A
O12 -- T5  -- O15 = 109.328 deg; O12 -- O15 = 3 A
O13 -- T5  -- O14 = 108.867 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 108.971 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 109.850 deg; O14 -- O15 = 3 A
       106.207 deg <-- 109.463 deg --> 113.557 deg

        O-T-O SUMMARY
          Range  = 63.3268 deg <--> 135.1705 deg
          Mean   = 106.2632 deg
          StdDev = 15.3985 deg

        O--O SUMMARY
          Range  = 1.7055 A <--> 3.3886 A
          Mean   = 2.6326 A
          StdDev = 0.3170 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 172.880 deg ; T1  -- T1   3.0662 A

T1  -- O2  -- T1  = 110.992 deg ; T1  -- T1   2.6791 A

T1  -- O3  -- T2  =  99.789 deg ; T1  -- T2   2.4403 A

T1  -- O4  -- T3  = 134.682 deg ; T1  -- T3   3.1457 A

T2  -- O5  -- T2  = 162.067 deg ; T2  -- T2   3.2315 A

T2  -- O6  -- T2  = 134.916 deg ; T2  -- T2   3.0470 A

T1  -- O7  -- T3  =  69.725 deg ; T1  -- T3   2.1486 A
T2  -- O7  -- T3  = 138.297 deg ; T2  -- T3   3.1219 A
T1  -- O7  -- T2  =  82.167 deg ; T1  -- T2   2.4403 A

T3  -- O8  -- T3  = 135.262 deg ; T3  -- T3   3.0635 A

T3  -- O9  -- T4  = 133.045 deg ; T3  -- T4   3.0241 A

T4  -- O10 -- T4  = 167.418 deg ; T4  -- T4   3.1130 A

T4  -- O11 -- T4  = 117.479 deg ; T4  -- T4   2.8630 A

T4  -- O12 -- T5  = 126.126 deg ; T4  -- T5   2.8650 A

T5  -- O13 -- T5  = 166.809 deg ; T5  -- T5   3.2112 A

T5  -- O14 -- T5  = 123.467 deg ; T5  -- T5   2.8091 A

T5  -- O15 -- T5  = 122.199 deg ; T5  -- T5   2.8235 A


        T-O-T SUMMARY
          Range  = 69.7254° <--> 172.8803 deg
          Mean   = 129.2541 deg
          StdDev = 27.9247 deg

        T--T SUMMARY
          Range  = 2.1486 A <--> 3.2315 A
          Mean   = 2.8878 A
          StdDev = 0.2976 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 1.7055 A
O1  -- O4  = 1.7055 A
O3  -- O4  = 2.0375 A
O3  -- O7  = 2.2179 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 3.0662 Angstrom
  T1  -- T1  = 2.6791 Angstrom
  T1  -- T3  = 2.1486 Angstrom
  T1  -- T2  = 2.4403 Angstrom
  T1  -- T3  = 3.1457 Angstrom
T2  -- T1  = 2.4403 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.1486 Angstrom
  T3  -- T1  = 3.1457 Angstrom
  T3  -- T3  = 3.0635 Angstrom
  T3  -- T4  = 3.0241 Angstrom
  T3  -- T2  = 3.1219 Angstrom