Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_40328718_WmB7FH.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 22.90 T-atoms per nm^3
Material density = 2.285 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6185 Angstrom
T1  -- O3  = 1.5653 Angstrom
T1  -- O2  = 1.5864 Angstrom
T1  -- O4  = 1.6180 Angstrom
      mean = 1.5970 Angstrom
        t1 = 0.025222  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017666  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5649 Angstrom
T2  -- O5  = 1.6108 Angstrom
T2  -- O6  = 1.6576 Angstrom
T2  -- O7  = 1.6221 Angstrom
      mean = 1.6139 Angstrom
        t1 = 0.043490  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027660  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6144 Angstrom
T3  -- O8  = 1.5947 Angstrom
T3  -- O9  = 1.6175 Angstrom
T3  -- O10 = 1.5984 Angstrom
      mean = 1.6062 Angstrom
        t1 = 0.009125  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007023  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.4908 Angstrom
T4  -- O12 = 1.6132 Angstrom
T4  -- O6  = 1.6505 Angstrom
T4  -- O13 = 1.7204 Angstrom
      mean = 1.6187 Angstrom
        t1 = 0.128291  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.085683  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6537 Angstrom
T5  -- O10 = 1.6314 Angstrom
T5  -- O13 = 1.7212 Angstrom
T5  -- O14 = 1.7572 Angstrom
      mean = 1.6909 Angstrom
        t1 = 0.077639  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.047775  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4908 A <--> 1.7572 A
          Mean   = 1.6253 A
          StdDev = 0.0581 A

       t1 Range  = 0.0091 <-- 0.0568 --> 0.1283
       t2 Range  = 0.0070 <-- 0.0372 --> 0.0857

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 117.816 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 106.344 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 108.982 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  = 109.117 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  = 108.767 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  = 105.070 deg; O2  -- O4  = 3 A
       105.070 deg <-- 109.349 deg --> 117.816 deg

O3  -- T2  -- O5  = 109.077 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.646 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 100.754 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 109.026 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.640 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 120.094 deg; O6  -- O7  = 3 A
       100.754 deg <-- 109.373 deg --> 120.094 deg

O4  -- T3  -- O8  = 109.929 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.576 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 110.939 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.116 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.536 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.705 deg; O9  -- O10 = 3 A
       107.536 deg <-- 109.467 deg --> 110.939 deg

O11 -- T4  -- O12 = 138.753 deg; O11 -- O12 = 3 A
O11 -- T4  -- O6  =  97.646 deg; O11 -- O6  = 2 A
O11 -- T4  -- O13 =  76.712 deg; O11 -- O13 = 2 A
O12 -- T4  -- O6  = 122.750 deg; O12 -- O6  = 3 A
O12 -- T4  -- O13 =  90.429 deg; O12 -- O13 = 2 A
O6  -- T4  -- O13 =  95.365 deg; O6  -- O13 = 2 A
       76.712 deg <-- 103.609 deg --> 138.753 deg

O7  -- T5  -- O10 = 102.049 deg; O7  -- O10 = 3 A
O7  -- T5  -- O13 = 101.984 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 115.672 deg; O7  -- O14 = 3 A
O10 -- T5  -- O13 = 109.130 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 105.026 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 121.353 deg; O13 -- O14 = 3 A
       101.984 deg <-- 109.202 deg --> 121.353 deg

        O-T-O SUMMARY
          Range  = 76.7122 deg <--> 138.7534 deg
          Mean   = 107.6806 deg
          StdDev = 10.0756 deg

        O--O SUMMARY
          Range  = 2.0008 A <--> 3.0328 A
          Mean   = 2.6184 A
          StdDev = 0.1872 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.068 deg ; T1  -- T1   3.0425 A

T1  -- O2  -- T1  = 140.102 deg ; T1  -- T1   2.9824 A

T1  -- O3  -- T2  = 118.438 deg ; T1  -- T2   2.6892 A

T1  -- O4  -- T3  = 146.536 deg ; T1  -- T3   3.0955 A

T2  -- O5  -- T2  = 128.266 deg ; T2  -- T2   2.8990 A

T2  -- O6  -- T4  = 172.548 deg ; T2  -- T4   3.3010 A

T2  -- O7  -- T5  = 139.487 deg ; T2  -- T5   3.0733 A

T3  -- O8  -- T3  = 159.204 deg ; T3  -- T3   3.1369 A

T3  -- O9  -- T3  = 132.250 deg ; T3  -- T3   2.9580 A

T3  -- O10 -- T5  = 155.972 deg ; T3  -- T5   3.1591 A

T4  -- O11 -- T4  = 135.324 deg ; T4  -- T4   2.7578 A

T4  -- O12 -- T4  = 110.837 deg ; T4  -- T4   2.6562 A

T4  -- O13 -- T5  = 140.984 deg ; T4  -- T5   3.2441 A

T5  -- O14 -- T5  = 136.851 deg ; T5  -- T5   3.2683 A


        T-O-T SUMMARY
          Range  = 110.8372° <--> 172.5476 deg
          Mean   = 139.7761 deg
          StdDev = 15.3015 deg

        T--T SUMMARY
          Range  = 2.6562 A <--> 3.3010 A
          Mean   = 3.0188 A
          StdDev = 0.2008 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O11 -- O13 = 2.0008 A
O11 -- O13 = 2.0008 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.6892 Angstrom
T2  -- T1  = 2.6892 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T3  = 3.1369 Angstrom
  T3  -- T3  = 2.9580 Angstrom
  T3  -- T4  = 3.2455 Angstrom
  T3  -- T5  = 3.1591 Angstrom
  T3  -- T1  = 3.0955 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 3.2455 Angstrom
  T4  -- T4  = 2.7578 Angstrom
  T4  -- T4  = 2.6562 Angstrom
  T4  -- T5  = 2.6670 Angstrom
  T4  -- T2  = 3.3010 Angstrom
  T4  -- T5  = 3.2441 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.0733 Angstrom
  T5  -- T3  = 3.1591 Angstrom
  T5  -- T4  = 2.6670 Angstrom
  T5  -- T4  = 3.2441 Angstrom
  T5  -- T5  = 3.2683 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

<TD10> = 894.000
Average ring size = 5.7143