Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39655071_fZPN6y.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.09 T-atoms per nm^3
Material density = 2.403 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5998 Angstrom
T1  -- O3  = 1.5776 Angstrom
T1  -- O2  = 1.6110 Angstrom
T1  -- O4  = 1.7193 Angstrom
      mean = 1.6269 Angstrom
        t1 = 0.100117  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063232  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4370 Angstrom
T2  -- O5  = 1.6667 Angstrom
T2  -- O6  = 1.6494 Angstrom
T2  -- O7  = 1.6195 Angstrom
      mean = 1.5931 Angstrom
        t1 = 0.106748  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.069251  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6803 Angstrom
T3  -- O8  = 1.7386 Angstrom
T3  -- O9  = 1.6088 Angstrom
T3  -- O10 = 1.5191 Angstrom
      mean = 1.6367 Angstrom
        t1 = 0.090703  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056346  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6852 Angstrom
T4  -- O11 = 1.7062 Angstrom
T4  -- O12 = 1.6392 Angstrom
T4  -- O13 = 1.6158 Angstrom
      mean = 1.6616 Angstrom
        t1 = 0.067326  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037550  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5467 Angstrom
T5  -- O13 = 1.6501 Angstrom
T5  -- O14 = 1.6723 Angstrom
T5  -- O15 = 1.6314 Angstrom
      mean = 1.6251 Angstrom
        t1 = 0.056744  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.050957  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4370 A <--> 1.7386 A
          Mean   = 1.6287 A
          StdDev = 0.0695 A

       t1 Range  = 0.0567 <-- 0.0843 --> 0.1067
       t2 Range  = 0.0376 <-- 0.0555 --> 0.0693

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 145.182 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 106.892 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  =  83.083 deg; O1  -- O4  = 2 A
O3  -- T1  -- O2  = 107.485 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  =  92.143 deg; O3  -- O4  = 2 A
O2  -- T1  -- O4  = 106.912 deg; O2  -- O4  = 3 A
       83.083 deg <-- 106.950 deg --> 145.182 deg

O3  -- T2  -- O5  = 106.249 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 109.254 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  83.785 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 115.248 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 120.899 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 115.298 deg; O6  -- O7  = 3 A
       83.785 deg <-- 108.455 deg --> 120.899 deg

O4  -- T3  -- O8  = 130.441 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 107.627 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  92.777 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 108.383 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.401 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 107.506 deg; O9  -- O10 = 3 A
       92.777 deg <-- 109.022 deg --> 130.441 deg

O7  -- T4  -- O11 = 121.718 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.466 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  94.448 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 109.392 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 112.360 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 108.113 deg; O12 -- O13 = 3 A
       94.448 deg <-- 109.249 deg --> 121.718 deg

O10 -- T5  -- O13 =  94.535 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 = 120.148 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 110.843 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 104.754 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 107.447 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 115.790 deg; O14 -- O15 = 3 A
       94.535 deg <-- 108.920 deg --> 120.148 deg

        O-T-O SUMMARY
          Range  = 83.0831 deg <--> 145.1819 deg
          Mean   = 108.2810 deg
          StdDev = 12.9398 deg

        O--O SUMMARY
          Range  = 2.0455 A <--> 3.1042 A
          Mean   = 2.6219 A
          StdDev = 0.2345 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 143.067 deg ; T1  -- T1   3.0349 A

T1  -- O2  -- T1  = 130.275 deg ; T1  -- T1   2.9233 A

T1  -- O3  -- T2  = 102.535 deg ; T1  -- T2   2.3533 A

T1  -- O4  -- T3  = 147.314 deg ; T1  -- T3   3.2623 A

T2  -- O5  -- T2  = 150.077 deg ; T2  -- T2   3.2203 A

T2  -- O6  -- T2  = 124.937 deg ; T2  -- T2   2.9250 A

T2  -- O7  -- T4  = 142.167 deg ; T2  -- T4   3.1263 A

T3  -- O8  -- T3  = 178.793 deg ; T3  -- T3   3.4768 A

T3  -- O9  -- T3  = 124.841 deg ; T3  -- T3   2.8519 A

T3  -- O10 -- T5  = 114.323 deg ; T3  -- T5   2.5759 A

T4  -- O11 -- T4  = 164.231 deg ; T4  -- T4   3.3801 A

T4  -- O12 -- T4  = 133.625 deg ; T4  -- T4   3.0134 A

T4  -- O13 -- T5  = 129.244 deg ; T4  -- T5   2.9507 A

T5  -- O14 -- T5  = 166.029 deg ; T5  -- T5   3.3196 A

T5  -- O15 -- T5  = 123.279 deg ; T5  -- T5   2.8712 A


        T-O-T SUMMARY
          Range  = 102.5346° <--> 178.7926 deg
          Mean   = 138.3157 deg
          StdDev = 19.9287 deg

        T--T SUMMARY
          Range  = 2.3533 A <--> 3.4768 A
          Mean   = 3.0190 A
          StdDev = 0.2894 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2029 A
O1  -- O4  = 2.2029 A
O3  -- O7  = 2.0455 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.0349 Angstrom
  T1  -- T1  = 2.9233 Angstrom
  T1  -- T2  = 2.3533 Angstrom
  T1  -- T4  = 2.9488 Angstrom
  T1  -- T3  = 3.2623 Angstrom
T2  -- T1  = 2.3533 Angstrom
T3  -- T5  = 2.5759 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 2.9488 Angstrom
  T4  -- T2  = 3.1263 Angstrom
  T4  -- T4  = 3.0134 Angstrom
  T4  -- T5  = 2.9507 Angstrom
  T4  -- T4  = 3.3801 Angstrom
T5  -- T3  = 2.5759 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

<TD10> = 975.600
Average ring size = 5.7307