Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39434080_kKv7hl.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 23.20 T-atoms per nm^3
Material density = 2.315 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6507 Angstrom
T1  -- O2  = 1.6265 Angstrom
T1  -- O3  = 1.5869 Angstrom
T1  -- O4  = 1.6099 Angstrom
      mean = 1.6185 Angstrom
        t1 = 0.055231  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037576  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6278 Angstrom
T2  -- O5  = 1.5632 Angstrom
T2  -- O6  = 1.6833 Angstrom
T2  -- O7  = 1.6300 Angstrom
      mean = 1.6261 Angstrom
        t1 = 0.057168  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061774  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6361 Angstrom
T3  -- O9  = 1.6069 Angstrom
T3  -- O10 = 1.5792 Angstrom
T3  -- O4  = 1.5644 Angstrom
      mean = 1.5967 Angstrom
        t1 = 0.060340  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052246  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6569 Angstrom
T4  -- O11 = 1.7329 Angstrom
T4  -- O12 = 1.6454 Angstrom
T4  -- O13 = 1.6730 Angstrom
      mean = 1.6771 Angstrom
        t1 = 0.062604  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.031019  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O14 = 1.6035 Angstrom
T5  -- O15 = 1.6454 Angstrom
T5  -- O10 = 1.6234 Angstrom
T5  -- O13 = 1.6616 Angstrom
      mean = 1.6335 Angstrom
        t1 = 0.122823  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.101216  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5632 A <--> 1.7329 A
          Mean   = 1.6304 A
          StdDev = 0.0406 A

       t1 Range  = 0.0552 <-- 0.0716 --> 0.1228
       t2 Range  = 0.0310 <-- 0.0568 --> 0.1012

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.941 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.735 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 117.752 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 117.761 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 105.817 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  94.603 deg; O3  -- O4  = 2 A
       94.603 deg <-- 109.435 deg --> 117.761 deg

O3  -- T2  -- O5  = 103.175 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 119.358 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 102.762 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 105.717 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 105.254 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 118.778 deg; O6  -- O7  = 3 A
       102.762 deg <-- 109.174 deg --> 119.358 deg

O8  -- T3  -- O9  = 111.813 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 117.279 deg; O8  -- O10 = 3 A
O8  -- T3  -- O4  = 109.172 deg; O8  -- O4  = 3 A
O9  -- T3  -- O10 = 112.980 deg; O9  -- O10 = 3 A
O9  -- T3  -- O4  = 111.800 deg; O9  -- O4  = 3 A
O10 -- T3  -- O4  =  92.159 deg; O10 -- O4  = 2 A
       92.159 deg <-- 109.200 deg --> 117.279 deg

O7  -- T4  -- O11 = 108.342 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.152 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 103.923 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 110.528 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 121.831 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 102.412 deg; O12 -- O13 = 3 A
       102.412 deg <-- 109.365 deg --> 121.831 deg

O14 -- T5  -- O15 = 121.750 deg; O14 -- O15 = 3 A
O14 -- T5  -- O10 = 121.354 deg; O14 -- O10 = 3 A
O14 -- T5  -- O13 =  82.586 deg; O14 -- O13 = 2 A
O15 -- T5  -- O10 = 116.777 deg; O15 -- O10 = 3 A
O15 -- T5  -- O13 = 105.827 deg; O15 -- O13 = 3 A
O10 -- T5  -- O13 =  78.654 deg; O10 -- O13 = 2 A
       78.654 deg <-- 104.491 deg --> 121.750 deg

        O-T-O SUMMARY
          Range  = 78.6536 deg <--> 121.8307 deg
          Mean   = 108.0406 deg
          StdDev = 10.7815 deg

        O--O SUMMARY
          Range  = 2.0821 A <--> 2.9766 A
          Mean   = 2.6266 A
          StdDev = 0.2060 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 174.058 deg ; T1  -- T1   3.2969 A

T1  -- O2  -- T1  = 111.658 deg ; T1  -- T1   2.6914 A

T1  -- O3  -- T2  = 118.847 deg ; T1  -- T2   2.7677 A

T1  -- O4  -- T3  = 118.243 deg ; T1  -- T3   2.7245 A

T2  -- O5  -- T2  = 160.857 deg ; T2  -- T2   3.0827 A

T2  -- O6  -- T2  = 129.413 deg ; T2  -- T2   3.0438 A

T2  -- O7  -- T4  = 120.309 deg ; T2  -- T4   2.8510 A

T3  -- O8  -- T3  = 107.595 deg ; T3  -- T3   2.6404 A

T3  -- O9  -- T3  = 129.504 deg ; T3  -- T3   2.9070 A

T3  -- O10 -- T5  = 145.032 deg ; T3  -- T5   3.0547 A

T4  -- O11 -- T4  = 166.488 deg ; T4  -- T4   3.4418 A

T4  -- O12 -- T4  = 131.050 deg ; T4  -- T4   2.9951 A

T4  -- O13 -- T5  = 161.624 deg ; T4  -- T5   3.2918 A

T5  -- O14 -- T5  = 170.734 deg ; T5  -- T5   3.1965 A

T5  -- O15 -- T5  = 120.619 deg ; T5  -- T5   2.8589 A


        T-O-T SUMMARY
          Range  = 107.5953° <--> 174.0583 deg
          Mean   = 137.7354 deg
          StdDev = 22.3770 deg

        T--T SUMMARY
          Range  = 2.6404 A <--> 3.4418 A
          Mean   = 2.9896 A
          StdDev = 0.2344 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O10 = 2.2644 A
O10 -- O13 = 2.0821 A
O13 -- O14 = 2.1551 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.6914 Angstrom
  T1  -- T2  = 2.7677 Angstrom
  T1  -- T5  = 2.9842 Angstrom
  T1  -- T1  = 3.2969 Angstrom
  T1  -- T3  = 2.7245 Angstrom
T2  -- T1  = 2.7677 Angstrom
T3  -- T3  = 2.6404 Angstrom
T3  -- T1  = 2.7245 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 2.9842 Angstrom
  T5  -- T5  = 3.1965 Angstrom
  T5  -- T5  = 2.8589 Angstrom
  T5  -- T3  = 3.0547 Angstrom
  T5  -- T4  = 3.2918 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

<TD10> = 975.600
Average ring size = 5.7307