Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39367031_LvfM9o.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 23.16 T-atoms per nm^3
Material density = 2.311 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5597 Angstrom
T1  -- O2  = 1.6888 Angstrom
T1  -- O3  = 1.6380 Angstrom
T1  -- O4  = 1.6376 Angstrom
      mean = 1.6310 Angstrom
        t1 = 0.062659  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052189  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6023 Angstrom
T2  -- O5  = 1.6466 Angstrom
T2  -- O6  = 1.6327 Angstrom
T2  -- O7  = 1.5904 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.067727  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.059757  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6668 Angstrom
T3  -- O8  = 1.7250 Angstrom
T3  -- O9  = 1.6456 Angstrom
T3  -- O10 = 1.6787 Angstrom
      mean = 1.6790 Angstrom
        t1 = 0.061321  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028261  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.4701 Angstrom
T4  -- O11 = 1.6117 Angstrom
T4  -- O12 = 1.6352 Angstrom
T4  -- O13 = 1.5475 Angstrom
      mean = 1.5661 Angstrom
        t1 = 0.065723  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6728 Angstrom
T5  -- O13 = 1.6019 Angstrom
T5  -- O14 = 1.5908 Angstrom
T5  -- O15 = 1.6354 Angstrom
      mean = 1.6252 Angstrom
        t1 = 0.100079  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.111752  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4701 A <--> 1.7250 A
          Mean   = 1.6239 A
          StdDev = 0.0550 A

       t1 Range  = 0.0613 <-- 0.0715 --> 0.1001
       t2 Range  = 0.0283 <-- 0.0582 --> 0.1118

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 104.271 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.241 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.641 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 120.682 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 119.512 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 102.369 deg; O3  -- O4  = 3 A
       102.369 deg <-- 109.119 deg --> 120.682 deg

O3  -- T2  -- O5  = 111.996 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 120.391 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  91.915 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 107.038 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 121.136 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 104.485 deg; O6  -- O7  = 3 A
       91.915 deg <-- 109.493 deg --> 121.136 deg

O4  -- T3  -- O8  = 107.987 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.837 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 107.309 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.153 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 121.242 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 100.875 deg; O9  -- O10 = 3 A
       100.875 deg <-- 109.401 deg --> 121.242 deg

O7  -- T4  -- O11 = 110.927 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.054 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  95.646 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 110.754 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 113.061 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 116.374 deg; O12 -- O13 = 3 A
       95.646 deg <-- 109.303 deg --> 116.374 deg

O10 -- T5  -- O13 =  85.915 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 =  84.837 deg; O10 -- O14 = 2 A
O10 -- T5  -- O15 = 108.252 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 121.432 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 116.613 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 121.207 deg; O14 -- O15 = 3 A
       84.837 deg <-- 106.376 deg --> 121.432 deg

        O-T-O SUMMARY
          Range  = 84.8369 deg <--> 121.4322 deg
          Mean   = 108.5796 deg
          StdDev = 10.1476 deg

        O--O SUMMARY
          Range  = 2.2023 A <--> 2.9661 A
          Mean   = 2.6260 A
          StdDev = 0.1980 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 159.279 deg ; T1  -- T1   3.0685 A

T1  -- O2  -- T1  = 130.708 deg ; T1  -- T1   3.0698 A

T1  -- O3  -- T2  = 115.819 deg ; T1  -- T2   2.7453 A

T1  -- O4  -- T3  = 120.290 deg ; T1  -- T3   2.8658 A

T2  -- O5  -- T2  = 173.203 deg ; T2  -- T2   3.2871 A

T2  -- O6  -- T2  = 110.446 deg ; T2  -- T2   2.6821 A

T2  -- O7  -- T4  = 114.847 deg ; T2  -- T4   2.5798 A

T3  -- O8  -- T3  = 164.962 deg ; T3  -- T3   3.4204 A

T3  -- O9  -- T3  = 129.455 deg ; T3  -- T3   2.9761 A

T3  -- O10 -- T5  = 167.355 deg ; T3  -- T5   3.3312 A

T4  -- O11 -- T4  = 129.854 deg ; T4  -- T4   2.9196 A

T4  -- O12 -- T4  = 107.620 deg ; T4  -- T4   2.6395 A

T4  -- O13 -- T5  = 152.340 deg ; T4  -- T5   3.0581 A

T5  -- O14 -- T5  = 173.956 deg ; T5  -- T5   3.1770 A

T5  -- O15 -- T5  = 117.024 deg ; T5  -- T5   2.7891 A


        T-O-T SUMMARY
          Range  = 107.6196° <--> 173.9559 deg
          Mean   = 137.8105 deg
          StdDev = 23.7357 deg

        T--T SUMMARY
          Range  = 2.5798 A <--> 3.4204 A
          Mean   = 2.9740 A
          StdDev = 0.2512 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O7  = 2.2950 A
O7  -- O13 = 2.2368 A
O10 -- O13 = 2.2322 A
O10 -- O14 = 2.2023 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.7453 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.7453 Angstrom
  T2  -- T2  = 3.2871 Angstrom
  T2  -- T2  = 2.6821 Angstrom
  T2  -- T4  = 2.5798 Angstrom
  T2  -- T5  = 3.0803 Angstrom
T4  -- T2  = 2.5798 Angstrom
T4  -- T4  = 2.6395 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.0803 Angstrom
  T5  -- T3  = 3.3312 Angstrom
  T5  -- T4  = 3.0581 Angstrom
  T5  -- T5  = 3.1770 Angstrom
  T5  -- T5  = 2.7891 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

<TD10> = 975.600
Average ring size = 5.7307