Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39366188_uB2aZO.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 21.31 T-atoms per nm^3
Material density = 2.126 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5971 Angstrom
T1  -- O2  = 1.6735 Angstrom
T1  -- O3  = 1.6802 Angstrom
T1  -- O4  = 1.6204 Angstrom
      mean = 1.6428 Angstrom
        t1 = 0.052181  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030855  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6403 Angstrom
T2  -- O5  = 1.6659 Angstrom
T2  -- O6  = 1.6429 Angstrom
T2  -- O7  = 1.5566 Angstrom
      mean = 1.6264 Angstrom
        t1 = 0.068354  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.057375  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6702 Angstrom
T3  -- O9  = 1.6309 Angstrom
T3  -- O10 = 1.6397 Angstrom
T3  -- O4  = 1.6496 Angstrom
      mean = 1.6476 Angstrom
        t1 = 0.029869  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021681  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.5089 Angstrom
T4  -- O11 = 1.5997 Angstrom
T4  -- O12 = 1.6288 Angstrom
T4  -- O13 = 1.6269 Angstrom
      mean = 1.5911 Angstrom
        t1 = 0.026949  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021947  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6332 Angstrom
T5  -- O13 = 1.6310 Angstrom
T5  -- O14 = 1.6553 Angstrom
T5  -- O15 = 1.6253 Angstrom
      mean = 1.6362 Angstrom
        t1 = 0.025853  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017146  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5089 A <--> 1.6802 A
          Mean   = 1.6288 A
          StdDev = 0.0393 A

       t1 Range  = 0.0259 <-- 0.0406 --> 0.0684
       t2 Range  = 0.0171 <-- 0.0298 --> 0.0574

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.816 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.878 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 101.622 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 117.456 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 116.606 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 102.379 deg; O3  -- O4  = 3 A
       101.622 deg <-- 109.293 deg --> 117.456 deg

O3  -- T2  -- O5  = 117.528 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 117.404 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  91.797 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 109.223 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 112.965 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 106.217 deg; O6  -- O7  = 3 A
       91.797 deg <-- 109.189 deg --> 117.528 deg

O8  -- T3  -- O9  = 110.435 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 113.440 deg; O8  -- O10 = 3 A
O8  -- T3  -- O4  = 110.468 deg; O8  -- O4  = 3 A
O9  -- T3  -- O10 = 106.951 deg; O9  -- O10 = 3 A
O9  -- T3  -- O4  = 108.815 deg; O9  -- O4  = 3 A
O10 -- T3  -- O4  = 106.533 deg; O10 -- O4  = 3 A
       106.533 deg <-- 109.440 deg --> 113.440 deg

O7  -- T4  -- O11 = 109.340 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 107.715 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 108.290 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 108.440 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 111.727 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 111.235 deg; O12 -- O13 = 3 A
       107.715 deg <-- 109.458 deg --> 111.727 deg

O10 -- T5  -- O13 = 106.457 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 111.546 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 107.650 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 114.324 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 107.422 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 109.156 deg; O14 -- O15 = 3 A
       106.457 deg <-- 109.426 deg --> 114.324 deg

        O-T-O SUMMARY
          Range  = 91.7973 deg <--> 117.5283 deg
          Mean   = 109.4109 deg
          StdDev = 5.3468 deg

        O--O SUMMARY
          Range  = 2.2964 A <--> 2.8664 A
          Mean   = 2.6554 A
          StdDev = 0.1170 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 129.250 deg; T1  -- T2  = 5.3569 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3854 A
T1  - O1  - T1  - O4  - T3  = 144.147 deg; T1  -- T3  = 5.5257 A
T2  - O2  - T1  - O3  - T1  = 131.088 deg; T2  -- T1  = 5.5121 A
T2  - O2  - T1  - O4  - T3  =  83.072 deg; T2  -- T3  = 3.7545 A
T1  - O3  - T1  - O4  - T3  =  74.084 deg; T1  -- T3  = 3.5876 A

T1  - O3  - T2  - O5  - T2  = 148.328 deg; T1  -- T2  = 5.9810 A
T1  - O3  - T2  - O6  - T2  = 121.526 deg; T1  -- T2  = 4.9071 A
T1  - O3  - T2  - O7  - T4  =  93.275 deg; T1  -- T4  = 4.0177 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.3031 A
T2  - O5  - T2  - O7  - T4  =  82.697 deg; T2  -- T4  = 3.9682 A
T2  - O6  - T2  - O7  - T4  =  90.408 deg; T2  -- T4  = 3.8054 A

T3  - O8  - T3  - O9  - T5  =  89.467 deg; T3  -- T5  = 4.3187 A
T3  - O8  - T3  - O10 - T1  = 120.836 deg; T3  -- T1  = 4.9449 A
T3  - O8  - T3  - O4  - T3  = 144.453 deg; T3  -- T3  = 5.9249 A
T5  - O9  - T3  - O10 - T1  = 126.941 deg; T5  -- T1  = 5.3561 A
T5  - O9  - T3  - O4  - T3  = 109.394 deg; T5  -- T3  = 5.3193 A
T1  - O10 - T3  - O4  - T3  =  71.790 deg; T1  -- T3  = 3.5876 A

T2  - O7  - T4  - O11 - T4  = 135.978 deg; T2  -- T4  = 5.1407 A
T2  - O7  - T4  - O12 - T4  =  89.592 deg; T2  -- T4  = 3.8054 A
T2  - O7  - T4  - O13 - T5  =  76.442 deg; T2  -- T5  = 3.6242 A
T4  - O11 - T4  - O12 - T4  = 120.000 deg; T4  -- T4  = 4.9223 A
T4  - O11 - T4  - O13 - T5  =  89.481 deg; T4  -- T5  = 4.2975 A
T4  - O12 - T4  - O13 - T5  = 147.013 deg; T4  -- T5  = 5.7108 A

T3  - O10 - T5  - O13 - T4  = 107.717 deg; T3  -- T4  = 5.1670 A
T3  - O10 - T5  - O14 - T5  = 119.513 deg; T3  -- T5  = 5.6357 A
T3  - O10 - T5  - O15 - T5  =  90.533 deg; T3  -- T5  = 4.3187 A
T4  - O13 - T5  - O14 - T5  = 105.512 deg; T4  -- T5  = 5.1716 A
T4  - O13 - T5  - O15 - T5  =  90.519 deg; T4  -- T5  = 4.2975 A
T5  - O14 - T5  - O15 - T5  = 137.883 deg; T5  -- T5  = 5.7571 A

        T-T-T SUMMARY
          Range  = 71.7900 deg <--> 148.3277 deg
          Mean   = 107.9141 deg
          StdDev = 24.0473 deg

        T--T SUMMARY
          Range  = 3.5876 A <--> 5.9810 A
          Mean   = 4.7300 A
          StdDev = 0.7762 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 163.991 deg ; T1  -- T1   3.1631 A

T1  -- O2  -- T1  = 130.344 deg ; T1  -- T1   3.0376 A

T1  -- O3  -- T2  = 121.064 deg ; T1  -- T2   2.8910 A

T1  -- O4  -- T3  = 115.751 deg ; T1  -- T3   2.7695 A

T2  -- O5  -- T2  = 172.680 deg ; T2  -- T2   3.3247 A

T2  -- O6  -- T2  = 112.487 deg ; T2  -- T2   2.7318 A

T2  -- O7  -- T4  = 118.150 deg ; T2  -- T4   2.6298 A

T3  -- O8  -- T3  = 163.197 deg ; T3  -- T3   3.3046 A

T3  -- O9  -- T3  = 126.747 deg ; T3  -- T3   2.9160 A

T3  -- O10 -- T5  = 158.025 deg ; T3  -- T5   3.2129 A

T4  -- O11 -- T4  = 131.219 deg ; T4  -- T4   2.9139 A

T4  -- O12 -- T4  = 116.440 deg ; T4  -- T4   2.7693 A

T4  -- O13 -- T5  = 155.758 deg ; T4  -- T5   3.1853 A

T5  -- O14 -- T5  = 179.319 deg ; T5  -- T5   3.3105 A

T5  -- O15 -- T5  = 122.948 deg ; T5  -- T5   2.8562 A


        T-O-T SUMMARY
          Range  = 112.4873° <--> 179.3190 deg
          Mean   = 139.2080 deg
          StdDev = 22.6252 deg

        T--T SUMMARY
          Range  = 2.6298 A <--> 3.3247 A
          Mean   = 3.0011 A
          StdDev = 0.2260 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O7  = 2.2964 A
T1  -- T3  = 2.7695 Angstrom
T2  -- T2  = 2.7318 Angstrom
T2  -- T4  = 2.6298 Angstrom
T3  -- T1  = 2.7695 Angstrom
T4  -- T2  = 2.6298 Angstrom
T4  -- T4  = 2.7693 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 38 59 88 124 165 206 256 317 376 438 510 591 678
TD10 = 973
Circuit symbol = 4.6.4.6.6.7_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.7_{2}.8
Weight = 22

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 59 87 116 157 207 256 308 370 439 511 592 680
TD10 = 954
Circuit symbol = 4.6.4.7_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.6.6
Weight = 18

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 63 91 125 166 214 265 321 388 459 528 603 686
TD10 = 1003
Circuit symbol = 4.4.6.7_{2}.7_{2}.8_{2}
Weight = 20
Vertex symbol  = 4.4.6.7_{2}.7_{2}.8
Weight = 20

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 35 56 86 123 161 204 255 314 374 439 514 599 686
TD10 = 956
Circuit symbol = 4.4.6.6.6.8_{6}
Weight = 24
Vertex symbol  = 4.4.6.6.6.8_{3}
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 23 41 62 92 124 160 210 265 320 380 448 524 600 677
TD10 = 992
Circuit symbol = 4.6.4.7_{2}.6.8_{2}
Weight = 18
Vertex symbol  = 4.6.4.7_{2}.7_{2}.8
Weight = 18

<TD10> = 975.600
Average ring size = 5.7307