Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39173401_BqRpYS.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 23.25 T-atoms per nm^3
Material density = 2.320 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5769 Angstrom
T1  -- O2  = 1.6429 Angstrom
T1  -- O3  = 1.6299 Angstrom
T1  -- O4  = 1.6390 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.040578  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032386  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6562 Angstrom
T2  -- O5  = 1.5910 Angstrom
T2  -- O6  = 1.6255 Angstrom
T2  -- O7  = 1.6077 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.031711  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022940  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6171 Angstrom
T3  -- O8  = 1.6669 Angstrom
T3  -- O9  = 1.7587 Angstrom
T3  -- O4  = 1.6474 Angstrom
      mean = 1.6725 Angstrom
        t1 = 0.063136  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032578  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.7625 Angstrom
T4  -- O10 = 1.6522 Angstrom
T4  -- O11 = 1.6850 Angstrom
T4  -- O12 = 1.5361 Angstrom
      mean = 1.6589 Angstrom
        t1 = 0.079835  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.087698  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6047 Angstrom
T5  -- O13 = 1.6367 Angstrom
T5  -- O14 = 1.5638 Angstrom
T5  -- O15 = 1.6138 Angstrom
      mean = 1.6047 Angstrom
        t1 = 0.040218  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049467  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5361 A <--> 1.7625 A
          Mean   = 1.6357 A
          StdDev = 0.0542 A

       t1 Range  = 0.0317 <-- 0.0511 --> 0.0798
       t2 Range  = 0.0229 <-- 0.0450 --> 0.0877

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.668 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.894 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 101.299 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 109.843 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 115.707 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 115.312 deg; O3  -- O4  = 3 A
       101.299 deg <-- 109.287 deg --> 115.707 deg

O3  -- T2  -- O5  = 108.742 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.312 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 113.988 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.695 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 101.342 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 110.479 deg; O6  -- O7  = 3 A
       101.342 deg <-- 109.426 deg --> 113.988 deg

O7  -- T3  -- O8  = 111.394 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 105.341 deg; O7  -- O9  = 3 A
O7  -- T3  -- O4  =  99.631 deg; O7  -- O4  = 2 A
O8  -- T3  -- O9  = 114.751 deg; O8  -- O9  = 3 A
O8  -- T3  -- O4  = 108.706 deg; O8  -- O4  = 3 A
O9  -- T3  -- O4  = 115.919 deg; O9  -- O4  = 3 A
       99.631 deg <-- 109.290 deg --> 115.919 deg

O9  -- T4  -- O10 = 115.452 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 122.052 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 =  97.681 deg; O9  -- O12 = 2 A
O10 -- T4  -- O11 = 109.390 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 107.538 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 101.948 deg; O11 -- O12 = 3 A
       97.681 deg <-- 109.010 deg --> 122.052 deg

O12 -- T5  -- O13 = 118.794 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 100.802 deg; O12 -- O14 = 2 A
O12 -- T5  -- O15 = 109.115 deg; O12 -- O15 = 3 A
O13 -- T5  -- O14 = 106.156 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.922 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 111.667 deg; O14 -- O15 = 3 A
       100.802 deg <-- 109.409 deg --> 118.794 deg

        O-T-O SUMMARY
          Range  = 97.6806 deg <--> 122.0519 deg
          Mean   = 109.2700 deg
          StdDev = 6.0759 deg

        O--O SUMMARY
          Range  = 2.4415 A <--> 3.0162 A
          Mean   = 2.6691 A
          StdDev = 0.1435 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  91.521 deg; T1  -- T2  = 4.1221 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1777 A
T1  - O1  - T1  - O4  - T3  = 130.991 deg; T1  -- T3  = 5.1326 A
T2  - O2  - T1  - O3  - T1  =  81.400 deg; T2  -- T1  = 4.0076 A
T2  - O2  - T1  - O4  - T3  = 128.642 deg; T2  -- T3  = 5.3074 A
T1  - O3  - T1  - O4  - T3  =  72.765 deg; T1  -- T3  = 3.5857 A

T1  - O3  - T2  - O5  - T2  = 140.343 deg; T1  -- T2  = 5.6805 A
T1  - O3  - T2  - O6  - T2  =  88.479 deg; T1  -- T2  = 4.1221 A
T1  - O3  - T2  - O7  - T3  =  76.945 deg; T1  -- T3  = 3.5857 A
T2  - O5  - T2  - O6  - T2  = 127.680 deg; T2  -- T2  = 5.3401 A
T2  - O5  - T2  - O7  - T3  =  87.263 deg; T2  -- T3  = 4.0052 A
T2  - O6  - T2  - O7  - T3  = 131.207 deg; T2  -- T3  = 5.1607 A

T2  - O7  - T3  - O8  - T3  = 128.642 deg; T2  -- T3  = 5.3560 A
T2  - O7  - T3  - O9  - T4  =  71.333 deg; T2  -- T4  = 3.6639 A
T2  - O7  - T3  - O4  - T1  =  90.382 deg; T2  -- T1  = 4.0076 A
T3  - O8  - T3  - O9  - T4  = 123.156 deg; T3  -- T4  = 5.8360 A
T3  - O8  - T3  - O4  - T1  = 117.982 deg; T3  -- T1  = 5.2069 A
T4  - O9  - T3  - O4  - T1  = 113.478 deg; T4  -- T1  = 5.3121 A

T3  - O9  - T4  - O10 - T4  = 114.602 deg; T3  -- T4  = 5.6675 A
T3  - O9  - T4  - O11 - T4  = 155.224 deg; T3  -- T4  = 6.2794 A
T3  - O9  - T4  - O12 - T5  =  76.406 deg; T3  -- T5  = 3.8646 A
T4  - O10 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.4307 A
T4  - O10 - T4  - O12 - T5  = 136.939 deg; T4  -- T5  = 5.5956 A
T4  - O11 - T4  - O12 - T5  =  87.704 deg; T4  -- T5  = 3.9569 A

T4  - O12 - T5  - O13 - T5  =  92.296 deg; T4  -- T5  = 3.9569 A
T4  - O12 - T5  - O14 - T5  = 139.513 deg; T4  -- T5  = 5.1940 A
T4  - O12 - T5  - O15 - T5  = 115.805 deg; T4  -- T5  = 4.7464 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 4.8189 A
T5  - O13 - T5  - O15 - T5  =  90.488 deg; T5  -- T5  = 3.9991 A
T5  - O14 - T5  - O15 - T5  =  89.512 deg; T5  -- T5  = 3.9991 A

        T-T-T SUMMARY
          Range  = 71.3334 deg <--> 155.2240 deg
          Mean   = 107.2629 deg
          StdDev = 24.1441 deg

        T--T SUMMARY
          Range  = 3.5857 A <--> 6.2794 A
          Mean   = 4.6950 A
          StdDev = 0.7910 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.335 deg ; T1  -- T1   3.1448 A

T1  -- O2  -- T1  = 113.639 deg ; T1  -- T1   2.7501 A

T1  -- O3  -- T2  = 131.704 deg ; T1  -- T2   2.9985 A

T1  -- O4  -- T3  = 123.153 deg ; T1  -- T3   2.8902 A

T2  -- O5  -- T2  = 145.652 deg ; T2  -- T2   3.0400 A

T2  -- O6  -- T2  = 126.988 deg ; T2  -- T2   2.9092 A

T2  -- O7  -- T3  = 117.504 deg ; T2  -- T3   2.7570 A

T3  -- O8  -- T3  = 145.322 deg ; T3  -- T3   3.1824 A

T3  -- O9  -- T4  = 157.225 deg ; T3  -- T4   3.4519 A

T4  -- O10 -- T4  = 166.735 deg ; T4  -- T4   3.2821 A

T4  -- O11 -- T4  = 124.056 deg ; T4  -- T4   2.9764 A

T4  -- O12 -- T5  = 120.659 deg ; T4  -- T5   2.7293 A

T5  -- O13 -- T5  = 122.715 deg ; T5  -- T5   2.8728 A

T5  -- O14 -- T5  = 127.650 deg ; T5  -- T5   2.8066 A

T5  -- O15 -- T5  = 117.391 deg ; T5  -- T5   2.7577 A


        T-O-T SUMMARY
          Range  = 113.6392° <--> 171.3353 deg
          Mean   = 134.1152 deg
          StdDev = 17.9940 deg

        T--T SUMMARY
          Range  = 2.7293 A <--> 3.4519 A
          Mean   = 2.9699 A
          StdDev = 0.2090 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7501 Angstrom
T2  -- T3  = 2.7570 Angstrom
T3  -- T2  = 2.7570 Angstrom
T4  -- T5  = 2.7293 Angstrom
T5  -- T4  = 2.7293 Angstrom
T5  -- T5  = 2.7577 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 17 36 59 85 123 164 203 256 318 377 445 530 617 697
TD10 = 956
Circuit symbol = 4.4.4.6.4.6_{3}
Weight = 11
Vertex symbol  = 4.4.4.6_{2}.4.8
Weight = 15

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 37 62 93 130 168 209 259 318 384 454 536 621 696
TD10 = 993
Circuit symbol = 4.6.4.6_{2}.6_{3}.8_{3}
Weight = 17
Vertex symbol  = 4.6.4.6_{2}.6_{2}.10
Weight = 22

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 36 62 91 121 164 220 274 323 386 461 534 616 713
TD10 = 1005
Circuit symbol = 4.6.6.8.6.8_{3}
Weight = 18
Vertex symbol  = 4.6.6.8_{2}.6.10_{8}
Weight = 24

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 22 39 55 77 119 165 202 252 317 379 444 526 612 688
TD10 = 946
Circuit symbol = 4.6.4.6.6.8_{2}
Weight = 13
Vertex symbol  = 4.6.4.6.10_{2}.10_{13}
Weight = 32

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 31 53 81 113 150 193 243 301 365 431 500 581 678
TD10 = 895
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8_{3}
Weight = 20

<TD10> = 959.000
Average ring size = 6.6012