Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_39151571_360OCx.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 22.83 T-atoms per nm^3
Material density = 2.278 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5759 Angstrom
T1  -- O3  = 1.6328 Angstrom
T1  -- O2  = 1.6418 Angstrom
T1  -- O4  = 1.6251 Angstrom
      mean = 1.6189 Angstrom
        t1 = 0.032235  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022664  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6051 Angstrom
T2  -- O5  = 1.6308 Angstrom
T2  -- O6  = 1.5781 Angstrom
T2  -- O7  = 1.5845 Angstrom
      mean = 1.5996 Angstrom
        t1 = 0.035722  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022884  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6342 Angstrom
T3  -- O8  = 1.6537 Angstrom
T3  -- O9  = 1.7761 Angstrom
T3  -- O10 = 1.6411 Angstrom
      mean = 1.6763 Angstrom
        t1 = 0.061194  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037612  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.7462 Angstrom
T4  -- O11 = 1.7073 Angstrom
T4  -- O12 = 1.7337 Angstrom
T4  -- O13 = 1.5444 Angstrom
      mean = 1.6829 Angstrom
        t1 = 0.096030  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.091041  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6162 Angstrom
T5  -- O13 = 1.5218 Angstrom
T5  -- O14 = 1.5837 Angstrom
T5  -- O15 = 1.6105 Angstrom
      mean = 1.5831 Angstrom
        t1 = 0.044948  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052650  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5218 A <--> 1.7761 A
          Mean   = 1.6322 A
          StdDev = 0.0642 A

       t1 Range  = 0.0322 <-- 0.0540 --> 0.0960
       t2 Range  = 0.0227 <-- 0.0454 --> 0.0910

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 108.091 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 107.632 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 103.072 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  = 109.647 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  = 112.407 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  = 115.454 deg; O2  -- O4  = 3 A
       103.072 deg <-- 109.384 deg --> 115.454 deg

O3  -- T2  -- O5  = 115.546 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.608 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 107.459 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 108.373 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 114.072 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 101.803 deg; O6  -- O7  = 2 A
       101.803 deg <-- 109.310 deg --> 115.546 deg

O4  -- T3  -- O8  = 106.600 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 112.971 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 103.442 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 113.850 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 106.781 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 112.428 deg; O9  -- O10 = 3 A
       103.442 deg <-- 109.345 deg --> 113.850 deg

O9  -- T4  -- O11 = 105.650 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 122.458 deg; O9  -- O12 = 3 A
O9  -- T4  -- O13 =  99.487 deg; O9  -- O13 = 3 A
O11 -- T4  -- O12 = 120.931 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.571 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 =  95.078 deg; O12 -- O13 = 2 A
       95.078 deg <-- 108.863 deg --> 122.458 deg

O10 -- T5  -- O13 = 104.760 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 =  96.653 deg; O10 -- O14 = 2 A
O10 -- T5  -- O15 = 112.612 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 113.867 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 113.391 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 113.973 deg; O14 -- O15 = 3 A
       96.653 deg <-- 109.210 deg --> 113.973 deg

        O-T-O SUMMARY
          Range  = 95.0775 deg <--> 122.4580 deg
          Mean   = 109.0102 deg
          StdDev = 6.2527 deg

        O--O SUMMARY
          Range  = 2.3903 A <--> 3.0503 A
          Mean   = 2.6573 A
          StdDev = 0.1504 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.890 deg ; T1  -- T1   3.1474 A

T1  -- O2  -- T1  = 112.338 deg ; T1  -- T1   2.7277 A

T1  -- O3  -- T2  = 119.166 deg ; T1  -- T2   2.7922 A

T1  -- O4  -- T3  = 132.314 deg ; T1  -- T3   2.9811 A

T2  -- O5  -- T2  = 176.732 deg ; T2  -- T2   3.2601 A

T2  -- O6  -- T2  = 115.378 deg ; T2  -- T2   2.6675 A

T2  -- O7  -- T2  = 118.114 deg ; T2  -- T2   2.7180 A

T3  -- O8  -- T3  = 125.381 deg ; T3  -- T3   2.9389 A

T3  -- O9  -- T4  = 138.820 deg ; T3  -- T4   3.2973 A

T3  -- O10 -- T5  = 124.792 deg ; T3  -- T5   2.8866 A

T4  -- O11 -- T4  = 159.889 deg ; T4  -- T4   3.3621 A

T4  -- O12 -- T4  = 151.147 deg ; T4  -- T4   3.3580 A

T4  -- O13 -- T5  = 119.735 deg ; T4  -- T5   2.6519 A

T5  -- O14 -- T5  = 179.275 deg ; T5  -- T5   3.1675 A

T5  -- O15 -- T5  = 111.426 deg ; T5  -- T5   2.6612 A


        T-O-T SUMMARY
          Range  = 111.4255° <--> 179.2747 deg
          Mean   = 137.2265 deg
          StdDev = 23.7732 deg

        T--T SUMMARY
          Range  = 2.6519 A <--> 3.3621 A
          Mean   = 2.9745 A
          StdDev = 0.2605 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.
T1  -- T1  = 2.7277 Angstrom
T1  -- T2  = 2.7922 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.7922 Angstrom
  T2  -- T2  = 3.2601 Angstrom
  T2  -- T2  = 2.6675 Angstrom
  T2  -- T2  = 2.7180 Angstrom
  T2  -- T4  = 3.1846 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T3  = 2.9389 Angstrom
  T3  -- T4  = 3.2973 Angstrom
  T3  -- T5  = 3.4285 Angstrom
  T3  -- T5  = 2.8866 Angstrom
  T3  -- T1  = 2.9811 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.1846 Angstrom
  T4  -- T3  = 3.2973 Angstrom
  T4  -- T4  = 3.3621 Angstrom
  T4  -- T4  = 3.3580 Angstrom
  T4  -- T5  = 2.6519 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T3  = 3.4285 Angstrom
  T5  -- T3  = 2.8866 Angstrom
  T5  -- T4  = 2.6519 Angstrom
  T5  -- T5  = 3.1675 Angstrom
  T5  -- T5  = 2.6612 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 54 82 121 162 206 258 314 373 444 526 608 688
TD10 = 955
Circuit symbol = 4.6.4.10_{12}.6.8_{5}
Weight = 34
Vertex symbol  = 4.6.4.10_{7}.8_{4}.10_{5}
Weight = 41

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 32 57 88 123 163 206 252 306 374 450 524 595 668
TD10 = 952
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.10_{4}
Weight = 23

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 32 56 83 115 158 208 266 329 391 457 530 610 694
TD10 = 949
Circuit symbol = 4.8_{2}.4_{2}.6.6_{4}.8_{3}
Weight = 18
Vertex symbol  = 4.8_{2}.4_{2}.6.6_{2}.8_{2}
Weight = 18

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 30 52 84 122 166 217 271 327 388 454 526 602 686
TD10 = 973
Circuit symbol = 4.8_{2}.4.8_{2}.4_{2}.10_{6}
Weight = 21
Vertex symbol  = 4.8_{2}.4.8_{2}.4_{2}.10_{2}
Weight = 21

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 7 12 25 47 76 110 151 199 251 308 371 442 516 586 660
TD10 = 883
Circuit symbol = 4.4.4.4_{2}.4.6_{5}
Weight = 11
Vertex symbol  = 4.4.4.4_{2}.4.6_{2}
Weight = 11

<TD10> = 942.400
Average ring size = 6.1314