Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_37888274_qosD2q.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 21.56 T-atoms per nm^3
Material density = 2.151 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6092 Angstrom
T1  -- O2  = 1.6494 Angstrom
T1  -- O3  = 1.6067 Angstrom
T1  -- O4  = 1.6688 Angstrom
      mean = 1.6335 Angstrom
        t1 = 0.028817  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025205  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6030 Angstrom
T2  -- O5  = 1.6175 Angstrom
T2  -- O6  = 1.6202 Angstrom
T2  -- O7  = 1.6130 Angstrom
      mean = 1.6134 Angstrom
        t1 = 0.004820  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003006  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6662 Angstrom
T3  -- O8  = 1.5161 Angstrom
T3  -- O9  = 1.6379 Angstrom
T3  -- O10 = 1.6829 Angstrom
      mean = 1.6258 Angstrom
        t1 = 0.069396  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044710  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.5138 Angstrom
T4  -- O11 = 1.5890 Angstrom
T4  -- O12 = 1.6685 Angstrom
T4  -- O9  = 1.6481 Angstrom
      mean = 1.6048 Angstrom
        t1 = 0.050986  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036746  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6820 Angstrom
T5  -- O12 = 1.6974 Angstrom
T5  -- O13 = 1.5998 Angstrom
T5  -- O14 = 1.6765 Angstrom
      mean = 1.6639 Angstrom
        t1 = 0.056968  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048943  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5138 A <--> 1.6974 A
          Mean   = 1.6283 A
          StdDev = 0.0493 A

       t1 Range  = 0.0048 <-- 0.0422 --> 0.0694
       t2 Range  = 0.0030 <-- 0.0317 --> 0.0489

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.366 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.877 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.622 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.225 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 115.164 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.272 deg; O3  -- O4  = 3 A
       106.877 deg <-- 109.421 deg --> 115.164 deg

O3  -- T2  -- O5  = 109.233 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.331 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.926 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.580 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.791 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.961 deg; O6  -- O7  = 3 A
       108.926 deg <-- 109.470 deg --> 109.961 deg

O4  -- T3  -- O8  = 106.457 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 103.877 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 120.756 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 106.140 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 =  98.239 deg; O8  -- O10 = 2 A
O9  -- T3  -- O10 = 119.645 deg; O9  -- O10 = 3 A
       98.239 deg <-- 109.186 deg --> 120.756 deg

O8  -- T4  -- O11 = 103.993 deg; O8  -- O11 = 2 A
O8  -- T4  -- O12 = 106.061 deg; O8  -- O12 = 3 A
O8  -- T4  -- O9  = 107.852 deg; O8  -- O9  = 3 A
O11 -- T4  -- O12 = 108.990 deg; O11 -- O12 = 3 A
O11 -- T4  -- O9  = 108.465 deg; O11 -- O9  = 3 A
O12 -- T4  -- O9  = 120.277 deg; O12 -- O9  = 3 A
       103.993 deg <-- 109.273 deg --> 120.277 deg

O10 -- T5  -- O12 = 113.298 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 101.558 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 119.516 deg; O10 -- O14 = 3 A
O12 -- T5  -- O13 = 107.649 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 108.849 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 104.729 deg; O13 -- O14 = 3 A
       101.558 deg <-- 109.267 deg --> 119.516 deg

        O-T-O SUMMARY
          Range  = 98.2393 deg <--> 120.7562 deg
          Mean   = 109.3813 deg
          StdDev = 5.4201 deg

        O--O SUMMARY
          Range  = 2.4212 A <--> 2.9115 A
          Mean   = 2.6567 A
          StdDev = 0.1287 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  89.881 deg; T1  -- T2  = 4.1033 A
T1  - O1  - T1  - O3  - T3  = 168.374 deg; T1  -- T3  = 5.8860 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3189 A
T2  - O2  - T1  - O3  - T3  =  90.400 deg; T2  -- T3  = 4.2039 A
T2  - O2  - T1  - O4  - T1  = 131.887 deg; T2  -- T1  = 5.5786 A
T3  - O3  - T1  - O4  - T1  =  98.435 deg; T3  -- T1  = 4.7076 A

T1  - O3  - T2  - O5  - T2  = 103.425 deg; T1  -- T2  = 4.6429 A
T1  - O3  - T2  - O6  - T2  =  90.119 deg; T1  -- T2  = 4.1033 A
T1  - O3  - T2  - O7  - T2  = 147.358 deg; T1  -- T2  = 5.6004 A
T2  - O5  - T2  - O6  - T2  =  90.368 deg; T2  -- T2  = 4.1828 A
T2  - O5  - T2  - O7  - T2  =  89.632 deg; T2  -- T2  = 4.1828 A
T2  - O6  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 5.0370 A

T1  - O4  - T3  - O8  - T4  =  88.574 deg; T1  -- T4  = 4.1463 A
T1  - O4  - T3  - O9  - T5  = 130.501 deg; T1  -- T5  = 5.4567 A
T1  - O4  - T3  - O10 - T4  =  79.906 deg; T1  -- T4  = 3.8285 A
T4  - O8  - T3  - O9  - T5  =  79.369 deg; T4  -- T5  = 3.7774 A
T4  - O8  - T3  - O10 - T4  =  89.408 deg; T4  -- T4  = 4.1276 A
T5  - O9  - T3  - O10 - T4  = 146.584 deg; T5  -- T4  = 5.6884 A

T3  - O8  - T4  - O11 - T4  = 140.902 deg; T3  -- T4  = 5.3263 A
T3  - O8  - T4  - O12 - T5  =  76.343 deg; T3  -- T5  = 3.5815 A
T3  - O8  - T4  - O9  - T3  =  90.537 deg; T3  -- T3  = 4.1685 A
T4  - O11 - T4  - O12 - T5  =  91.815 deg; T4  -- T5  = 4.0254 A
T4  - O11 - T4  - O9  - T3  = 114.114 deg; T4  -- T3  = 4.7647 A
T5  - O12 - T4  - O9  - T3  = 150.285 deg; T5  -- T3  = 5.6244 A

T3  - O10 - T5  - O12 - T4  = 122.358 deg; T3  -- T4  = 5.1399 A
T3  - O10 - T5  - O13 - T5  =  70.776 deg; T3  -- T5  = 3.5815 A
T3  - O10 - T5  - O14 - T5  = 136.648 deg; T3  -- T5  = 5.4876 A
T4  - O12 - T5  - O13 - T5  =  76.954 deg; T4  -- T5  = 3.7774 A
T4  - O12 - T5  - O14 - T5  =  88.185 deg; T4  -- T5  = 4.0254 A
T5  - O13 - T5  - O14 - T5  =  90.000 deg; T5  -- T5  = 4.3157 A

        T-T-T SUMMARY
          Range  = 70.7762 deg <--> 168.3736 deg
          Mean   = 106.6617 deg
          StdDev = 27.0332 deg

        T--T SUMMARY
          Range  = 3.5815 A <--> 5.8860 A
          Mean   = 4.5993 A
          StdDev = 0.7251 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.629 deg ; T1  -- T1   3.1997 A

T1  -- O2  -- T1  = 123.139 deg ; T1  -- T1   2.9009 A

T1  -- O3  -- T2  = 129.926 deg ; T1  -- T2   2.9081 A

T1  -- O4  -- T3  = 129.427 deg ; T1  -- T3   3.0155 A

T2  -- O5  -- T2  = 136.683 deg ; T2  -- T2   3.0066 A

T2  -- O6  -- T2  = 126.128 deg ; T2  -- T2   2.8888 A

T2  -- O7  -- T2  = 130.306 deg ; T2  -- T2   2.9274 A

T3  -- O8  -- T4  = 149.298 deg ; T3  -- T4   2.9218 A

T3  -- O9  -- T4  = 127.408 deg ; T3  -- T4   2.9459 A

T3  -- O10 -- T5  = 125.624 deg ; T3  -- T5   2.9932 A

T4  -- O11 -- T4  = 118.421 deg ; T4  -- T4   2.7300 A

T4  -- O12 -- T5  = 117.206 deg ; T4  -- T5   2.8730 A

T5  -- O13 -- T5  = 169.242 deg ; T5  -- T5   3.1853 A

T5  -- O14 -- T5  = 120.561 deg ; T5  -- T5   2.9119 A


        T-O-T SUMMARY
          Range  = 117.2063° <--> 169.2425 deg
          Mean   = 133.6427 deg
          StdDev = 16.1902 deg

        T--T SUMMARY
          Range  = 2.7300 A <--> 3.1997 A
          Mean   = 2.9577 A
          StdDev = 0.1170 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T4  -- T4  = 2.7300 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 34 45 64 98 133 162 200 253 306 365 424 488 570
TD10 = 771
Circuit symbol = 4.5_{2}.4.8_{4}.6.7_{2}
Weight = 20
Vertex symbol  = 4.5_{2}.4.8_{4}.12_{18}.*
Weight = 39

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 33 53 74 95 123 165 215 262 306 357 425 505 584
TD10 = 790
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8_{3}
Weight = 22

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 17 30 49 69 88 136 168 205 241 311 371 427 490 590
TD10 = 777
Circuit symbol = 4.5.4.7.5.6
Weight = 8
Vertex symbol  = 4.5.4.8_{2}.5.12_{10}
Weight = 35

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 29 46 70 95 124 165 210 252 300 367 440 504 560
TD10 = 770
Circuit symbol = 4.4.4.8_{4}.6.6_{3}
Weight = 15
Vertex symbol  = 4.4.4.8.6_{2}.12_{6}
Weight = 35

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 8 15 28 47 68 94 125 162 204 254 309 358 431 507 560
TD10 = 756
Circuit symbol = 4.4.4.6.4.6_{3}
Weight = 11
Vertex symbol  = 4.4.4.6_{2}.4.8
Weight = 15

<TD10> = 772.800
Average ring size = 7.2887