Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_37887429_j1pjqK.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.28 T-atoms per nm^3
Material density = 2.422 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5556 Angstrom
T1  -- O2  = 1.6130 Angstrom
T1  -- O3  = 1.6264 Angstrom
T1  -- O4  = 1.6228 Angstrom
      mean = 1.6044 Angstrom
        t1 = 0.046388  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.045377  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6224 Angstrom
T2  -- O5  = 1.6144 Angstrom
T2  -- O6  = 1.6251 Angstrom
T2  -- O7  = 1.6358 Angstrom
      mean = 1.6244 Angstrom
        t1 = 0.016303  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011130  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6551 Angstrom
T3  -- O8  = 1.6663 Angstrom
T3  -- O9  = 1.6338 Angstrom
T3  -- O10 = 1.7138 Angstrom
      mean = 1.6673 Angstrom
        t1 = 0.067615  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.069494  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.5417 Angstrom
T4  -- O12 = 1.5466 Angstrom
T4  -- O13 = 1.6711 Angstrom
T4  -- O9  = 1.5964 Angstrom
      mean = 1.5889 Angstrom
        t1 = 0.094725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.091371  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.8275 Angstrom
T5  -- O10 = 1.7247 Angstrom
T5  -- O13 = 1.6728 Angstrom
T5  -- O14 = 1.6737 Angstrom
T5  -- O15 = 1.7653 Angstrom
      mean = 1.7328 Angstrom

        T-O SUMMARY
          Range  = 1.5417 A <--> 1.8275 A
          Mean   = 1.6478 A
          StdDev = 0.0677 A

       t1 Range  = 0.0163 <-- 0.0450 --> 0.0947
       t2 Range  = 0.0111 <-- 0.0435 --> 0.0914

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.385 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 101.805 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 103.252 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 112.381 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.326 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 120.129 deg; O3  -- O4  = 3 A
       101.805 deg <-- 109.213 deg --> 120.129 deg

O3  -- T2  -- O5  = 109.732 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.719 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 113.590 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 107.722 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.610 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.310 deg; O6  -- O7  = 3 A
       107.719 deg <-- 109.447 deg --> 113.590 deg

O4  -- T3  -- O8  = 114.630 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  =  96.857 deg; O4  -- O9  = 2 A
O4  -- T3  -- O10 = 109.697 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 101.834 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 111.771 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 121.406 deg; O9  -- O10 = 3 A
       96.857 deg <-- 109.366 deg --> 121.406 deg

O11 -- T4  -- O12 =  95.018 deg; O11 -- O12 = 2 A
O11 -- T4  -- O13 = 125.527 deg; O11 -- O13 = 3 A
O11 -- T4  -- O9  =  91.706 deg; O11 -- O9  = 2 A
O12 -- T4  -- O13 = 105.249 deg; O12 -- O13 = 3 A
O12 -- T4  -- O9  = 115.629 deg; O12 -- O9  = 3 A
O13 -- T4  -- O9  = 121.314 deg; O13 -- O9  = 3 A
       91.706 deg <-- 109.074 deg --> 125.527 deg

O4  -- T5  -- O10 =  90.970 deg; O4  -- O10 = 3 A
O4  -- T5  -- O13 = 164.074 deg; O4  -- O13 = 3 A
O4  -- T5  -- O14 =  93.696 deg; O4  -- O14 = 3 A
O4  -- T5  -- O15 = 103.849 deg; O4  -- O15 = 3 A
O10 -- T5  -- O13 =  73.991 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 = 105.802 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 125.149 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 =  85.618 deg; O13 -- O14 = 2 A
O13 -- T5  -- O15 =  89.405 deg; O13 -- O15 = 2 A
O14 -- T5  -- O15 = 124.990 deg; O14 -- O15 = 3 A
       73.991 deg <-- 105.754 deg --> 164.074 deg

        O-T-O SUMMARY
          Range  = 73.9906 deg <--> 164.0743 deg
          Mean   = 108.1814 deg
          StdDev = 15.7397 deg

        O--O SUMMARY
          Range  = 2.0449 A <--> 3.4667 A
          Mean   = 2.6587 A
          StdDev = 0.2636 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 125.842 deg ; T1  -- T1   2.7702 A

T1  -- O2  -- T1  = 134.000 deg ; T1  -- T1   2.9696 A

T1  -- O3  -- T2  = 176.070 deg ; T1  -- T2   3.2469 A

T1  -- O4  -- T3  = 134.586 deg ; T1  -- T3   3.0239 A
T1  -- O4  -- T5  =  94.767 deg ; T1  -- T5   2.5429 A
T3  -- O4  -- T5  = 115.872 deg ; T3  -- T5   2.9528 A

T2  -- O5  -- T2  = 174.517 deg ; T2  -- T2   3.2250 A

T2  -- O6  -- T2  = 118.672 deg ; T2  -- T2   2.7957 A

T2  -- O7  -- T2  = 119.532 deg ; T2  -- T2   2.8266 A

T3  -- O8  -- T3  = 125.762 deg ; T3  -- T3   2.9663 A

T3  -- O9  -- T4  = 144.235 deg ; T3  -- T4   3.0742 A

T3  -- O10 -- T5  = 126.036 deg ; T3  -- T5   3.0643 A

T4  -- O11 -- T4  = 140.750 deg ; T4  -- T4   2.9042 A

T4  -- O12 -- T4  = 108.592 deg ; T4  -- T4   2.5118 A

T4  -- O13 -- T5  = 148.046 deg ; T4  -- T5   3.2148 A

T5  -- O14 -- T5  = 127.978 deg ; T5  -- T5   3.0083 A

T5  -- O15 -- T5  = 167.593 deg ; T5  -- T5   3.5099 A


        T-O-T SUMMARY
          Range  = 94.7673° <--> 176.0697 deg
          Mean   = 134.2853 deg
          StdDev = 21.8168 deg

        T--T SUMMARY
          Range  = 2.5118 A <--> 3.5099 A
          Mean   = 2.9769 A
          StdDev = 0.2432 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O9  -- O11 = 2.2521 A
O10 -- O13 = 2.0449 A
O11 -- O12 = 2.2772 A
O11 -- O12 = 2.2772 A
O13 -- O14 = 2.2742 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.9696 Angstrom
  T1  -- T2  = 3.2469 Angstrom
  T1  -- T3  = 3.0239 Angstrom
  T1  -- T5  = 2.5429 Angstrom
  T1  -- T1  = 2.7702 Angstrom
T2  -- T2  = 2.7957 Angstrom
T3  has 7 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.0239 Angstrom
  T3  -- T3  = 3.3266 Angstrom
  T3  -- T3  = 2.9663 Angstrom
  T3  -- T4  = 3.3199 Angstrom
  T3  -- T5  = 2.9528 Angstrom
  T3  -- T5  = 3.0643 Angstrom
  T3  -- T4  = 3.0742 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 3.3199 Angstrom
  T4  -- T4  = 2.5118 Angstrom
  T4  -- T5  = 3.2148 Angstrom
  T4  -- T3  = 3.0742 Angstrom
  T4  -- T4  = 2.9042 Angstrom
T5  has 5 oxygen-bridged T-atoms within 3.50 A
  T5  -- T1  = 2.5429 Angstrom
  T5  -- T3  = 2.9528 Angstrom
  T5  -- T3  = 3.0643 Angstrom
  T5  -- T4  = 3.2148 Angstrom
  T5  -- T5  = 3.0083 Angstrom