Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_37885656_vE42w7.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.34 T-atoms per nm^3
Material density = 2.428 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5723 Angstrom
T1  -- O3  = 1.5401 Angstrom
T1  -- O2  = 1.6487 Angstrom
T1  -- O4  = 1.5710 Angstrom
      mean = 1.5830 Angstrom
        t1 = 0.043916  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026790  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5735 Angstrom
T2  -- O5  = 1.5801 Angstrom
T2  -- O6  = 1.6161 Angstrom
T2  -- O7  = 1.6219 Angstrom
      mean = 1.5979 Angstrom
        t1 = 0.024221  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014616  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O10 = 1.6427 Angstrom
T3  -- O4  = 1.6317 Angstrom
T3  -- O8  = 1.5622 Angstrom
T3  -- O9  = 1.6457 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.054350  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037410  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6470 Angstrom
T4  -- O11 = 1.5863 Angstrom
T4  -- O12 = 1.6588 Angstrom
T4  -- O13 = 1.6602 Angstrom
      mean = 1.6381 Angstrom
        t1 = 0.042588  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026726  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6409 Angstrom
T5  -- O13 = 1.6573 Angstrom
T5  -- O14 = 1.6933 Angstrom
T5  -- O15 = 1.7154 Angstrom
      mean = 1.6767 Angstrom
        t1 = 0.090846  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090949  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5401 A <--> 1.7154 A
          Mean   = 1.6233 A
          StdDev = 0.0455 A

       t1 Range  = 0.0242 <-- 0.0512 --> 0.0908
       t2 Range  = 0.0146 <-- 0.0393 --> 0.0909

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 112.808 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.270 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 102.708 deg; O1  -- O4  = 2 A
O3  -- T1  -- O2  = 109.672 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  = 104.664 deg; O3  -- O4  = 2 A
O2  -- T1  -- O4  = 118.675 deg; O2  -- O4  = 3 A
       102.708 deg <-- 109.466 deg --> 118.675 deg

O3  -- T2  -- O5  = 104.136 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 109.519 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 113.693 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.232 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.654 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.376 deg; O6  -- O7  = 3 A
       104.136 deg <-- 109.435 deg --> 113.693 deg

O10 -- T3  -- O4  = 118.702 deg; O10 -- O4  = 3 A
O10 -- T3  -- O8  = 106.760 deg; O10 -- O8  = 3 A
O10 -- T3  -- O9  = 116.468 deg; O10 -- O9  = 3 A
O4  -- T3  -- O8  =  98.704 deg; O4  -- O8  = 2 A
O4  -- T3  -- O9  = 109.740 deg; O4  -- O9  = 3 A
O8  -- T3  -- O9  = 103.648 deg; O8  -- O9  = 3 A
       98.704 deg <-- 109.004 deg --> 118.702 deg

O9  -- T4  -- O11 = 106.275 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 110.395 deg; O9  -- O12 = 3 A
O9  -- T4  -- O13 = 113.571 deg; O9  -- O13 = 3 A
O11 -- T4  -- O12 = 106.162 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 102.788 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 116.543 deg; O12 -- O13 = 3 A
       102.788 deg <-- 109.289 deg --> 116.543 deg

O10 -- T5  -- O13 =  96.810 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 =  91.148 deg; O10 -- O14 = 2 A
O10 -- T5  -- O15 = 101.439 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 114.800 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 115.318 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 126.086 deg; O14 -- O15 = 3 A
       91.148 deg <-- 107.600 deg --> 126.086 deg

        O-T-O SUMMARY
          Range  = 91.1478 deg <--> 126.0863 deg
          Mean   = 108.6620 deg
          StdDev = 7.1403 deg

        O--O SUMMARY
          Range  = 2.3815 A <--> 3.0383 A
          Mean   = 2.6325 A
          StdDev = 0.1439 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  =  90.281 deg; T1  -- T2  = 3.8181 A
T1  - O1  - T1  - O2  - T3  = 173.881 deg; T1  -- T3  = 5.6028 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1161 A
T2  - O3  - T1  - O2  - T3  =  84.911 deg; T2  -- T3  = 3.8373 A
T2  - O3  - T1  - O4  - T1  = 141.901 deg; T2  -- T1  = 5.5497 A
T3  - O2  - T1  - O4  - T1  =  96.119 deg; T3  -- T1  = 4.5349 A

T1  - O3  - T2  - O5  - T2  = 128.030 deg; T1  -- T2  = 5.2838 A
T1  - O3  - T2  - O6  - T2  =  89.719 deg; T1  -- T2  = 3.8181 A
T1  - O3  - T2  - O7  - T2  = 133.150 deg; T1  -- T2  = 4.9539 A
T2  - O5  - T2  - O6  - T2  =  89.872 deg; T2  -- T2  = 4.1326 A
T2  - O5  - T2  - O7  - T2  =  90.128 deg; T2  -- T2  = 4.1326 A
T2  - O6  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 4.6392 A

T1  - O10 - T3  - O4  - T3  = 126.119 deg; T1  -- T3  = 5.2363 A
T1  - O10 - T3  - O8  - T5  =  93.404 deg; T1  -- T5  = 4.5402 A
T1  - O10 - T3  - O9  - T4  = 116.447 deg; T1  -- T4  = 5.0765 A
T3  - O4  - T3  - O8  - T5  =  92.576 deg; T3  -- T5  = 4.4885 A
T3  - O4  - T3  - O9  - T4  =  89.944 deg; T3  -- T4  = 4.1995 A
T5  - O8  - T3  - O9  - T4  = 140.415 deg; T5  -- T4  = 5.9266 A

T3  - O9  - T4  - O11 - T4  =  84.412 deg; T3  -- T4  = 4.1494 A
T3  - O9  - T4  - O12 - T4  =  90.056 deg; T3  -- T4  = 4.1995 A
T3  - O9  - T4  - O13 - T5  = 104.696 deg; T3  -- T5  = 4.7640 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.2963 A
T4  - O11 - T4  - O13 - T5  =  88.001 deg; T4  -- T5  = 4.2758 A
T4  - O12 - T4  - O13 - T5  = 164.836 deg; T4  -- T5  = 5.8619 A

T3  - O10 - T5  - O13 - T4  =  82.265 deg; T3  -- T4  = 4.1340 A
T3  - O10 - T5  - O14 - T5  =  89.185 deg; T3  -- T5  = 4.6406 A
T3  - O10 - T5  - O15 - T5  =  87.424 deg; T3  -- T5  = 4.4885 A
T4  - O13 - T5  - O14 - T5  =  84.830 deg; T4  -- T5  = 4.2758 A
T4  - O13 - T5  - O15 - T5  = 124.100 deg; T4  -- T5  = 5.4903 A
T5  - O14 - T5  - O15 - T5  = 150.000 deg; T5  -- T5  = 6.3245 A

        T-T-T SUMMARY
          Range  = 82.2648 deg <--> 173.8814 deg
          Mean   = 106.2874 deg
          StdDev = 24.6155 deg

        T--T SUMMARY
          Range  = 3.8181 A <--> 6.3245 A
          Mean   = 4.6749 A
          StdDev = 0.6509 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 175.565 deg ; T1  -- T1   3.1422 A

T1  -- O2  -- T1  = 107.470 deg ; T1  -- T1   2.6587 A

T1  -- O3  -- T2  = 122.311 deg ; T1  -- T2   2.7273 A

T1  -- O4  -- T3  = 134.362 deg ; T1  -- T3   2.9521 A

T2  -- O5  -- T2  = 169.585 deg ; T2  -- T2   3.1471 A

T2  -- O6  -- T2  = 112.368 deg ; T2  -- T2   2.6855 A

T2  -- O7  -- T2  = 110.881 deg ; T2  -- T2   2.6715 A

T3  -- O8  -- T3  = 138.479 deg ; T3  -- T3   2.9217 A

T3  -- O9  -- T4  = 132.977 deg ; T3  -- T4   3.0194 A

T3  -- O10 -- T5  = 173.675 deg ; T3  -- T5   3.2786 A

T4  -- O11 -- T4  = 168.026 deg ; T4  -- T4   3.1553 A

T4  -- O12 -- T4  = 123.027 deg ; T4  -- T4   2.9158 A

T4  -- O13 -- T5  = 129.275 deg ; T4  -- T5   2.9977 A

T5  -- O14 -- T5  = 159.231 deg ; T5  -- T5   3.3311 A

T5  -- O15 -- T5  = 139.284 deg ; T5  -- T5   3.2164 A


        T-O-T SUMMARY
          Range  = 107.4701° <--> 175.5652 deg
          Mean   = 139.7677 deg
          StdDev = 22.9680 deg

        T--T SUMMARY
          Range  = 2.6587 A <--> 3.3311 A
          Mean   = 2.9880 A
          StdDev = 0.2180 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6587 Angstrom
T1  -- T2  = 2.7273 Angstrom
T2  -- T1  = 2.7273 Angstrom
T2  -- T2  = 2.6855 Angstrom
T2  -- T2  = 2.6715 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 32 46 68 102 140 176 218 271 333 400 471 546 620
TD10 = 817
Circuit symbol = 4.6.4.6_{2}.6.8_{4}
Weight = 19
Vertex symbol  = 4.6.4.6_{2}.8.10
Weight = 24

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 30 49 72 98 132 175 219 262 313 381 462 545 627
TD10 = 806
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 18

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 36 57 79 107 147 197 251 305 359 420 495 578 664
TD10 = 909
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.6.6
Weight = 14

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 35 60 86 112 147 196 256 315 367 421 487 571 667
TD10 = 924
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 13
Vertex symbol  = 4.4.4.6_{2}.10_{4}.12
Weight = 35

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 88 126 166 207 253 305 368 444 519 589 662
TD10 = 969
Circuit symbol = 4.4.6_{2}.8.8_{3}.8_{4}
Weight = 24
Vertex symbol  = 4.4.6_{2}.8.8_{2}.10_{3}
Weight = 29

<TD10> = 885.000
Average ring size = 5.8427