Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_37646709_0DmrK6.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 22.72 T-atoms per nm^3
Material density = 2.267 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6024 Angstrom
T1  -- O2  = 1.6626 Angstrom
T1  -- O3  = 1.6763 Angstrom
T1  -- O4  = 1.6292 Angstrom
      mean = 1.6427 Angstrom
        t1 = 0.038725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027166  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6971 Angstrom
T2  -- O5  = 1.7049 Angstrom
T2  -- O6  = 1.7110 Angstrom
T2  -- O7  = 1.6272 Angstrom
      mean = 1.6851 Angstrom
        t1 = 0.060156  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025133  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6236 Angstrom
T3  -- O7  = 1.6219 Angstrom
T3  -- O8  = 1.5724 Angstrom
T3  -- O9  = 1.6125 Angstrom
      mean = 1.6076 Angstrom
        t1 = 0.028758  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019217  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.5928 Angstrom
T4  -- O10 = 1.5703 Angstrom
T4  -- O11 = 1.6287 Angstrom
T4  -- O12 = 1.6022 Angstrom
      mean = 1.5985 Angstrom
        t1 = 0.029551  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030020  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5938 Angstrom
T5  -- O13 = 1.6044 Angstrom
T5  -- O14 = 1.5990 Angstrom
T5  -- O15 = 1.6101 Angstrom
      mean = 1.6018 Angstrom
        t1 = 0.007377  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007725  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5703 A <--> 1.7110 A
          Mean   = 1.6271 A
          StdDev = 0.0408 A

       t1 Range  = 0.0074 <-- 0.0329 --> 0.0602
       t2 Range  = 0.0077 <-- 0.0219 --> 0.0300

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.916 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.258 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.681 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 118.312 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.884 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.422 deg; O3  -- O4  = 3 A
       105.258 deg <-- 109.412 deg --> 118.312 deg

O3  -- T2  -- O5  = 110.368 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.142 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 103.891 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 118.451 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 105.100 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.834 deg; O6  -- O7  = 3 A
       103.891 deg <-- 109.298 deg --> 118.451 deg

O4  -- T3  -- O7  = 112.411 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 108.680 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 111.466 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 107.108 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 113.352 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 103.212 deg; O8  -- O9  = 2 A
       103.212 deg <-- 109.372 deg --> 113.352 deg

O9  -- T4  -- O10 = 104.516 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 114.309 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 111.916 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 109.771 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 105.007 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 110.708 deg; O11 -- O12 = 3 A
       104.516 deg <-- 109.371 deg --> 114.309 deg

O12 -- T5  -- O13 = 110.035 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 108.245 deg; O12 -- O14 = 3 A
O12 -- T5  -- O15 = 109.211 deg; O12 -- O15 = 3 A
O13 -- T5  -- O14 = 109.742 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.840 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 109.743 deg; O14 -- O15 = 3 A
       108.245 deg <-- 109.469 deg --> 110.035 deg

        O-T-O SUMMARY
          Range  = 103.2119 deg <--> 118.4507 deg
          Mean   = 109.2333 deg
          StdDev = 3.5617 deg

        O--O SUMMARY
          Range  = 2.4963 A <--> 2.9349 A
          Mean   = 2.6526 A
          StdDev = 0.0910 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 176.288 deg; T1  -- T2  = 5.8399 A
T1  - O1  - T1  - O3  - T3  =  91.098 deg; T1  -- T3  = 4.1725 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2872 A
T2  - O2  - T1  - O3  - T3  =  92.425 deg; T2  -- T3  = 4.3177 A
T2  - O2  - T1  - O4  - T1  =  91.432 deg; T2  -- T1  = 4.4341 A
T3  - O3  - T1  - O4  - T1  =  85.592 deg; T3  -- T1  = 4.2089 A

T1  - O3  - T2  - O5  - T2  = 122.964 deg; T1  -- T2  = 5.5209 A
T1  - O3  - T2  - O6  - T3  =  93.812 deg; T1  -- T3  = 4.4976 A
T1  - O3  - T2  - O7  - T2  =  88.213 deg; T1  -- T2  = 4.4341 A
T2  - O5  - T2  - O6  - T3  =  87.072 deg; T2  -- T3  = 4.4490 A
T2  - O5  - T2  - O7  - T2  = 141.786 deg; T2  -- T2  = 6.2928 A
T3  - O6  - T2  - O7  - T2  = 114.633 deg; T3  -- T2  = 5.5017 A

T1  - O4  - T3  - O7  - T2  = 139.354 deg; T1  -- T2  = 5.7744 A
T1  - O4  - T3  - O8  - T3  =  88.902 deg; T1  -- T3  = 4.1725 A
T1  - O4  - T3  - O9  - T4  = 119.757 deg; T1  -- T4  = 5.0111 A
T2  - O7  - T3  - O8  - T3  =  92.928 deg; T2  -- T3  = 4.4490 A
T2  - O7  - T3  - O9  - T4  =  90.967 deg; T2  -- T4  = 4.2634 A
T3  - O8  - T3  - O9  - T4  = 126.733 deg; T3  -- T4  = 5.1575 A

T3  - O9  - T4  - O10 - T4  =  96.891 deg; T3  -- T4  = 4.4499 A
T3  - O9  - T4  - O11 - T4  = 173.089 deg; T3  -- T4  = 5.4725 A
T3  - O9  - T4  - O12 - T5  =  85.818 deg; T3  -- T5  = 3.9547 A
T4  - O10 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.1266 A
T4  - O10 - T4  - O12 - T5  = 124.797 deg; T4  -- T5  = 5.4417 A
T4  - O11 - T4  - O12 - T5  =  90.685 deg; T4  -- T5  = 4.0492 A

T4  - O12 - T5  - O13 - T5  = 126.656 deg; T4  -- T5  = 5.1272 A
T4  - O12 - T5  - O14 - T5  =  89.315 deg; T4  -- T5  = 4.0492 A
T4  - O12 - T5  - O15 - T5  = 136.852 deg; T4  -- T5  = 5.7497 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 4.7510 A
T5  - O13 - T5  - O15 - T5  =  90.173 deg; T5  -- T5  = 4.1993 A
T5  - O14 - T5  - O15 - T5  =  89.827 deg; T5  -- T5  = 4.1993 A

        T-T-T SUMMARY
          Range  = 85.5917 deg <--> 176.2885 deg
          Mean   = 108.1993 deg
          StdDev = 24.3987 deg

        T--T SUMMARY
          Range  = 3.9547 A <--> 6.2928 A
          Mean   = 4.7619 A
          StdDev = 0.6602 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.899 deg ; T1  -- T1   3.2003 A

T1  -- O2  -- T1  = 118.163 deg ; T1  -- T1   2.8528 A

T1  -- O3  -- T2  = 124.849 deg ; T1  -- T2   2.9902 A

T1  -- O4  -- T3  = 133.675 deg ; T1  -- T3   2.9907 A

T2  -- O5  -- T2  = 162.206 deg ; T2  -- T2   3.3687 A

T2  -- O6  -- T2  = 148.170 deg ; T2  -- T2   3.2909 A

T2  -- O7  -- T3  = 154.125 deg ; T2  -- T3   3.1667 A

T3  -- O8  -- T3  = 141.336 deg ; T3  -- T3   2.9674 A

T3  -- O9  -- T4  = 121.874 deg ; T3  -- T4   2.8017 A

T4  -- O10 -- T4  = 174.939 deg ; T4  -- T4   3.1373 A

T4  -- O11 -- T4  = 110.755 deg ; T4  -- T4   2.6808 A

T4  -- O12 -- T5  = 139.956 deg ; T4  -- T5   3.0028 A

T5  -- O13 -- T5  = 164.529 deg ; T5  -- T5   3.1797 A

T5  -- O14 -- T5  = 117.463 deg ; T5  -- T5   2.7333 A

T5  -- O15 -- T5  = 117.474 deg ; T5  -- T5   2.7526 A


        T-O-T SUMMARY
          Range  = 110.7551° <--> 174.9385 deg
          Mean   = 140.2275 deg
          StdDev = 21.1185 deg

        T--T SUMMARY
          Range  = 2.6808 A <--> 3.3687 A
          Mean   = 3.0077 A
          StdDev = 0.2060 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T4  -- T4  = 2.6808 Angstrom
T5  -- T5  = 2.7333 Angstrom
T5  -- T5  = 2.7526 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 35 60 86 112 147 196 256 315 367 421 487 571 667
TD10 = 924
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 13
Vertex symbol  = 4.4.4.6_{2}.10_{4}.12
Weight = 35

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 57 88 126 166 207 253 305 368 444 519 589 662
TD10 = 969
Circuit symbol = 4.4.6_{2}.8.8_{3}.8_{4}
Weight = 24
Vertex symbol  = 4.4.6_{2}.8.8_{2}.10_{3}
Weight = 29

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 36 57 79 107 147 197 251 305 359 420 495 578 664
TD10 = 909
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.6.6
Weight = 14

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 32 46 68 102 140 176 218 271 333 400 471 546 620
TD10 = 817
Circuit symbol = 4.6.4.6_{2}.6.8_{4}
Weight = 19
Vertex symbol  = 4.6.4.6_{2}.8.10
Weight = 24

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 30 49 72 98 132 175 219 262 313 381 462 545 627
TD10 = 806
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 18

<TD10> = 885.000
Average ring size = 5.8427