Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_34607549_CvIec3.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 24.78 T-atoms per nm^3
Material density = 2.472 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6366 Angstrom
T1  -- O2  = 1.6236 Angstrom
T1  -- O4  = 1.6089 Angstrom
T1  -- O3  = 1.6471 Angstrom
      mean = 1.6290 Angstrom
        t1 = 0.021262  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012906  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6093 Angstrom
T2  -- O5  = 1.6193 Angstrom
T2  -- O6  = 1.6412 Angstrom
T2  -- O7  = 1.6672 Angstrom
      mean = 1.6343 Angstrom
        t1 = 0.023564  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013560  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6269 Angstrom
T3  -- O8  = 1.6473 Angstrom
T3  -- O9  = 1.6238 Angstrom
T3  -- O10 = 1.6238 Angstrom
      mean = 1.6305 Angstrom
        t1 = 0.028152  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020227  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6019 Angstrom
T4  -- O11 = 1.6169 Angstrom
T4  -- O12 = 1.6110 Angstrom
T4  -- O13 = 1.6064 Angstrom
      mean = 1.6090 Angstrom
        t1 = 0.010828  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009888  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6394 Angstrom
T5  -- O14 = 1.6364 Angstrom
T5  -- O15 = 1.6333 Angstrom
T5  -- O16 = 1.6231 Angstrom
      mean = 1.6330 Angstrom
        t1 = 0.015786  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006507  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6019 A <--> 1.6672 A
          Mean   = 1.6272 A
          StdDev = 0.0161 A

       t1 Range  = 0.0108 <-- 0.0199 --> 0.0282
       t2 Range  = 0.0065 <-- 0.0126 --> 0.0202

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.322 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 108.393 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 114.325 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 108.100 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.253 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 108.282 deg; O4  -- O3  = 3 A
       108.100 deg <-- 109.446 deg --> 114.325 deg

O4  -- T2  -- O5  = 108.259 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.439 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 108.772 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.100 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.566 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 113.581 deg; O6  -- O7  = 3 A
       108.259 deg <-- 109.453 deg --> 113.581 deg

O7  -- T3  -- O8  = 116.587 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 106.717 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 104.734 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 108.473 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.560 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 111.794 deg; O9  -- O10 = 3 A
       104.734 deg <-- 109.477 deg --> 116.587 deg

O9  -- T4  -- O11 = 112.910 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 107.895 deg; O9  -- O12 = 3 A
O9  -- T4  -- O13 = 108.169 deg; O9  -- O13 = 3 A
O11 -- T4  -- O12 = 108.787 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.557 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.470 deg; O12 -- O13 = 3 A
       107.895 deg <-- 109.464 deg --> 112.910 deg

O10 -- T5  -- O14 = 110.481 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 107.886 deg; O10 -- O15 = 3 A
O10 -- T5  -- O16 = 108.877 deg; O10 -- O16 = 3 A
O14 -- T5  -- O15 = 110.773 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 109.315 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 109.472 deg; O15 -- O16 = 3 A
       107.886 deg <-- 109.467 deg --> 110.773 deg

        O-T-O SUMMARY
          Range  = 104.7345 deg <--> 116.5868 deg
          Mean   = 109.3864 deg
          StdDev = 2.4213 deg

        O--O SUMMARY
          Range  = 2.5744 A <--> 2.7856 A
          Mean   = 2.6555 A
          StdDev = 0.0490 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.536 deg ; T1  -- T1   3.2539 A

T1  -- O2  -- T1  = 125.530 deg ; T1  -- T1   2.8872 A

T1  -- O3  -- T1  = 127.646 deg ; T1  -- T1   2.9562 A

T1  -- O4  -- T2  = 178.829 deg ; T1  -- T2   3.2181 A

T2  -- O5  -- T2  = 122.728 deg ; T2  -- T2   2.8425 A

T2  -- O6  -- T2  = 125.057 deg ; T2  -- T2   2.9124 A

T2  -- O7  -- T3  = 118.762 deg ; T2  -- T3   2.8349 A

T3  -- O8  -- T3  = 112.831 deg ; T3  -- T3   2.7448 A

T3  -- O9  -- T4  = 127.051 deg ; T3  -- T4   2.8875 A

T3  -- O10 -- T5  = 122.999 deg ; T3  -- T5   2.8677 A

T4  -- O11 -- T4  = 169.510 deg ; T4  -- T4   3.2203 A

T4  -- O12 -- T4  = 115.534 deg ; T4  -- T4   2.7253 A

T4  -- O13 -- T4  = 115.844 deg ; T4  -- T4   2.7223 A

T5  -- O14 -- T5  = 150.835 deg ; T5  -- T5   3.1673 A

T5  -- O15 -- T5  = 131.940 deg ; T5  -- T5   2.9834 A

T5  -- O16 -- T5  = 138.760 deg ; T5  -- T5   3.0382 A


        T-O-T SUMMARY
          Range  = 112.8310° <--> 178.8288 deg
          Mean   = 134.4621 deg
          StdDev = 20.2375 deg

        T--T SUMMARY
          Range  = 2.7223 A <--> 3.2539 A
          Mean   = 2.9539 A
          StdDev = 0.1731 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.8872 Angstrom
  T1  -- T1  = 2.9562 Angstrom
  T1  -- T2  = 3.2181 Angstrom
  T1  -- T4  = 3.4711 Angstrom
  T1  -- T1  = 3.2539 Angstrom
T3  -- T3  = 2.7448 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.4711 Angstrom
  T4  -- T3  = 2.8875 Angstrom
  T4  -- T4  = 2.7223 Angstrom
  T4  -- T4  = 2.7253 Angstrom
  T4  -- T4  = 3.2203 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 32 51 75 103 140 188 243 300 353 406 468 544 628
TD10 = 864
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 35 55 79 109 146 190 240 293 348 408 479 557 631
TD10 = 889
Circuit symbol = 4.6_{2}.4.8.6_{2}.8_{4}
Weight = 27
Vertex symbol  = 4.6_{2}.4.8.6.8_{2}
Weight = 27

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 36 55 82 117 154 190 233 290 353 414 476 546 627
TD10 = 903
Circuit symbol = 4.6.4.6.6_{2}.8_{3}
Weight = 16
Vertex symbol  = 4.6.4.6.6.8
Weight = 16

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 26 43 70 105 145 187 229 274 330 399 469 532 598
TD10 = 835
Circuit symbol = 4.4.4.6_{2}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.6_{2}.6.8
Weight = 20

T5 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 21 38 61 89 121 156 194 239 294 354 414 478 552 636
TD10 = 934
Circuit symbol = 4.4.6.8_{3}.6_{2}.8_{2}
Weight = 24
Vertex symbol  = 4.4.6.8.6_{2}.8
Weight = 24

<TD10> = 885.000
Average ring size = 5.4545