Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_20180274_bsinIf.cif"

There are 180 T-atoms per unit cell
There are 360 O-atoms per unit cell

Framework density = 21.17 T-atoms per nm^3
Material density = 2.112 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6119 Angstrom
T1  -- O2  = 1.6842 Angstrom
T1  -- O3  = 1.5461 Angstrom
T1  -- O4  = 1.6620 Angstrom
      mean = 1.6261 Angstrom
        t1 = 0.056068  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053230  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5115 Angstrom
T2  -- O5  = 1.5975 Angstrom
T2  -- O6  = 1.6378 Angstrom
T2  -- O7  = 1.5468 Angstrom
      mean = 1.5734 Angstrom
        t1 = 0.049996  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033776  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O9  = 1.5817 Angstrom
T3  -- O10 = 1.6250 Angstrom
T3  -- O4  = 1.6622 Angstrom
T3  -- O8  = 1.6984 Angstrom
T3  -- O10 = 1.7638 Angstrom
      mean = 1.6662 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.5429 Angstrom
T4  -- O11 = 1.6220 Angstrom
T4  -- O12 = 1.5994 Angstrom
T4  -- O13 = 1.6044 Angstrom
      mean = 1.5922 Angstrom
        t1 = 0.023871  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023965  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.4518 Angstrom
T5  -- O10 = 1.7180 Angstrom
T5  -- O14 = 1.6653 Angstrom
T5  -- O15 = 1.6753 Angstrom
      mean = 1.6276 Angstrom
        t1 = 0.109591  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.108434  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4518 A <--> 1.7638 A
          Mean   = 1.6194 A
          StdDev = 0.0721 A

       t1 Range  = 0.0239 <-- 0.0479 --> 0.1096
       t2 Range  = 0.0240 <-- 0.0439 --> 0.1084

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.268 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.515 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 110.188 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.920 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 119.746 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 100.487 deg; O3  -- O4  = 2 A
       100.487 deg <-- 109.187 deg --> 119.746 deg

O3  -- T2  -- O5  = 103.781 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 113.871 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 102.897 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 115.129 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.541 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.738 deg; O6  -- O7  = 3 A
       102.897 deg <-- 109.326 deg --> 115.129 deg

O9  -- T3  -- O10 =  91.347 deg; O9  -- O10 = 2 A
O9  -- T3  -- O4  =  75.028 deg; O9  -- O4  = 2 A
O9  -- T3  -- O8  = 102.092 deg; O9  -- O8  = 3 A
O9  -- T3  -- O10 = 132.006 deg; O9  -- O10 = 3 A
O10 -- T3  -- O4  = 131.339 deg; O10 -- O4  = 3 A
O10 -- T3  -- O8  = 122.170 deg; O10 -- O8  = 3 A
O10 -- T3  -- O10 =  97.125 deg; O10 -- O10 = 3 A
O4  -- T3  -- O8  = 106.413 deg; O4  -- O8  = 3 A
O4  -- T3  -- O10 =  64.081 deg; O4  -- O10 = 2 A
O8  -- T3  -- O10 = 112.383 deg; O8  -- O10 = 3 A
       64.081 deg <-- 103.398 deg --> 132.006 deg

O7  -- T4  -- O11 = 111.914 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 106.518 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 106.729 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 110.409 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 110.060 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 111.116 deg; O12 -- O13 = 3 A
       106.518 deg <-- 109.458 deg --> 111.914 deg

O9  -- T5  -- O10 =  92.347 deg; O9  -- O10 = 2 A
O9  -- T5  -- O14 =  93.679 deg; O9  -- O14 = 2 A
O9  -- T5  -- O15 = 104.273 deg; O9  -- O15 = 2 A
O10 -- T5  -- O14 = 125.073 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 116.745 deg; O10 -- O15 = 3 A
O14 -- T5  -- O15 = 114.330 deg; O14 -- O15 = 3 A
       92.347 deg <-- 107.741 deg --> 125.073 deg

        O-T-O SUMMARY
          Range  = 64.0810 deg <--> 132.0062 deg
          Mean   = 106.8420 deg
          StdDev = 13.8853 deg

        O--O SUMMARY
          Range  = 1.8196 A <--> 3.0572 A
          Mean   = 2.5889 A
          StdDev = 0.2754 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.827 deg ; T1  -- T1   3.1582 A

T1  -- O2  -- T1  = 175.815 deg ; T1  -- T1   3.3662 A

T1  -- O3  -- T2  = 131.777 deg ; T1  -- T2   2.7908 A

T1  -- O4  -- T3  = 126.270 deg ; T1  -- T3   2.9655 A

T2  -- O5  -- T2  = 169.252 deg ; T2  -- T2   3.1809 A

T2  -- O6  -- T2  = 127.501 deg ; T2  -- T2   2.9378 A

T2  -- O7  -- T4  = 116.500 deg ; T2  -- T4   2.6274 A

T3  -- O8  -- T3  = 140.071 deg ; T3  -- T3   3.1927 A

T3  -- O9  -- T5  =  87.185 deg ; T3  -- T5   2.0938 A

T3  -- O10 -- T3  =  82.799 deg ; T3  -- T3   2.2434 A
T3  -- O10 -- T5  =  77.503 deg ; T3  -- T5   2.0938 A
T3  -- O10 -- T5  = 151.164 deg ; T3  -- T5   3.3721 A

T4  -- O11 -- T4  = 176.323 deg ; T4  -- T4   3.2422 A

T4  -- O12 -- T4  = 105.879 deg ; T4  -- T4   2.5527 A

T4  -- O13 -- T4  = 109.544 deg ; T4  -- T4   2.6211 A

T5  -- O14 -- T5  = 136.746 deg ; T5  -- T5   3.0961 A

T5  -- O15 -- T5  = 136.448 deg ; T5  -- T5   3.1113 A


        T-O-T SUMMARY
          Range  = 77.5026° <--> 176.3234 deg
          Mean   = 129.8590 deg
          StdDev = 29.8911 deg

        T--T SUMMARY
          Range  = 2.0938 A <--> 3.3721 A
          Mean   = 2.8615 A
          StdDev = 0.4111 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O10 = 1.8196 A
O4  -- O9  = 1.9764 A
O9  -- O10 = 2.2942 A
O9  -- O14 = 2.2784 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.3662 Angstrom
  T1  -- T2  = 2.7908 Angstrom
  T1  -- T3  = 2.9655 Angstrom
  T1  -- T5  = 3.3433 Angstrom
  T1  -- T1  = 3.1582 Angstrom
T2  -- T1  = 2.7908 Angstrom
T2  -- T4  = 2.6274 Angstrom
T3  has 5 oxygen-bridged T-atoms within 3.50 A
  T3  -- T3  = 2.2434 Angstrom
  T3  -- T3  = 3.1927 Angstrom
  T3  -- T5  = 2.0938 Angstrom
  T3  -- T1  = 2.9655 Angstrom
  T3  -- T5  = 3.3721 Angstrom
T4  -- T2  = 2.6274 Angstrom
T4  -- T4  = 2.5527 Angstrom
T4  -- T4  = 2.6211 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T1  = 3.3433 Angstrom
  T5  -- T3  = 2.0938 Angstrom
  T5  -- T3  = 3.3721 Angstrom
  T5  -- T5  = 3.0961 Angstrom
  T5  -- T5  = 3.1113 Angstrom