Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_4_965964_5Ey04v.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 23.59 T-atoms per nm^3
Material density = 2.353 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6313 Angstrom
T1  -- O2  = 1.6431 Angstrom
T1  -- O3  = 1.5528 Angstrom
T1  -- O4  = 1.5878 Angstrom
      mean = 1.6037 Angstrom
        t1 = 0.046426  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029649  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5332 Angstrom
T2  -- O5  = 1.6509 Angstrom
T2  -- O6  = 1.6404 Angstrom
T2  -- O7  = 1.6852 Angstrom
      mean = 1.6274 Angstrom
        t1 = 0.028371  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034875  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6497 Angstrom
T3  -- O7  = 1.6769 Angstrom
T3  -- O8  = 1.4941 Angstrom
T3  -- O9  = 1.6533 Angstrom
      mean = 1.6185 Angstrom
        t1 = 0.064070  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.057513  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.5230 Angstrom
T4  -- O9  = 1.6740 Angstrom
T4  -- O10 = 1.6005 Angstrom
T4  -- O11 = 1.6215 Angstrom
      mean = 1.6048 Angstrom
        t1 = 0.022262  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025584  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4941 A <--> 1.6852 A
          Mean   = 1.6136 A
          StdDev = 0.0573 A

       t1 Range  = 0.0223 <-- 0.0403 --> 0.0641
       t2 Range  = 0.0256 <-- 0.0369 --> 0.0575

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.788 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.545 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.024 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.986 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 115.807 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.840 deg; O3  -- O4  = 2 A
       97.840 deg <-- 109.332 deg --> 115.807 deg

O3  -- T2  -- O5  = 111.247 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.559 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 111.096 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.706 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.174 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 107.842 deg; O6  -- O7  = 3 A
       105.559 deg <-- 109.437 deg --> 111.247 deg

O4  -- T3  -- O7  = 116.037 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  = 103.189 deg; O4  -- O8  = 2 A
O4  -- T3  -- O9  = 108.342 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 102.343 deg; O7  -- O8  = 2 A
O7  -- T3  -- O9  = 119.695 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 105.034 deg; O8  -- O9  = 2 A
       102.343 deg <-- 109.107 deg --> 119.695 deg

O8  -- T4  -- O9  = 112.465 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 = 108.293 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 108.172 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 = 108.579 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 108.539 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 = 110.809 deg; O10 -- O11 = 3 A
       108.172 deg <-- 109.476 deg --> 112.465 deg

        O-T-O SUMMARY
          Range  = 97.8397 deg <--> 119.6947 deg
          Mean   = 109.2427 deg
          StdDev = 4.6505 deg

        O--O SUMMARY
          Range  = 2.3674 A <--> 2.8796 A
          Mean   = 2.6288 A
          StdDev = 0.1171 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.2121 A
T1  - O1  - T1  - O3  - T2  =  91.121 deg; T1  -- T2  = 4.2674 A
T1  - O1  - T1  - O4  - T3  = 113.492 deg; T1  -- T3  = 5.0269 A
T1  - O2  - T1  - O3  - T2  =  91.121 deg; T1  -- T2  = 4.0642 A
T1  - O2  - T1  - O4  - T3  = 126.432 deg; T1  -- T3  = 5.1170 A
T2  - O3  - T1  - O4  - T3  =  85.052 deg; T2  -- T3  = 3.8421 A

T1  - O3  - T2  - O5  - T2  =  88.879 deg; T1  -- T2  = 4.2674 A
T1  - O3  - T2  - O6  - T2  =  88.879 deg; T1  -- T2  = 4.0642 A
T1  - O3  - T2  - O7  - T3  = 149.030 deg; T1  -- T3  = 5.8112 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.4034 A
T2  - O5  - T2  - O7  - T3  = 109.786 deg; T2  -- T3  = 5.2881 A
T2  - O6  - T2  - O7  - T3  = 101.729 deg; T2  -- T3  = 4.8016 A

T1  - O4  - T3  - O7  - T2  = 107.383 deg; T1  -- T2  = 4.8951 A
T1  - O4  - T3  - O8  - T4  = 108.445 deg; T1  -- T4  = 4.5858 A
T1  - O4  - T3  - O9  - T4  =  97.412 deg; T1  -- T4  = 4.5115 A
T2  - O7  - T3  - O8  - T4  = 100.186 deg; T2  -- T4  = 4.6082 A
T2  - O7  - T3  - O9  - T4  = 147.578 deg; T2  -- T4  = 6.0928 A
T4  - O8  - T3  - O9  - T4  =  91.138 deg; T4  -- T4  = 4.2401 A

T3  - O8  - T4  - O9  - T3  =  81.110 deg; T3  -- T3  = 3.8633 A
T3  - O8  - T4  - O10 - T4  = 116.427 deg; T3  -- T4  = 4.8752 A
T3  - O8  - T4  - O11 - T4  = 105.974 deg; T3  -- T4  = 4.4229 A
T3  - O9  - T4  - O10 - T4  = 121.992 deg; T3  -- T4  = 5.3203 A
T3  - O9  - T4  - O11 - T4  = 104.164 deg; T3  -- T4  = 4.6500 A
T4  - O10 - T4  - O11 - T4  = 120.000 deg; T4  -- T4  = 4.9314 A

        T-T-T SUMMARY
          Range  = 81.1098 deg <--> 149.0304 deg
          Mean   = 106.9924 deg
          StdDev = 17.8372 deg

        T--T SUMMARY
          Range  = 3.8421 A <--> 6.0928 A
          Mean   = 4.7284 A
          StdDev = 0.5823 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 149.324 deg ; T1  -- T1   3.1463 A

T1  -- O2  -- T1  = 121.704 deg ; T1  -- T1   2.8700 A

T1  -- O3  -- T2  = 132.256 deg ; T1  -- T2   2.8220 A

T1  -- O4  -- T3  = 124.251 deg ; T1  -- T3   2.8620 A

T2  -- O5  -- T2  = 161.061 deg ; T2  -- T2   3.2568 A

T2  -- O6  -- T2  = 130.568 deg ; T2  -- T2   2.9804 A

T2  -- O7  -- T3  = 145.078 deg ; T2  -- T3   3.2072 A

T3  -- O8  -- T4  = 135.268 deg ; T3  -- T4   2.7902 A

T3  -- O9  -- T4  = 141.145 deg ; T3  -- T4   3.1378 A

T4  -- O10 -- T4  = 133.810 deg ; T4  -- T4   2.9445 A

T4  -- O11 -- T4  = 115.898 deg ; T4  -- T4   2.7487 A


        T-O-T SUMMARY
          Range  = 115.8980° <--> 161.0605 deg
          Mean   = 135.4876 deg
          StdDev = 12.4727 deg

        T--T SUMMARY
          Range  = 2.7487 A <--> 3.2568 A
          Mean   = 2.9787 A
          StdDev = 0.1715 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T4  = 2.7902 Angstrom
T4  -- T3  = 2.7902 Angstrom
T4  -- T4  = 2.7487 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 34 53 78 109 143 176 211 254 307 365 423 482 544
TD10 = 839
Circuit symbol = 4.6.4.6_{2}.6.6_{2}
Weight = 20
Vertex symbol  = 4.6.4.6_{2}.6.6
Weight = 20

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 32 52 79 110 141 174 213 258 308 361 418 480 546
TD10 = 835
Circuit symbol = 4.6_{2}.4.6_{2}.6.6_{2}
Weight = 21
Vertex symbol  = 4.6_{2}.4.6_{2}.6.6
Weight = 21

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 35 54 80 107 136 173 217 263 306 359 419 482 547
TD10 = 839
Circuit symbol = 4.6_{2}.6.6.6.6_{2}
Weight = 20
Vertex symbol  = 4.6_{2}.6.6.6.6_{2}
Weight = 20

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 39 58 78 103 135 173 217 263 311 360 415 480 550
TD10 = 842
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

<TD10> = 838.750
Average ring size = 5.5135