Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_2_275_nGXPoe.cif"

There are 54 T-atoms per unit cell
There are 108 O-atoms per unit cell

Framework density = 20.83 T-atoms per nm^3
Material density = 2.078 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6192 Angstrom
T1  -- O2  = 1.6283 Angstrom
T1  -- O3  = 1.6157 Angstrom
T1  -- O4  = 1.6321 Angstrom
      mean = 1.6238 Angstrom
        t1 = 0.011288  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006685  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6156 Angstrom
T2  -- O4  = 1.6254 Angstrom
T2  -- O3  = 1.6156 Angstrom
T2  -- O4  = 1.6254 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.012960  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011876  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6156 A <--> 1.6321 A
          Mean   = 1.6227 A
          StdDev = 0.0063 A

       t1 Range  = 0.0113 <-- 0.0121 --> 0.0130
       t2 Range  = 0.0067 <-- 0.0093 --> 0.0119

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.189 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.864 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.933 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.145 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.514 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.149 deg; O3  -- O4  = 3 A
       108.149 deg <-- 109.466 deg --> 111.145 deg

O3  -- T2  -- O4  = 108.434 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 107.513 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 110.001 deg; O3  -- O4  = 3 A
O4  -- T2  -- O3  = 110.001 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 112.347 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  = 108.434 deg; O3  -- O4  = 3 A
       107.513 deg <-- 109.455 deg --> 112.347 deg

        O-T-O SUMMARY
          Range  = 107.5127 deg <--> 112.3475 deg
          Mean   = 109.4720 deg
          StdDev = 1.3579 deg

        O--O SUMMARY
          Range  = 2.6060 A <--> 2.7006 A
          Mean   = 2.6487 A
          StdDev = 0.0259 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 110.725 deg; T1  -- T2  = 4.8355 A
T1  - O1  - T1  - O3  - T2  = 111.522 deg; T1  -- T2  = 4.8888 A
T1  - O1  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 5.1427 A
T2  - O2  - T1  - O3  - T2  =  93.275 deg; T2  -- T2  = 4.3675 A
T2  - O2  - T1  - O4  - T1  = 109.142 deg; T2  -- T1  = 4.9151 A
T2  - O3  - T1  - O4  - T1  = 108.904 deg; T2  -- T1  = 4.9372 A

T1  - O3  - T2  - O4  - T1  =  74.360 deg; T1  -- T1  = 3.6304 A
T1  - O3  - T2  - O3  - T1  = 140.339 deg; T1  -- T1  = 5.6510 A
T1  - O3  - T2  - O4  - T1  =  94.032 deg; T1  -- T1  = 4.3681 A
T1  - O4  - T2  - O3  - T1  = 136.957 deg; T1  -- T1  = 5.6221 A
T1  - O4  - T2  - O4  - T1  = 140.339 deg; T1  -- T1  = 5.6510 A
T1  - O3  - T2  - O4  - T1  =  74.360 deg; T1  -- T1  = 3.6304 A

        T-T-T SUMMARY
          Range  = 74.3599 deg <--> 140.3385 deg
          Mean   = 109.4426 deg
          StdDev = 22.3753 deg

        T--T SUMMARY
          Range  = 3.6304 A <--> 5.6510 A
          Mean   = 4.8019 A
          StdDev = 0.6856 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 126.471 deg ; T1  -- T1   2.8913 A

T1  -- O2  -- T1  = 138.600 deg ; T1  -- T1   3.0464 A

T1  -- O3  -- T2  = 135.015 deg ; T1  -- T2   2.9855 A

T1  -- O4  -- T2  = 136.134 deg ; T1  -- T2   3.0217 A


        T-O-T SUMMARY
          Range  = 126.4707° <--> 138.6001 deg
          Mean   = 134.0551 deg
          StdDev = 4.5828 deg

        T--T SUMMARY
          Range  = 2.8913 A <--> 3.0464 A
          Mean   = 2.9862 A
          StdDev = 0.0591 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 36 56 81 107 138 177 221 262 308 367 431 486 546
TD10 = 853
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

T2 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 21 36 55 78 108 144 176 210 263 324 365 408 488 576
TD10 = 843
Circuit symbol = 4.4.6.6.6.6_{2}
Weight = 18
Vertex symbol  = 4.4.6.6.6.6_{2}
Weight = 18

<TD10> = 849.667
Average ring size = 5.6129