Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166-2_2_35058_gAD75q.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 27.34 T-atoms per nm^3
Material density = 2.728 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6241 Angstrom
T1  -- O3  = 1.5900 Angstrom
T1  -- O1  = 1.6627 Angstrom
T1  -- O4  = 1.6236 Angstrom
      mean = 1.6251 Angstrom
        t1 = 0.031373  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020652  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6149 Angstrom
T2  -- O3  = 1.6149 Angstrom
T2  -- O4  = 1.6203 Angstrom
T2  -- O4  = 1.6203 Angstrom
      mean = 1.6176 Angstrom
        t1 = 0.031264  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033294  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5900 A <--> 1.6627 A
          Mean   = 1.6226 A
          StdDev = 0.0215 A

       t1 Range  = 0.0313 <-- 0.0313 --> 0.0314
       t2 Range  = 0.0207 <-- 0.0270 --> 0.0333

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 107.471 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.596 deg; O2  -- O1  = 3 A
O2  -- T1  -- O4  = 108.335 deg; O2  -- O4  = 3 A
O3  -- T1  -- O1  = 117.381 deg; O3  -- O1  = 3 A
O3  -- T1  -- O4  = 103.801 deg; O3  -- O4  = 3 A
O1  -- T1  -- O4  = 109.833 deg; O1  -- O4  = 3 A
       103.801 deg <-- 109.403 deg --> 117.381 deg

O3  -- T2  -- O3  = 105.129 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 116.617 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 105.533 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 105.533 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 116.617 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 107.857 deg; O4  -- O4  = 3 A
       105.129 deg <-- 109.548 deg --> 116.617 deg

        O-T-O SUMMARY
          Range  = 103.8010 deg <--> 117.3806 deg
          Mean   = 109.4699 deg
          StdDev = 4.7237 deg

        O--O SUMMARY
          Range  = 2.5291 A <--> 2.7793 A
          Mean   = 2.6440 A
          StdDev = 0.0822 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T2  = 102.003 deg; T1  -- T2  = 4.5312 A
T1  - O2  - T1  - O1  - T2  = 101.570 deg; T1  -- T2  = 4.6053 A
T1  - O2  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 5.0771 A
T2  - O3  - T1  - O1  - T2  =  73.976 deg; T2  -- T2  = 3.6814 A
T2  - O3  - T1  - O4  - T1  = 137.804 deg; T2  -- T1  = 5.6341 A
T2  - O1  - T1  - O4  - T1  =  99.601 deg; T2  -- T1  = 4.6974 A

T1  - O3  - T2  - O3  - T1  = 101.106 deg; T1  -- T1  = 4.7242 A
T1  - O3  - T2  - O4  - T1  = 110.590 deg; T1  -- T1  = 5.0292 A
T1  - O3  - T2  - O4  - T1  =  84.393 deg; T1  -- T1  = 4.0343 A
T1  - O3  - T2  - O4  - T1  = 136.895 deg; T1  -- T1  = 5.7924 A
T1  - O3  - T2  - O4  - T1  = 110.590 deg; T1  -- T1  = 5.0292 A
T1  - O4  - T2  - O4  - T1  = 101.106 deg; T1  -- T1  = 4.7242 A

        T-T-T SUMMARY
          Range  = 73.9762 deg <--> 137.8036 deg
          Mean   = 106.8564 deg
          StdDev = 18.2506 deg

        T--T SUMMARY
          Range  = 3.6814 A <--> 5.7924 A
          Mean   = 4.8050 A
          StdDev = 0.5779 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.824 deg ; T1  -- T1   3.0358 A

T1  -- O2  -- T1  = 120.880 deg ; T1  -- T1   2.8255 A

T1  -- O3  -- T2  = 139.124 deg ; T1  -- T2   3.0032 A

T1  -- O4  -- T2  = 147.447 deg ; T1  -- T2   3.1139 A


        T-O-T SUMMARY
          Range  = 120.8795° <--> 147.4470 deg
          Mean   = 134.8186 deg
          StdDev = 9.8665 deg

        T--T SUMMARY
          Range  = 2.8255 A <--> 3.1139 A
          Mean   = 2.9946 A
          StdDev = 0.1067 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 21 36 56 81 107 138 177 221 262 308 367 431 486 546
TD10 = 853
Circuit symbol = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23
Vertex symbol  = 4.6.6.6_{3}.6_{2}.6_{3}
Weight = 23

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 36 55 78 108 144 176 210 263 324 365 408 488 576
TD10 = 843
Circuit symbol = 4.4.6.6.6.6_{2}
Weight = 18
Vertex symbol  = 4.4.6.6.6.6_{2}
Weight = 18

<TD10> = 849.667
Average ring size = 5.6129