Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166-2_2_30169_ugtlgQ.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 18.24 T-atoms per nm^3
Material density = 1.820 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5961 Angstrom
T1  -- O3  = 1.6152 Angstrom
T1  -- O4  = 1.6394 Angstrom
T1  -- O2  = 1.6575 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.025966  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022332  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O6  = 1.6312 Angstrom
T2  -- O7  = 1.5385 Angstrom
T2  -- O4  = 1.6181 Angstrom
T2  -- O5  = 1.7071 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.057659  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039531  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5385 A <--> 1.7071 A
          Mean   = 1.6254 A
          StdDev = 0.0457 A

       t1 Range  = 0.0260 <-- 0.0418 --> 0.0577
       t2 Range  = 0.0223 <-- 0.0309 --> 0.0395

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 106.415 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.119 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.328 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.471 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 112.725 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 112.399 deg; O4  -- O2  = 3 A
       106.119 deg <-- 109.409 deg --> 112.725 deg

O6  -- T2  -- O7  = 108.458 deg; O6  -- O7  = 3 A
O6  -- T2  -- O4  = 112.981 deg; O6  -- O4  = 3 A
O6  -- T2  -- O5  = 114.029 deg; O6  -- O5  = 3 A
O7  -- T2  -- O4  =  99.328 deg; O7  -- O4  = 2 A
O7  -- T2  -- O5  = 121.311 deg; O7  -- O5  = 3 A
O4  -- T2  -- O5  =  99.312 deg; O4  -- O5  = 3 A
       99.312 deg <-- 109.237 deg --> 121.311 deg

        O-T-O SUMMARY
          Range  = 99.3120 deg <--> 121.3109 deg
          Mean   = 108.4159 deg
          StdDev = 5.9828 deg

        O--O SUMMARY
          Range  = 2.4067 A <--> 2.8304 A
          Mean   = 2.6346 A
          StdDev = 0.1172 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 134.856 deg; T1  -- T2  = 5.5266 A
T1  - O1  - T1  - O4  - T1  =  90.425 deg; T1  -- T1  = 4.4404 A
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.4877 A
T2  - O3  - T1  - O4  - T1  = 130.878 deg; T2  -- T1  = 5.4126 A
T2  - O3  - T1  - O2  - T1  =  82.790 deg; T2  -- T1  = 3.9960 A
T1  - O4  - T1  - O2  - T1  =  89.575 deg; T1  -- T1  = 4.4404 A

T2  - O6  - T2  - O7  - T2  = 120.000 deg; T2  -- T2  = 4.8598 A
T2  - O6  - T2  - O4  - T1  = 125.437 deg; T2  -- T1  = 5.2978 A
T2  - O6  - T2  - O5  - T2  = 126.161 deg; T2  -- T2  = 5.8279 A
T2  - O7  - T2  - O4  - T1  =  97.210 deg; T2  -- T1  = 3.9960 A
T2  - O7  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2190 A
T1  - O4  - T2  - O5  - T2  =  88.655 deg; T1  -- T2  = 4.3883 A

        T-T-T SUMMARY
          Range  = 82.7897 deg <--> 134.8555 deg
          Mean   = 106.5648 deg
          StdDev = 18.6373 deg

        T--T SUMMARY
          Range  = 3.9960 A <--> 5.8279 A
          Mean   = 4.7705 A
          StdDev = 0.6002 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 154.143 deg ; T1  -- T1   3.1112 A

T1  -- O2  -- T1  = 148.619 deg ; T1  -- T1   3.1914 A

T1  -- O3  -- T1  = 153.628 deg ; T1  -- T1   3.1452 A

T1  -- O4  -- T2  = 121.239 deg ; T1  -- T2   2.8385 A

T2  -- O5  -- T2  = 178.494 deg ; T2  -- T2   3.4140 A

T2  -- O6  -- T2  = 146.072 deg ; T2  -- T2   3.1205 A

T2  -- O7  -- T2  = 107.341 deg ; T2  -- T2   2.4789 A


        T-O-T SUMMARY
          Range  = 107.3406° <--> 178.4938 deg
          Mean   = 144.2194 deg
          StdDev = 21.7522 deg

        T--T SUMMARY
          Range  = 2.4789 A <--> 3.4140 A
          Mean   = 3.0428 A
          StdDev = 0.2796 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.4789 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 9 17 30 50 75 100 126 157 194 234 275 323 381 444 505
TD10 = 763
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 71 95 124 158 197 239 282 329 380 435 495
TD10 = 763
Circuit symbol = 4.6.4.8_{2}.6.6_{2}
Weight = 21
Vertex symbol  = 4.6.4.8.6.6
Weight = 21

<TD10> = 763.000
Average ring size = 5.1429