Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166-2_2_27486_CCBTNo.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.19 T-atoms per nm^3
Material density = 1.915 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6729 Angstrom
T1  -- O2  = 1.6965 Angstrom
T1  -- O3  = 1.5884 Angstrom
T1  -- O4  = 1.6714 Angstrom
      mean = 1.6573 Angstrom
        t1 = 0.055327  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033269  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5967 Angstrom
T2  -- O4  = 1.5921 Angstrom
T2  -- O5  = 1.5113 Angstrom
T2  -- O6  = 1.5705 Angstrom
      mean = 1.5676 Angstrom
        t1 = 0.068123  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043329  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5113 A <--> 1.6965 A
          Mean   = 1.6125 A
          StdDev = 0.0589 A

       t1 Range  = 0.0553 <-- 0.0617 --> 0.0681
       t2 Range  = 0.0333 <-- 0.0383 --> 0.0433

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 112.065 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.833 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.342 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.204 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 117.802 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  99.428 deg; O3  -- O4  = 2 A
       99.428 deg <-- 109.279 deg --> 117.802 deg

O3  -- T2  -- O4  = 116.595 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 114.787 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.740 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 100.520 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 116.492 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  =  95.368 deg; O5  -- O6  = 2 A
       95.368 deg <-- 109.084 deg --> 116.595 deg

        O-T-O SUMMARY
          Range  = 95.3682 deg <--> 117.8015 deg
          Mean   = 109.6780 deg
          StdDev = 6.6839 deg

        O--O SUMMARY
          Range  = 2.2791 A <--> 2.8839 A
          Mean   = 2.6332 A
          StdDev = 0.1496 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 113.633 deg; T1  -- T1  = 5.4914 A
T1  - O1  - T1  - O3  - T2  =  93.474 deg; T1  -- T2  = 4.6607 A
T1  - O1  - T1  - O4  - T2  = 117.690 deg; T1  -- T2  = 5.5705 A
T1  - O2  - T1  - O3  - T2  =  87.572 deg; T1  -- T2  = 4.4129 A
T1  - O2  - T1  - O4  - T2  = 122.030 deg; T1  -- T2  = 5.6742 A
T2  - O3  - T1  - O4  - T2  = 113.662 deg; T2  -- T2  = 5.2929 A

T1  - O3  - T2  - O4  - T2  =  92.428 deg; T1  -- T2  = 4.4129 A
T1  - O3  - T2  - O5  - T2  = 103.399 deg; T1  -- T2  = 4.5496 A
T1  - O3  - T2  - O6  - T1  = 119.602 deg; T1  -- T1  = 5.4650 A
T2  - O4  - T2  - O5  - T2  = 133.254 deg; T2  -- T2  = 5.2231 A
T2  - O4  - T2  - O6  - T1  = 116.814 deg; T2  -- T1  = 5.3022 A
T2  - O5  - T2  - O6  - T1  =  93.048 deg; T2  -- T1  = 4.2967 A

        T-T-T SUMMARY
          Range  = 87.5716 deg <--> 133.2538 deg
          Mean   = 109.3878 deg
          StdDev = 14.1030 deg

        T--T SUMMARY
          Range  = 4.2967 A <--> 5.6742 A
          Mean   = 5.0416 A
          StdDev = 0.4861 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 159.418 deg ; T1  -- T1   3.2920 A

T1  -- O2  -- T1  = 148.985 deg ; T1  -- T1   3.2694 A

T1  -- O3  -- T2  = 154.349 deg ; T1  -- T2   3.1057 A

T1  -- O4  -- T2  = 160.651 deg ; T1  -- T2   3.2172 A

T2  -- O5  -- T2  = 125.089 deg ; T2  -- T2   2.6821 A

T2  -- O6  -- T2  = 146.319 deg ; T2  -- T2   3.0062 A


        T-O-T SUMMARY
          Range  = 125.0894° <--> 160.6507 deg
          Mean   = 149.1352 deg
          StdDev = 11.9978 deg

        T--T SUMMARY
          Range  = 2.6821 A <--> 3.2920 A
          Mean   = 3.0954 A
          StdDev = 0.2107 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O5  -- O6  = 2.2791 A
O5  -- O6  = 2.2791 A
T2  -- T2  = 2.6821 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 22 37 59 85 114 147 184 230 280 331 386 445 515 589
TD10 = 894
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{3}
Weight = 23

<TD10> = 894.000
Average ring size = 5.7143