Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166-2_1_21_sAgp8O.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 23.01 T-atoms per nm^3
Material density = 2.296 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6911 Angstrom
T1  -- O3  = 1.6751 Angstrom
T1  -- O1  = 2.0215 Angstrom
T1  -- O1  = 1.8047 Angstrom
T1  -- O2  = 1.5010 Angstrom
      mean = 1.7387 Angstrom

        T-O SUMMARY
          Range  = 1.5010 A <--> 2.0215 A
          Mean   = 1.7387 A
          StdDev = 0.1730 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 116.477 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  94.695 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  = 126.532 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  74.119 deg; O1  -- O2  = 2 A
O3  -- T1  -- O1  =  86.453 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 116.098 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  =  94.019 deg; O3  -- O2  = 2 A
O1  -- T1  -- O1  =  79.444 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 167.749 deg; O1  -- O2  = 4 A
O1  -- T1  -- O2  = 111.083 deg; O1  -- O2  = 3 A
       74.119 deg <-- 106.667 deg --> 167.749 deg

        O-T-O SUMMARY
          Range  = 74.1185 deg <--> 167.7485 deg
          Mean   = 107.3325 deg
          StdDev = 26.7902 deg

        O--O SUMMARY
          Range  = 1.9297 A <--> 3.5028 A
          Mean   = 2.7368 A
          StdDev = 0.4189 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 132.325 deg ; T1  -- T1   3.1979 A
T1  -- O1  -- T1  =  79.191 deg ; T1  -- T1   2.3799 A
T1  -- O1  -- T1  =  90.256 deg ; T1  -- T1   2.7159 A

T1  -- O2  -- T1  = 153.657 deg ; T1  -- T1   2.9229 A

T1  -- O3  -- T1  = 134.473 deg ; T1  -- T1   3.0892 A


        T-O-T SUMMARY
          Range  = 79.1907° <--> 153.6571 deg
          Mean   = 117.9802 deg
          StdDev = 28.6080 deg

        T--T SUMMARY
          Range  = 2.3799 A <--> 3.1979 A
          Mean   = 2.8612 A
          StdDev = 0.2929 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.9297 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.0616 Angstrom
  T1  -- T1  = 3.0892 Angstrom
  T1  -- T1  = 2.7159 Angstrom
  T1  -- T1  = 3.1979 Angstrom
  T1  -- T1  = 2.3799 Angstrom
  T1  -- T1  = 3.1979 Angstrom
  T1  -- T1  = 2.9229 Angstrom