Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166-2_1_13_p0D2K2.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 26.47 T-atoms per nm^3
Material density = 2.641 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9927 Angstrom
T1  -- O1  = 1.7334 Angstrom
T1  -- O2  = 1.6309 Angstrom
T1  -- O1  = 1.7511 Angstrom
T1  -- O3  = 1.7067 Angstrom
      mean = 1.7630 Angstrom

        T-O SUMMARY
          Range  = 1.6309 A <--> 1.9927 A
          Mean   = 1.7630 A
          StdDev = 0.1230 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  82.305 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  72.862 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  =  78.544 deg; O1  -- O1  = 2 A
O1  -- T1  -- O3  = 157.264 deg; O1  -- O3  = 4 A
O1  -- T1  -- O2  =  62.364 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 141.229 deg; O1  -- O1  = 3 A
O1  -- T1  -- O3  = 108.983 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  =  79.808 deg; O2  -- O1  = 2 A
O2  -- T1  -- O3  = 129.762 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 101.364 deg; O1  -- O3  = 3 A
       62.364 deg <-- 101.448 deg --> 157.264 deg

        O-T-O SUMMARY
          Range  = 62.3637 deg <--> 157.2642 deg
          Mean   = 99.9582 deg
          StdDev = 30.6368 deg

        O--O SUMMARY
          Range  = 1.7441 A <--> 3.6273 A
          Mean   = 2.6132 A
          StdDev = 0.5482 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  44.104 deg ; T1  -- T1   1.4195 A
T1  -- O1  -- T1  =  82.578 deg ; T1  -- T1   2.4770 A
T1  -- O1  -- T1  = 126.667 deg ; T1  -- T1   3.1139 A

T1  -- O2  -- T1  =  98.824 deg ; T1  -- T1   2.4770 A

T1  -- O3  -- T1  = 116.307 deg ; T1  -- T1   2.8996 A


        T-O-T SUMMARY
          Range  = 44.1040° <--> 126.6665 deg
          Mean   = 93.6960 deg
          StdDev = 29.2537 deg

        T--T SUMMARY
          Range  = 1.4195 A <--> 3.1139 A
          Mean   = 2.4774 A
          StdDev = 0.5885 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.1715 A
O1  -- O2  = 1.7441 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 1.4195 Angstrom
  T1  -- T1  = 3.1139 Angstrom
  T1  -- T1  = 2.4770 Angstrom
  T1  -- T1  = 3.2284 Angstrom
  T1  -- T1  = 2.8996 Angstrom
  T1  -- T1  = 3.1139 Angstrom