Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_165_2_21334_LrbP0V.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 21.53 T-atoms per nm^3
Material density = 2.148 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6222 Angstrom
T1  -- O1  = 1.6256 Angstrom
T1  -- O2  = 1.6131 Angstrom
T1  -- O3  = 1.6159 Angstrom
      mean = 1.6192 Angstrom
        t1 = 0.006545  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003708  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6147 Angstrom
T2  -- O4  = 1.6228 Angstrom
T2  -- O3  = 1.6168 Angstrom
T2  -- O4  = 1.6270 Angstrom
      mean = 1.6203 Angstrom
        t1 = 0.007186  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003612  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6131 A <--> 1.6270 A
          Mean   = 1.6198 A
          StdDev = 0.0050 A

       t1 Range  = 0.0065 <-- 0.0069 --> 0.0072
       t2 Range  = 0.0036 <-- 0.0037 --> 0.0037

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.642 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 110.416 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.175 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.009 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.013 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.554 deg; O2  -- O3  = 3 A
       108.642 deg <-- 109.468 deg --> 110.416 deg

O2  -- T2  -- O4  = 110.021 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 109.168 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.478 deg; O2  -- O4  = 3 A
O4  -- T2  -- O3  = 108.853 deg; O4  -- O3  = 3 A
O4  -- T2  -- O4  = 109.479 deg; O4  -- O4  = 3 A
O3  -- T2  -- O4  = 109.827 deg; O3  -- O4  = 3 A
       108.853 deg <-- 109.471 deg --> 110.021 deg

        O-T-O SUMMARY
          Range  = 108.6417 deg <--> 110.4161 deg
          Mean   = 109.4697 deg
          StdDev = 0.5349 deg

        O--O SUMMARY
          Range  = 2.6335 A <--> 2.6569 A
          Mean   = 2.6450 A
          StdDev = 0.0087 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9595 A
T1  - O1  - T1  - O2  - T2  = 126.435 deg; T1  -- T2  = 5.4373 A
T1  - O1  - T1  - O3  - T2  = 126.451 deg; T1  -- T2  = 5.4415 A
T1  - O1  - T1  - O2  - T2  = 111.374 deg; T1  -- T2  = 5.0312 A
T1  - O1  - T1  - O3  - T2  = 111.208 deg; T1  -- T2  = 5.0297 A
T2  - O2  - T1  - O3  - T2  = 106.417 deg; T2  -- T2  = 5.0174 A

T1  - O2  - T2  - O4  - T2  = 113.119 deg; T1  -- T2  = 5.1357 A
T1  - O2  - T2  - O3  - T1  = 107.928 deg; T1  -- T1  = 5.0664 A
T1  - O2  - T2  - O4  - T2  = 101.696 deg; T1  -- T2  = 4.7729 A
T2  - O4  - T2  - O3  - T1  = 101.019 deg; T2  -- T1  = 4.7531 A
T2  - O4  - T2  - O4  - T2  = 119.998 deg; T2  -- T2  = 5.2370 A
T1  - O3  - T2  - O4  - T2  = 112.959 deg; T1  -- T2  = 5.1345 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 126.4514 deg
          Mean   = 108.2170 deg
          StdDev = 16.6186 deg

        T--T SUMMARY
          Range  = 2.9595 A <--> 5.4415 A
          Mean   = 4.9180 A
          StdDev = 0.6267 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.358 deg ; T1  -- T1   2.9595 A

T1  -- O2  -- T2  = 151.795 deg ; T1  -- T2   3.1305 A

T1  -- O3  -- T2  = 151.729 deg ; T1  -- T2   3.1348 A

T2  -- O4  -- T2  = 136.995 deg ; T2  -- T2   3.0236 A


        T-O-T SUMMARY
          Range  = 131.3582° <--> 151.7955 deg
          Mean   = 142.9694 deg
          StdDev = 9.1112 deg

        T--T SUMMARY
          Range  = 2.9595 A <--> 3.1348 A
          Mean   = 3.0621 A
          StdDev = 0.0749 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 44 64 100 122 164 214 264 322 362 432 512 600 672
TD10 = 1011
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 1011.000
Average ring size = 5.6000