Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_165_2_13094_PBvz8d.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 25.29 T-atoms per nm^3
Material density = 2.523 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6333 Angstrom
T1  -- O1  = 1.6333 Angstrom
T1  -- O2  = 1.6113 Angstrom
T1  -- O3  = 1.6346 Angstrom
      mean = 1.6281 Angstrom
        t1 = 0.019921  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012070  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6117 Angstrom
T2  -- O3  = 1.6664 Angstrom
T2  -- O4  = 1.6313 Angstrom
T2  -- O5  = 1.6294 Angstrom
      mean = 1.6347 Angstrom
        t1 = 0.035714  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026391  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6113 A <--> 1.6664 A
          Mean   = 1.6314 A
          StdDev = 0.0160 A

       t1 Range  = 0.0199 <-- 0.0278 --> 0.0357
       t2 Range  = 0.0121 <-- 0.0192 --> 0.0264

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 107.705 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.438 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.395 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.303 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.784 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 107.072 deg; O2  -- O3  = 3 A
       107.072 deg <-- 109.449 deg --> 112.784 deg

O2  -- T2  -- O3  = 105.542 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 106.344 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 106.277 deg; O2  -- O5  = 3 A
O3  -- T2  -- O4  = 115.628 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 115.255 deg; O3  -- O5  = 3 A
O4  -- T2  -- O5  = 107.043 deg; O4  -- O5  = 3 A
       105.542 deg <-- 109.348 deg --> 115.628 deg

        O-T-O SUMMARY
          Range  = 105.5422 deg <--> 115.6278 deg
          Mean   = 109.5013 deg
          StdDev = 3.5087 deg

        O--O SUMMARY
          Range  = 2.5932 A <--> 2.7910 A
          Mean   = 2.6637 A
          StdDev = 0.0698 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.8295 A
T1  - O1  - T1  - O2  - T2  = 121.533 deg; T1  -- T2  = 4.8998 A
T1  - O1  - T1  - O3  - T2  = 120.474 deg; T1  -- T2  = 4.9518 A
T1  - O1  - T1  - O2  - T2  = 121.884 deg; T1  -- T2  = 4.9082 A
T1  - O1  - T1  - O3  - T2  = 120.754 deg; T1  -- T2  = 4.9587 A
T2  - O2  - T1  - O3  - T2  = 106.614 deg; T2  -- T2  = 4.5388 A

T1  - O2  - T2  - O3  - T2  =  88.808 deg; T1  -- T2  = 4.2455 A
T1  - O2  - T2  - O4  - T2  =  89.040 deg; T1  -- T2  = 4.2512 A
T1  - O2  - T2  - O5  - T1  = 106.614 deg; T1  -- T1  = 4.5388 A
T2  - O3  - T2  - O4  - T2  = 106.651 deg; T2  -- T2  = 5.2303 A
T2  - O3  - T2  - O5  - T1  = 125.363 deg; T2  -- T1  = 5.4557 A
T2  - O4  - T2  - O5  - T1  = 125.176 deg; T2  -- T1  = 5.4476 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 125.3626 deg
          Mean   = 106.9847 deg
          StdDev = 19.1087 deg

        T--T SUMMARY
          Range  = 2.8295 A <--> 5.4557 A
          Mean   = 4.6550 A
          StdDev = 0.6801 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.039 deg ; T1  -- T1   2.8295 A

T1  -- O2  -- T2  = 119.582 deg ; T1  -- T2   2.7853 A

T1  -- O3  -- T2  = 121.114 deg ; T1  -- T2   2.8747 A

T2  -- O4  -- T2  = 179.637 deg ; T2  -- T2   3.2626 A

T2  -- O5  -- T2  = 178.702 deg ; T2  -- T2   3.2587 A


        T-O-T SUMMARY
          Range  = 119.5819° <--> 179.6372 deg
          Mean   = 143.8147 deg
          StdDev = 29.1165 deg

        T--T SUMMARY
          Range  = 2.7853 A <--> 3.2626 A
          Mean   = 3.0022 A
          StdDev = 0.2147 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.7853 Angstrom
T2  -- T1  = 2.7853 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 44 64 100 122 164 214 264 322 362 432 512 600 672
TD10 = 1011
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 1011.000
Average ring size = 5.6000