Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_164_3_303372_dO3mOB.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 18.64 T-atoms per nm^3
Material density = 1.860 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O3  = 1.6205 Angstrom
T1  -- O1  = 1.6245 Angstrom
T1  -- O1  = 1.6244 Angstrom
T1  -- O2  = 1.6205 Angstrom
      mean = 1.6224 Angstrom
        t1 = 0.008823  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002768  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6167 Angstrom
T2  -- O4  = 1.6104 Angstrom
T2  -- O5  = 1.6176 Angstrom
T2  -- O5  = 1.6177 Angstrom
      mean = 1.6156 Angstrom
        t1 = 0.004008  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001976  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6191 Angstrom
T3  -- O4  = 1.6103 Angstrom
T3  -- O5  = 1.6178 Angstrom
T3  -- O5  = 1.6177 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.004065  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000817  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6103 A <--> 1.6245 A
          Mean   = 1.6181 A
          StdDev = 0.0043 A

       t1 Range  = 0.0040 <-- 0.0056 --> 0.0088
       t2 Range  = 0.0008 <-- 0.0019 --> 0.0028

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O3  -- T1  -- O1  = 109.360 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 109.365 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 111.064 deg; O3  -- O2  = 3 A
O1  -- T1  -- O1  = 108.279 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.359 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.364 deg; O1  -- O2  = 3 A
       108.279 deg <-- 109.465 deg --> 111.064 deg

O2  -- T2  -- O4  = 109.725 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 108.928 deg; O2  -- O5  = 3 A
O2  -- T2  -- O5  = 108.923 deg; O2  -- O5  = 3 A
O4  -- T2  -- O5  = 110.043 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 110.038 deg; O4  -- O5  = 3 A
O5  -- T2  -- O5  = 109.157 deg; O5  -- O5  = 3 A
       108.923 deg <-- 109.469 deg --> 110.043 deg

O3  -- T3  -- O4  = 109.500 deg; O3  -- O4  = 3 A
O3  -- T3  -- O5  = 109.270 deg; O3  -- O5  = 3 A
O3  -- T3  -- O5  = 109.275 deg; O3  -- O5  = 3 A
O4  -- T3  -- O5  = 109.915 deg; O4  -- O5  = 3 A
O4  -- T3  -- O5  = 109.920 deg; O4  -- O5  = 3 A
O5  -- T3  -- O5  = 108.943 deg; O5  -- O5  = 3 A
       108.943 deg <-- 109.470 deg --> 109.920 deg

        O-T-O SUMMARY
          Range  = 108.2786 deg <--> 111.0640 deg
          Mean   = 109.4586 deg
          StdDev = 0.5450 deg

        O--O SUMMARY
          Range  = 2.6319 A <--> 2.6720 A
          Mean   = 2.6410 A
          StdDev = 0.0080 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O3  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9647 A
T1  - O3  - T1  - O1  - T3  = 131.750 deg; T1  -- T3  = 5.5476 A
T1  - O3  - T1  - O2  - T2  = 131.777 deg; T1  -- T2  = 5.5523 A
T1  - O1  - T1  - O1  - T3  = 131.752 deg; T1  -- T3  = 5.5477 A
T1  - O1  - T1  - O2  - T2  = 131.779 deg; T1  -- T2  = 5.5524 A
T3  - O1  - T1  - O2  - T2  =  79.452 deg; T3  -- T2  = 3.9826 A

T3  - O2  - T2  - O4  - T3  =  90.066 deg; T3  -- T3  = 4.4522 A
T3  - O2  - T2  - O5  - T3  =  90.066 deg; T3  -- T3  = 4.4524 A
T3  - O2  - T2  - O5  - T1  = 129.622 deg; T3  -- T1  = 5.7279 A
T3  - O4  - T2  - O5  - T3  = 120.153 deg; T3  -- T3  = 5.3385 A
T3  - O4  - T2  - O5  - T1  = 112.551 deg; T3  -- T1  = 5.1548 A
T3  - O5  - T2  - O5  - T1  = 112.551 deg; T3  -- T1  = 5.1549 A

T1  - O3  - T3  - O4  - T2  = 129.829 deg; T1  -- T2  = 5.7287 A
T1  - O3  - T3  - O5  - T2  = 112.682 deg; T1  -- T2  = 5.1549 A
T1  - O3  - T3  - O5  - T2  = 112.682 deg; T1  -- T2  = 5.1551 A
T2  - O4  - T3  - O5  - T2  =  89.933 deg; T2  -- T2  = 4.4471 A
T2  - O4  - T3  - O5  - T2  =  89.933 deg; T2  -- T2  = 4.4472 A
T2  - O5  - T3  - O5  - T2  = 119.847 deg; T2  -- T2  = 5.3303 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 131.7795 deg
          Mean   = 109.5159 deg
          StdDev = 18.7089 deg

        T--T SUMMARY
          Range  = 2.9647 A <--> 5.7287 A
          Mean   = 5.0019 A
          StdDev = 0.6212 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.720 deg ; T1  -- T1   2.9647 A

T1  -- O2  -- T2  = 148.805 deg ; T1  -- T2   3.1180 A

T1  -- O3  -- T3  = 147.919 deg ; T1  -- T3   3.1135 A

T2  -- O4  -- T3  = 171.437 deg ; T2  -- T3   3.2117 A

T2  -- O5  -- T3  = 144.321 deg ; T2  -- T3   3.0799 A


        T-O-T SUMMARY
          Range  = 131.7201° <--> 171.4374 deg
          Mean   = 148.8406 deg
          StdDev = 13.0648 deg

        T--T SUMMARY
          Range  = 2.9647 A <--> 3.2117 A
          Mean   = 3.0976 A
          StdDev = 0.0809 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T3 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

<TD10> = 907.000
Average ring size = 6.2143