Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_164_3_296442_sAMM8f.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 24.40 T-atoms per nm^3
Material density = 2.434 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6168 Angstrom
T1  -- O3  = 1.6124 Angstrom
T1  -- O4  = 1.6505 Angstrom
T1  -- O2  = 1.6282 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.015987  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007574  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6197 Angstrom
T2  -- O4  = 1.6196 Angstrom
T2  -- O5  = 1.6130 Angstrom
T2  -- O6  = 1.6203 Angstrom
      mean = 1.6181 Angstrom
        t1 = 0.028634  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019259  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6389 Angstrom
T3  -- O7  = 1.6535 Angstrom
T3  -- O7  = 1.6535 Angstrom
T3  -- O8  = 1.6740 Angstrom
      mean = 1.6550 Angstrom
        t1 = 0.038203  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020841  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6124 A <--> 1.6740 A
          Mean   = 1.6318 A
          StdDev = 0.0186 A

       t1 Range  = 0.0160 <-- 0.0276 --> 0.0382
       t2 Range  = 0.0076 <-- 0.0159 --> 0.0208

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.316 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.666 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 108.516 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.151 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 108.792 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 112.359 deg; O4  -- O2  = 3 A
       108.516 deg <-- 109.467 deg --> 112.359 deg

O4  -- T2  -- O4  = 116.455 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 107.704 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.955 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 107.708 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.959 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 115.367 deg; O5  -- O6  = 3 A
       104.955 deg <-- 109.525 deg --> 116.455 deg

O6  -- T3  -- O7  = 106.991 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 106.991 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 107.799 deg; O6  -- O8  = 3 A
O7  -- T3  -- O7  = 105.559 deg; O7  -- O7  = 3 A
O7  -- T3  -- O8  = 114.515 deg; O7  -- O8  = 3 A
O7  -- T3  -- O8  = 114.515 deg; O7  -- O8  = 3 A
       105.559 deg <-- 109.395 deg --> 114.515 deg

        O-T-O SUMMARY
          Range  = 104.9551 deg <--> 116.4545 deg
          Mean   = 109.3183 deg
          StdDev = 3.5552 deg

        O--O SUMMARY
          Range  = 2.5696 A <--> 2.7989 A
          Mean   = 2.6592 A
          StdDev = 0.0669 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  = 120.250 deg; T1  -- T2  = 4.8173 A
T1  - O1  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 4.8256 A
T1  - O1  - T1  - O2  - T1  =  90.490 deg; T1  -- T1  = 4.2674 A
T2  - O3  - T1  - O4  - T1  = 119.750 deg; T2  -- T1  = 4.8530 A
T2  - O3  - T1  - O2  - T1  =  89.930 deg; T2  -- T1  = 4.2722 A
T1  - O4  - T1  - O2  - T1  =  89.510 deg; T1  -- T1  = 4.2674 A

T1  - O4  - T2  - O4  - T1  = 179.483 deg; T1  -- T1  = 5.5942 A
T1  - O4  - T2  - O5  - T2  =  90.068 deg; T1  -- T2  = 4.2722 A
T1  - O4  - T2  - O6  - T3  =  90.082 deg; T1  -- T3  = 3.9667 A
T1  - O4  - T2  - O5  - T2  =  90.068 deg; T1  -- T2  = 4.2722 A
T1  - O4  - T2  - O6  - T3  =  90.084 deg; T1  -- T3  = 3.9667 A
T2  - O5  - T2  - O6  - T3  = 146.047 deg; T2  -- T3  = 5.7729 A

T3  - O6  - T3  - O7  - T3  =  60.000 deg; T3  -- T3  = 2.8821 A
T3  - O6  - T3  - O7  - T3  = 143.778 deg; T3  -- T3  = 5.9233 A
T3  - O6  - T3  - O8  - T2  = 118.816 deg; T3  -- T2  = 4.8988 A
T3  - O7  - T3  - O7  - T3  = 143.778 deg; T3  -- T3  = 5.9233 A
T3  - O7  - T3  - O8  - T2  = 118.817 deg; T3  -- T2  = 4.8988 A
T3  - O7  - T3  - O8  - T2  =  77.505 deg; T3  -- T2  = 3.8767 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 179.4831 deg
          Mean   = 109.5193 deg
          StdDev = 29.3390 deg

        T--T SUMMARY
          Range  = 2.8821 A <--> 5.9233 A
          Mean   = 4.5988 A
          StdDev = 0.7164 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 177.257 deg ; T1  -- T1   3.2326 A

T1  -- O2  -- T1  = 119.551 deg ; T1  -- T1   2.8137 A

T1  -- O3  -- T1  = 117.608 deg ; T1  -- T1   2.7584 A

T1  -- O4  -- T2  = 117.596 deg ; T1  -- T2   2.7972 A

T2  -- O5  -- T2  = 179.996 deg ; T2  -- T2   3.2259 A

T2  -- O6  -- T3  = 119.026 deg ; T2  -- T3   2.8086 A

T3  -- O7  -- T3  = 121.268 deg ; T3  -- T3   2.8821 A

T3  -- O8  -- T3  = 180.000 deg ; T3  -- T3   3.3480 A


        T-O-T SUMMARY
          Range  = 117.5962° <--> 180.0000 deg
          Mean   = 138.6929 deg
          StdDev = 28.4667 deg

        T--T SUMMARY
          Range  = 2.7584 A <--> 3.3480 A
          Mean   = 2.9557 A
          StdDev = 0.2206 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7584 Angstrom
T1  -- T2  = 2.7972 Angstrom
T2  -- T1  = 2.7972 Angstrom
T2  -- T1  = 2.7971 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 9 17 30 49 78 116 160 206 256 324 406 495 575 657 753
TD10 = 926
Circuit symbol = 4.6.4.6_{2}.4.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.8_{2}
Weight = 21

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 20 36 60 96 134 171 220 292 371 445 506 588 689 811
TD10 = 1044
Circuit symbol = 4.6.4.6.6.8_{6}
Weight = 17
Vertex symbol  = 4.6.4.6.8_{2}.9_{2}
Weight = 25

T3 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 46 72 100 145 203 264 324 385 457 552 652 751 853
TD10 = 1193
Circuit symbol = 3.8_{2}.6.8.6.8
Weight = 28
Vertex symbol  = 3.8_{2}.6.8.6.8
Weight = 28

<TD10> = 1022.250
Average ring size = 5.6432