Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_162_2_9496_vWOJsw.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 17.18 T-atoms per nm^3
Material density = 1.714 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6160 Angstrom
T1  -- O2  = 1.6216 Angstrom
T1  -- O4  = 1.6147 Angstrom
T1  -- O3  = 1.6127 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.008963  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010379  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6146 Angstrom
T2  -- O4  = 1.6126 Angstrom
T2  -- O5  = 1.6204 Angstrom
T2  -- O6  = 1.6213 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.009030  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008454  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6126 A <--> 1.6216 A
          Mean   = 1.6167 A
          StdDev = 0.0036 A

       t1 Range  = 0.0090 <-- 0.0090 --> 0.0090
       t2 Range  = 0.0085 <-- 0.0094 --> 0.0104

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.726 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 107.267 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 110.363 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 111.235 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 108.959 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.283 deg; O4  -- O3  = 3 A
       107.267 deg <-- 109.472 deg --> 111.235 deg

O3  -- T2  -- O4  = 109.405 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 111.211 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.423 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 108.633 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 110.708 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.466 deg; O5  -- O6  = 3 A
       107.423 deg <-- 109.474 deg --> 111.211 deg

        O-T-O SUMMARY
          Range  = 107.2667 deg <--> 111.2348 deg
          Mean   = 109.4620 deg
          StdDev = 1.3037 deg

        O--O SUMMARY
          Range  = 2.6015 A <--> 2.6709 A
          Mean   = 2.6393 A
          StdDev = 0.0219 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 123.133 deg; T2  -- T1  = 5.5729 A
T2  - O1  - T1  - O4  - T1  =  93.633 deg; T2  -- T1  = 4.5229 A
T2  - O1  - T1  - O3  - T2  = 111.422 deg; T2  -- T2  = 5.2175 A
T1  - O2  - T1  - O4  - T1  = 119.449 deg; T1  -- T1  = 5.3747 A
T1  - O2  - T1  - O3  - T2  = 115.228 deg; T1  -- T2  = 5.3505 A
T1  - O4  - T1  - O3  - T2  =  86.413 deg; T1  -- T2  = 4.2459 A

T1  - O3  - T2  - O4  - T2  =  86.346 deg; T1  -- T2  = 4.2459 A
T1  - O3  - T2  - O5  - T2  = 106.377 deg; T1  -- T2  = 4.9605 A
T1  - O3  - T2  - O6  - T1  = 111.422 deg; T1  -- T1  = 5.2175 A
T2  - O4  - T2  - O5  - T2  = 149.709 deg; T2  -- T2  = 5.8722 A
T2  - O4  - T2  - O6  - T1  =  93.609 deg; T2  -- T1  = 4.5229 A
T2  - O5  - T2  - O6  - T1  = 106.384 deg; T2  -- T1  = 4.9597 A

        T-T-T SUMMARY
          Range  = 86.3459 deg <--> 149.7092 deg
          Mean   = 108.0334 deg
          StdDev = 17.6824 deg

        T--T SUMMARY
          Range  = 4.2459 A <--> 5.8722 A
          Mean   = 4.9815 A
          StdDev = 0.5131 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 159.260 deg ; T1  -- T1   3.1792 A

T1  -- O2  -- T1  = 139.607 deg ; T1  -- T1   3.0438 A

T1  -- O3  -- T2  = 156.016 deg ; T1  -- T2   3.1569 A

T1  -- O4  -- T2  = 156.233 deg ; T1  -- T2   3.1581 A

T2  -- O5  -- T2  = 140.093 deg ; T2  -- T2   3.0464 A

T2  -- O6  -- T2  = 138.990 deg ; T2  -- T2   3.0371 A


        T-O-T SUMMARY
          Range  = 138.9904° <--> 159.2598 deg
          Mean   = 148.3667 deg
          StdDev = 8.9331 deg

        T--T SUMMARY
          Range  = 3.0371 A <--> 3.1792 A
          Mean   = 3.1036 A
          StdDev = 0.0621 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 102 134 165 196 232 277 333 399 464 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 35 51 72 97 127 162 202 247 289 333 385 440 503
TD10 = 782
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12
Weight = 25

<TD10> = 785.000
Average ring size = 5.3333