Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_161_2_5322_mie33x.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 19.17 T-atoms per nm^3
Material density = 1.913 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6213 Angstrom
T1  -- O2  = 1.6213 Angstrom
T1  -- O4  = 1.6212 Angstrom
T1  -- O3  = 1.6212 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.006987  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000043  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6213 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O3  = 1.6212 Angstrom
T2  -- O4  = 1.6212 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.006951  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000062  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6212 A <--> 1.6213 A
          Mean   = 1.6212 A
          StdDev = 0.0000 A

       t1 Range  = 0.0070 <-- 0.0070 --> 0.0070
       t2 Range  = 0.0000 <-- 0.0001 --> 0.0001

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.475 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.476 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.471 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.455 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.487 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.464 deg; O4  -- O3  = 3 A
       109.455 deg <-- 109.471 deg --> 109.487 deg

O1  -- T2  -- O2  = 109.475 deg; O1  -- O2  = 3 A
O1  -- T2  -- O3  = 109.481 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 109.459 deg; O1  -- O4  = 3 A
O2  -- T2  -- O3  = 109.469 deg; O2  -- O3  = 3 A
O2  -- T2  -- O4  = 109.483 deg; O2  -- O4  = 3 A
O3  -- T2  -- O4  = 109.460 deg; O3  -- O4  = 3 A
       109.459 deg <-- 109.471 deg --> 109.483 deg

        O-T-O SUMMARY
          Range  = 109.4555 deg <--> 109.4868 deg
          Mean   = 109.4712 deg
          StdDev = 0.0096 deg

        O--O SUMMARY
          Range  = 2.6472 A <--> 2.6477 A
          Mean   = 2.6474 A
          StdDev = 0.0002 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 120.002 deg; T2  -- T2  = 5.2388 A
T2  - O1  - T1  - O4  - T2  =  89.999 deg; T2  -- T2  = 4.2772 A
T2  - O1  - T1  - O3  - T2  = 120.003 deg; T2  -- T2  = 5.2385 A
T2  - O2  - T1  - O4  - T2  = 119.989 deg; T2  -- T2  = 5.2382 A
T2  - O2  - T1  - O3  - T2  =  90.001 deg; T2  -- T2  = 4.2772 A
T2  - O4  - T1  - O3  - T2  = 120.006 deg; T2  -- T2  = 5.2384 A

T1  - O1  - T2  - O2  - T1  = 119.998 deg; T1  -- T1  = 5.2387 A
T1  - O1  - T2  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2772 A
T1  - O1  - T2  - O4  - T1  = 119.990 deg; T1  -- T1  = 5.2382 A
T1  - O2  - T2  - O3  - T1  = 120.005 deg; T1  -- T1  = 5.2385 A
T1  - O2  - T2  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2772 A
T1  - O3  - T2  - O4  - T1  = 120.007 deg; T1  -- T1  = 5.2384 A

        T-T-T SUMMARY
          Range  = 89.9988 deg <--> 120.0073 deg
          Mean   = 110.0000 deg
          StdDev = 14.1750 deg

        T--T SUMMARY
          Range  = 4.2772 A <--> 5.2388 A
          Mean   = 4.9180 A
          StdDev = 0.4542 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 137.750 deg ; T1  -- T2   3.0246 A

T1  -- O2  -- T2  = 137.750 deg ; T1  -- T2   3.0245 A

T1  -- O3  -- T2  = 137.726 deg ; T1  -- T2   3.0242 A

T1  -- O4  -- T2  = 137.731 deg ; T1  -- T2   3.0243 A


        T-O-T SUMMARY
          Range  = 137.7258° <--> 137.7499 deg
          Mean   = 137.7392 deg
          StdDev = 0.0109 deg

        T--T SUMMARY
          Range  = 3.0242 A <--> 3.0246 A
          Mean   = 3.0244 A
          StdDev = 0.0002 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T2 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 20 34 52 74 100 130 164 202 244 290 340 394 452 514
TD10 = 791
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

<TD10> = 791.000
Average ring size = 5.1429