Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_161-2_2_215346_SsrrTs.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 24.49 T-atoms per nm^3
Material density = 2.443 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5911 Angstrom
T1  -- O2  = 1.6760 Angstrom
T1  -- O1  = 1.6744 Angstrom
T1  -- O3  = 1.6908 Angstrom
      mean = 1.6581 Angstrom
        t1 = 0.098405  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076889  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6289 Angstrom
T2  -- O4  = 1.5530 Angstrom
T2  -- O4  = 1.6137 Angstrom
T2  -- O3  = 1.6625 Angstrom
      mean = 1.6145 Angstrom
        t1 = 0.111839  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.074369  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5530 A <--> 1.6908 A
          Mean   = 1.6363 A
          StdDev = 0.0455 A

       t1 Range  = 0.0984 <-- 0.1051 --> 0.1118
       t2 Range  = 0.0744 <-- 0.0756 --> 0.0769

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  87.666 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  =  98.875 deg; O1  -- O1  = 2 A
O1  -- T1  -- O3  = 125.963 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 126.235 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 111.740 deg; O2  -- O3  = 3 A
O1  -- T1  -- O3  = 106.774 deg; O1  -- O3  = 3 A
       87.666 deg <-- 109.542 deg --> 126.235 deg

O2  -- T2  -- O4  = 120.282 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 101.524 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 119.189 deg; O2  -- O3  = 3 A
O4  -- T2  -- O4  =  89.663 deg; O4  -- O4  = 2 A
O4  -- T2  -- O3  =  88.756 deg; O4  -- O3  = 2 A
O4  -- T2  -- O3  = 133.285 deg; O4  -- O3  = 3 A
       88.756 deg <-- 108.783 deg --> 133.285 deg

        O-T-O SUMMARY
          Range  = 87.6661 deg <--> 133.2847 deg
          Mean   = 109.1625 deg
          StdDev = 15.4238 deg

        O--O SUMMARY
          Range  = 2.2330 A <--> 3.0078 A
          Mean   = 2.6455 A
          StdDev = 0.2784 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  74.842 deg; T1  -- T2  = 3.6475 A
T1  - O1  - T1  - O1  - T1  = 112.379 deg; T1  -- T1  = 4.4660 A
T1  - O1  - T1  - O3  - T2  = 153.095 deg; T1  -- T2  = 5.7868 A
T2  - O2  - T1  - O1  - T1  = 108.292 deg; T2  -- T1  = 4.8381 A
T2  - O2  - T1  - O3  - T2  = 117.747 deg; T2  -- T2  = 5.5882 A
T1  - O1  - T1  - O3  - T2  =  87.188 deg; T1  -- T2  = 4.1227 A

T1  - O2  - T2  - O4  - T2  =  72.606 deg; T1  -- T2  = 3.6475 A
T1  - O2  - T2  - O4  - T1  = 133.547 deg; T1  -- T1  = 5.9989 A
T1  - O2  - T2  - O3  - T2  = 103.876 deg; T1  -- T2  = 4.8381 A
T2  - O4  - T2  - O4  - T1  = 148.819 deg; T2  -- T1  = 5.9063 A
T2  - O4  - T2  - O3  - T2  = 102.165 deg; T2  -- T2  = 4.4660 A
T1  - O4  - T2  - O3  - T2  =  88.542 deg; T1  -- T2  = 4.2889 A

        T-T-T SUMMARY
          Range  = 72.6062 deg <--> 153.0945 deg
          Mean   = 108.5915 deg
          StdDev = 25.4715 deg

        T--T SUMMARY
          Range  = 3.6475 A <--> 5.9989 A
          Mean   = 4.7996 A
          StdDev = 0.8149 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 110.746 deg ; T1  -- T1   2.6875 A

T1  -- O2  -- T2  = 162.622 deg ; T1  -- T2   3.2670 A

T1  -- O3  -- T2  = 153.052 deg ; T1  -- T2   3.2610 A

T2  -- O4  -- T2  = 129.990 deg ; T2  -- T2   2.8700 A


        T-O-T SUMMARY
          Range  = 110.7462° <--> 162.6219 deg
          Mean   = 139.1025 deg
          StdDev = 20.6516 deg

        T--T SUMMARY
          Range  = 2.6875 A <--> 3.2670 A
          Mean   = 3.0214 A
          StdDev = 0.2565 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2635 A
O3  -- O4  = 2.2502 A
O4  -- O4  = 2.2330 A
O4  -- O4  = 2.2330 A
T1  -- T1  = 2.6875 Angstrom
T1  -- T1  = 2.6875 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 40 65 93 126 168 213 263 323 382 444 516 597 683
TD10 = 1004
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{26}
Weight = 36

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 21 40 65 93 126 168 213 263 323 382 444 516 597 683
TD10 = 1004
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.10_{26}
Weight = 36

<TD10> = 1004.000
Average ring size = 8.6111